Gray rubber quartz plate and preparation method thereof

A quartz plate and rubber technology, applied in the field of rubber plates, can solve the problems of strong light resistance, wear resistance, acid resistance, poor alkali resistance, acid resistance, alkali resistance, and wear resistance, etc. Save time and improve wear resistance

Active Publication Date: 2013-11-27
李彦峰
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In rescue and evacuation passages, overpasses, sidewalks and other places, in order to prevent slipping, anti-slip rubber quartz plates are laid on cement pavements or metal pavements. The rubber sheet produced from these components has the disadvantages of strong light resistance, wear resistance, acid resistance and alkali resistance, and is flammable, so there are many unsafe factors in application.
In order to solve its flammable shortcomings, Chinese patent 200410051340.3 discloses a wear-resistant and flame-retardant rubber sheet, which is composed of rubber, vulcanizing agent, activator, accelerator, anti-aging agent, softener and flame retardant
Although this patent solves the shortcomings of the rubber sheet being flammable, its acid resistance and alkali resistance are still poor, and its wear resistance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gray rubber quartz plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] The preparation method of above-mentioned gray rubber quartz plate, this method comprises the following steps:

[0063] Step One, Ingredients

[0064] Weigh the raw materials for preparing the board according to the weight ratio of each raw material, and put them into a barrel with a stirring mechanism and stir evenly;

[0065] The second step, secret refining

[0066] Put the evenly stirred mixture into the internal mixer for internal mixing, the internal mixing temperature is 80°C~120°C, and the internal mixing time is 24-26min;

[0067] The third step is to make a film

[0068] Use an open mill to make the mixed rubber into a film;

[0069] The fourth step, vulcanization

[0070] Put the film together with the rough surface layer into the vulcanizer for vulcanization, the vulcanization temperature is controlled at 145-165°C, and the time is controlled at 24-26min to obtain the finished product;

[0071] The fifth step, packaging.

[0072] For producing the rubb...

Embodiment 11

[0075] Step One, Ingredients

[0076] Weigh 95 kg of EPDM rubber, 5 kg of chlorosulfonated polyethylene, 27--kg of quartz powder, 39--kg of white carbon black, zinc oxide and stearin with a weight ratio of 3:1 Acid mixture 4 kg, a mixture of Accelerator M, Accelerator TMTD and Accelerator ZDC in a weight ratio of 5:3:3 5.2 kg, sulfur 1.4 kg, paraffin oil 44 kg, carbon black 0.9 kg, binder A 0.9 Kilogram, 1 kilogram of anti-aging agent 445, 1.9 kilograms of coumarone resin, and it is put into the barrel with stirring mechanism and stirs;

[0077] The second step, secret refining

[0078] Put the evenly stirred mixture into a banbury mixer for banburying, the banburying temperature is 80°C, and the banburying time is 26min;

[0079] The third step is to make a film

[0080] Use an open mill to make the mixed rubber into a film;

[0081] The fourth step, vulcanization

[0082] Put the film together with the matte layer into the vulcanizer for vulcanization, the vulcanization...

Embodiment 12

[0085] Step One, Ingredients

[0086] Weigh 95 kg of EPDM EPDM rubber, 5 kg of chlorosulfonated polyethylene, 29--kg of quartz powder, 41--kg of white carbon black, zinc oxide and stearin with a weight ratio of 3:1 Acid mixture 4.2 kg, a mixture of Accelerator M, Accelerator TMTD and Accelerator ZDC in a weight ratio of 5:3:3 5.5 kg, sulfur 1.6 kg, paraffin oil 46 kg, carbon black 1.1 kg, binder A 1.1 Kilogram, anti-aging agent 445 1.1 kilogram, coumarone resin 2.1 kilogram, and it is put into the barrel with stirring mechanism and stirs;

[0087] The second step, secret refining

[0088] Put the evenly stirred mixture into a banbury mixer for banburying, the banburying temperature is 120°C, and the banburying time is 24min;

[0089] The third step is to make a film

[0090] Use an open mill to make the mixed rubber into a film;

[0091] The fourth step, vulcanization

[0092] Put the film together with the rough surface layer into the vulcanizer for vulcanization, the vu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of rubber quartz plates, and particularly discloses a gray rubber quartz plate and a preparation method of the gray rubber quartz plate. The gray rubber quartz plate has the technical scheme that the quartz plate comprises a plate body and a rough surface layer, and is characterized in that the plate body comprises the following materials in parts by weight: 100 parts of rubber, 5.9-29 parts of quartz powder, 10-52 parts of white carbon black, 4-18 parts of activating agent, 0.8-5.5 parts of accelerating agent, 0.9-8.5 parts of vulcanizing agent, 2-50 parts of softener, 0.8-1.1 parts of coloring agent, 0.8-2 parts of bonding agent, 1-5 parts of anti-aging agent and 1.8-4.0 parts of solubilizer. The wear-resistant performance as well as the acid-resistant and alkaline-resistant properties of the rubber quartz plate can be improved, the heat absorption and the high light reflection can be reduced, and the service life is greatly prolonged.

Description

technical field [0001] The invention belongs to the technical field of rubber plates, in particular to a gray rubber quartz plate and a preparation method thereof. Background technique [0002] In rescue and evacuation passages, overpasses, sidewalks and other places, in order to prevent slipping, anti-slip rubber quartz plates are laid on cement pavement or metal pavement. The components of anti-slip rubber plates currently produced are mostly composed of rubber, vulcanizing agent, activator, and accelerator. The rubber sheet produced from these components has the disadvantages of strong light resistance, wear resistance, acid resistance and alkali resistance, and is flammable, so there are many unsafe factors in application. In order to solve its flammable shortcomings, Chinese patent 200410051340.3 discloses a wear-resistant and flame-retardant rubber sheet, which is composed of rubber, vulcanizing agent, activator, accelerator, anti-aging agent, softener and flame retard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/16C08L23/34C08L11/00C08L7/00C08K13/02C08K3/36C08K3/40C08L25/16C08K3/04C08K5/01B32B25/04
Inventor 李彦峰李玉李亚楠李杰
Owner 李彦峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More