Preparation method for amphiprotic potato starch microcrystalline wax/AKD (Alkyl Ketene dimer) neutral/alkaline sizing agent
A technology of potato starch and microcrystalline wax, which is applied in the direction of water-repellent addition, etc., can solve the problems of poor market competitiveness, high price and high price of AKD emulsion, achieve environmental protection improvement, improve emulsion stability and sizing performance, The effect of applying effect enhancement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] Example one
[0014] A preparation method of amphoteric potato starch microcrystalline wax / AKD medium / alkaline sizing agent, comprising the following steps:
[0015] In the first step, 200 grams of water, 100 grams of potato starch, 2 grams of sodium hydroxide and 1 gram of hydrogen peroxide were added to the first reactor and reacted at 80°C for 1.0 hour to obtain oxidatively degraded potato starch, water, potato starch, and hydroxide The mass ratio of sodium to hydrogen peroxide is 200:100:2:1, then 7 grams of sodium hydroxide and 49 grams of 3-chloro-2-hydroxypropyltrimethylammonium chloride are added to the first reactor, and the temperature is raised to 90 React for 2 hours at ℃, add 5 g of acetic acid after cooling to 50℃, and then reduce to 20℃. The mass ratio of potato starch, sodium hydroxide, 3-chloro-2-hydroxypropyltrimethylammonium chloride and acetic acid is 100: 7:49:5,
[0016] In the second step, add water to the first reactor, adjust the solid content of the...
Example Embodiment
[0019] Example two
[0020] A preparation method of amphoteric potato starch microcrystalline wax / AKD medium / alkaline sizing agent, comprising the following steps:
[0021] In the first step, 200 grams of water, 100 grams of potato starch, 2 grams of sodium hydroxide and 1 gram of hydrogen peroxide are added to the first reactor and reacted at 81°C for 1.1 hours to obtain oxidatively degraded potato starch, water, potato starch, and hydroxide The mass ratio of sodium to hydrogen peroxide is 200:100:2:1, then 7 grams of sodium hydroxide and 49 grams of 3-chloro-2-hydroxypropyltrimethylammonium chloride are added to the first reactor, and the temperature is raised to 91 React for 1.8 hours at ℃, add 5 g of acetic acid after cooling to 51℃, and then reduce to 22℃. The mass ratio of potato starch, sodium hydroxide, 3-chloro-2-hydroxypropyltrimethylammonium chloride and acetic acid is 100: 7:49:5,
[0022] In the second step, add water to the first reactor, adjust the solid content of t...
Example Embodiment
[0025] Example three
[0026] A preparation method of amphoteric potato starch microcrystalline wax / AKD medium / alkaline sizing agent, comprising the following steps:
[0027] In the first step, add 200 grams of water, 100 grams of potato starch, 2 grams of sodium hydroxide and 1 gram of hydrogen peroxide to the first reactor and react for 1.2 hours at 82°C to obtain oxidatively degraded potato starch, water, potato starch, and hydroxide. The mass ratio of sodium to hydrogen peroxide is 200:100:2:1, then 7 grams of sodium hydroxide and 49 grams of 3-chloro-2-hydroxypropyltrimethylammonium chloride are added to the first reactor, and the temperature is raised to 92 React for 1.6 hours at ℃, add 5 g of acetic acid after cooling to 52℃, and then reduce to 24℃. The mass ratio of potato starch, sodium hydroxide, 3-chloro-2-hydroxypropyltrimethylammonium chloride and acetic acid is 100: 7:49:5,
[0028] In the second step, water is added to the first reactor to adjust the solid content of...
PUM
Property | Measurement | Unit |
---|---|---|
Cobb value | aaaaa | aaaaa |
Ring pressure index | aaaaa | aaaaa |
Cobb value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap