Borax oxide remover for internal surface of hot continuous rolled steel pipe and method for preparing same

A technology for rolling steel pipes on the inner surface, which is applied in the field of borax deoxidizer on the inner surface of hot continuous rolling steel pipes and its preparation. The effect of preventing hardening

Active Publication Date: 2012-10-03
BAOTOU HERUN METALLURGICAL LUBRICATION MATERIALS
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a borax deoxidizer for the inner surface of hot continuous rolling steel pipes and its preparation method, which solves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] Embodiment: prepare 1 kilogram of borax deoxidizer

[0015] 1. raw material

[0016] Borax, sodium sulfate, raw material stearic acid and sodium hydroxide for preparation of reducing agent, flux.

[0017] 2. Process points

[0018] (1) Add stearic acid and sodium hydroxide in a molar ratio of 1:1 to prepare the reducing agent sodium stearate;

[0019] (2) Borax is dried for 10 hours, and the moisture content is controlled to 24%;

[0020] (3) According to 55% of borax, 32% of sodium sulfate, and 1% of flux, mixed, ground and granulated, and sieved with 20 meshes; all refer to the percentage of the total amount;

[0021] (4) Sieve the reducing agent obtained in step (1) through 20 meshes, take 120 grams, and mix 880 grams of borax, sodium sulfate and flux mixture and sieved material obtained in step (3) for 60 minutes to obtain borax 1 kg of deoxidizer.

[0022] 3. The content of each component in the product is borax: 55%, sodium sulfate: 32%, reducing agent sod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A borax oxide remover for an internal surface of a hot continuous rolled steel pipe and a method for preparing the same belong to the technical field of hot continuous rolled steel pipes. The oxide remover comprises the following components of 53-58% of borax, 30-35% of sodium sulfate, 10-15% of reducing agent and 1-2% of fluxing agent according to mass percent content; and the maximum granularity of each component is less than or equal to 20 meshes. The preparation process of the borax oxide remover comprises the following steps of: preparing the reducing agent (sodium stearate), drying the borax, adding the fluxing agent and mixing together for granulating and screening, and then preparing the borax oxide remover. The method for preparing the borax oxide remover has the advantages that the problems of melt aggregation, high moisture content, poor blowing homogeneity and the like in the hot continuous rolling process can be solved; the quality of the internal surface of the steel pipe can be improved; the requirements on hot continuous rolling are met; and the method is moderate in cost, high in cost performance and suitable for population and application in the metallurgical field.

Description

technical field [0001] The invention belongs to the technical field of hot continuous rolling steel pipes, and in particular provides a borax deoxidizer for the inner surface of hot continuous rolling steel pipes and a preparation method thereof. Background technique [0002] In the production process of seamless steel pipe, the tube blank heated in the ring furnace is first perforated to make a hollow capillary tube, and then the capillary tube is sent to the continuous rolling mill to be inserted into the mandrel for rolling. After the tube blank is pierced, the inner cavity of the capillary tube is in contact with air, which inevitably produces oxidation, which will cause uneven scars on the inner wall of the steel pipe, which will seriously affect the quality of the steel pipe and the service life of the mandrel. Therefore, the inner wall of the capillary must be for deoxygenation. [0003] At present, there are two main processes for removing the oxide skin on the inne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/32
Inventor 陈向明刘杰民曲俊涛
Owner BAOTOU HERUN METALLURGICAL LUBRICATION MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap