A laser cladding and laser technology, applied in laser welding equipment, manufacturing tools, coatings, etc., can solve the problems of high power consumption and low energy absorption and utilization rate of laser beams, and achieve high energy conversion efficiency and energy absorption and utilization rate High, power-saving effect

Active Publication Date: 2012-09-19
SHANDONG ENERGY HEAVY EQUIP MFG GRP CO LTD +2
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the carbon dioxide laser is used for laser cladding, the laser from the carbon dioxide laser is irradiated on the column of the hydraulic support, and the energy absorption and utilization rate of the laser beam is very low.
Moreover, the power consumption in this process is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] This embodiment is a laser cladding method for mine hydraulic support columns

[0048] The hydraulic support column used in this embodiment is the column of the mining hydraulic support used by Xinwen Mining Group Xinjulong Energy Co., Ltd. The column is a hydraulic support column based on 27SiMn, with a diameter of 300mm.

[0049] Laser cladding is performed using the following methods:

[0050] (1) Derust and roughen the column of the mining hydraulic support.

[0051] (2) Loading into a laser processing machine tool, which is a semiconductor laser processing machine tool (that is, a processing machine tool including a semiconductor laser).

[0052] (3) Cooperating with the rotation movement of the main shaft C and the feed movement of the X linear axis of the laser head, powder feeding and laser cladding are carried out synchronously in one working step; the output power of the semiconductor laser is 4000W, and the laser from the semiconductor laser The distance f...

Embodiment 2

[0064] This embodiment is a laser cladding method for mine hydraulic support columns

[0065] The hydraulic support column used in this embodiment is the column of the mining hydraulic support used by Xinwen Mining Group Xinjulong Energy Co., Ltd. The column is a hydraulic support column based on 27SiMn, with a diameter of 400mm.

[0066] Laser cladding is performed using the following methods:

[0067] (1) Derust and roughen the column of the mining hydraulic support.

[0068] (2) Loading into a laser processing machine tool, which is a semiconductor laser processing machine tool.

[0069] (3) Cooperating with the rotation movement of the main shaft C and the feed movement of the X linear axis of the laser head, powder feeding and laser cladding are carried out synchronously in one working step; the output power of the semiconductor laser is 4000W, and the laser from the semiconductor laser The distance from the beam exit to the surface of the column of the hydraulic suppo...

Embodiment 3

[0077] This embodiment is a laser cladding method for mine hydraulic support columns

[0078] The hydraulic support column used in this embodiment is the column of the mining hydraulic support used by Xinwen Mining Group Xinjulong Energy Co., Ltd. The column is a hydraulic support column based on 27SiMn, with a diameter of 350mm.

[0079] Laser cladding is performed using the following methods:

[0080] (1) Derust and roughen the column of the mining hydraulic support.

[0081] (2) Loading into a laser processing machine tool, which is a semiconductor laser processing machine tool.

[0082] (3) Cooperating with the rotation movement of the main shaft C and the feed movement of the X linear axis of the laser head, powder feeding and laser cladding are carried out synchronously in one working step; the output power of the semiconductor laser is 4000W, and the laser from the semiconductor laser The distance from the beam exit to the surface of the column of the hydraulic suppo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention provides a laser cladding method belonging to the field of laser machining. The laser cladding method is characterized in that a laser cladding layer is formed through melting alloy powder for laser cladding on the surface of an upright of a hydraulic support by utilizing a laser beam emitted by a semiconductor laser; the semiconductor laser takes a semiconductor material as a working substance and emits light by utilizing the transition of the semiconductor material between energy bands; and the upright of the hydraulic support is mainly made of 27SiMn alloy steel materials. The laser cladding method can be used for increasing the energy absorption efficiency of the laser beam and is high in electric energy utilization ratio so that the power consumption is reduced.

Description

technical field [0001] The invention relates to a laser cladding method, which belongs to the field of laser processing and manufacturing. Background technique [0002] The hydraulic support column is a key component of mining equipment. In China, the hydraulic support column is usually treated with chrome plating to prevent surface rust and corrosion. However, the wear resistance of the chrome plating layer is poor. Generally, after 1 to 1.5 years, the chrome plating layer will appear peeling and peeling. Therefore, the emulsion will corrode the surface of the column, which will affect the use effect of the hydraulic support. [0003] The Chinese patent with the announcement CN101875128B discloses a laser cladding method for mining hydraulic support columns, which cladding three layers of metallurgical materials through specific laser cladding process conditions, thereby solving the wear resistance of the surface of mining hydraulic support columns Non-toxic, anti-corrosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/10C22C38/40
CPCC23C24/10C23C24/103B23K26/34C22C38/40C23C24/106B23K26/342
Inventor 李希勇李伦实周峰杜伯奇杨庆东苏伦昌董春春杨帆
Owner SHANDONG ENERGY HEAVY EQUIP MFG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap