Epoxy coating and preparation method and application thereof

An epoxy coating and epoxy resin technology, applied in the field of coatings, can solve the problems of shortening the life of the paint film, failing to meet the design requirements, and high surface treatment costs, achieving low volatile organic compound content, good thick coating, good adhesion

Active Publication Date: 2012-08-01
北京红狮科技发展有限公司
View PDF3 Cites 61 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the anti-corrosion coating of many steel substrates requires an anti-corrosion period of more than 10 years, and the steel surface treatment before coating largely determines the protection period of the anti-corrosion coating. Most anti-corrosion coatings require steel surface treatment Sand blasting or shot blasting is required, and the rust removal level must reach Sa2.5 or above, so the surface treatment cost is very high, and in some occasions, it is almost impossible to mee...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy coating and preparation method and application thereof
  • Epoxy coating and preparation method and application thereof
  • Epoxy coating and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Prepare the epoxy coating according to the following composition and parts by weight,

[0030] Main paint:

[0031]

[0032]

[0033] Hardener:

[0034]

[0035] The preparation method of this product is:

[0036] It is characterized by mixing low molecular weight bisphenol A epoxy resin DER331, petroleum resin, dibutyl phthalate, xylene, n-butanol, BYK-P104, BYK-052, and bentonite BENTONE 38 together at high speed and stirring evenly. Then add plaster of paris, zinc phosphate, mica iron oxide, aluminum powder slurry, and talcum powder to disperse at high speed for 0.5-1 hour, then grind until the fineness meets the requirements, then adjust the viscosity of the product, and pack it after passing the test; the curing agent is formulated separately. When using, the ratio of main paint and curing agent is configured according to the weight ratio of 10:1, and it is used after stirring evenly.

Embodiment 2

[0037] Embodiment 2 is formulated according to the following composition and parts by weight to prepare epoxy coatings,

[0038] Main paint:

[0039]

[0040] Hardener:

[0041] Polyaminoamide 40

[0042] Cardanol Modified Phenalkamine 50

[0043] Methyl isobutyl ketone 10

[0044] Total 100

[0045] The preparation method of this high-performance epoxy anticorrosion coating is:

[0046] It is characterized in that low molecular weight bisphenol A epoxy resin Epikote 828, K-FLEX 171-90, dibutyl phthalate, xylene, n-butanol, ANTI-TERRA-U, BYK054, DISPARLON 630-20X Mix together at high speed and stir evenly, then add Paris plaster powder, zinc chromate, mica iron oxide, aluminum powder slurry, sericite powder, disperse at high speed for 0.5-1 hour, then grind until the fineness meets the requirements, and then adjust the product viscosity, Packaged after passing the test; the curing agent is formulated separately. When using, the ratio of main paint and curing agent is...

Embodiment 3

[0047] Embodiment 3 is formulated according to the following composition and parts by weight to prepare epoxy coatings,

[0048] Main paint:

[0049]

[0050] Hardener:

[0051] Polyaminoamide 40

[0052] Cardanol modified phenalkamine 40

[0053] Toluene 20

[0054] Total 100

[0055] The preparation method of this high-performance epoxy anticorrosion coating is:

[0056]It is characterized by first mixing low molecular weight bisphenol A epoxy resin NPEL-128, Desmocap 11, dibutyl phthalate, toluene, isopropanol, ANTI-TERRA-U, BYK-051, BYK-430 together at high speed Stir evenly, then add plaster of paris powder, zinc oxide, mica iron oxide, aluminum powder slurry, sericite powder, disperse at high speed for 0.5-1 hour, then grind until the fineness meets the requirements, then adjust the product viscosity, and pack after passing the test; The curing agent is formulated separately. When using, the ratio of main paint and curing agent is configured according to the we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel epoxy coating and a preparation method thereof. The coating not only has excellent corrosion resistance, but also has excellent compatibility with a base material or a lower coating film, particularly an epoxy coating, a polyurethane coating, a fluorocarbon coating or an alkyd resin coating. The epoxy coating comprises a main paint and a curing agent, wherein the main paint contains bisphenol A epoxy resin and modifying resin for modifying the bisphenol A epoxy resin; and the curing agent contains polyamino amide and cardanol modified phenolic amine.

Description

technical field [0001] The invention relates to paint technology, in particular to an epoxy paint with excellent adhesion and / or anti-corrosion performance and its preparation method and application. Background technique [0002] At present, the anti-corrosion coating of many steel substrates requires an anti-corrosion period of more than 10 years, and the steel surface treatment before coating largely determines the protection period of the anti-corrosion coating. Most anti-corrosion coatings require steel surface treatment Sand blasting or shot blasting is required, and the rust removal level must reach Sa2.5 or above, so the surface treatment cost is very high, and in some occasions, it is almost impossible to meet the design requirements due to limited conditions; and the high-pressure water or wet sand blasting process There will be flash rust on the surface of steel; most of the steel structure anti-corrosion coatings before the 1990s have entered the maintenance perio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/02C09D167/00C09D157/02C09D193/04C09D133/00C09D175/04C09D5/08C09D7/12
Inventor 郭祥恩李运德王克正董祥云
Owner 北京红狮科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka