An anti-ultraviolet and polyethylene technology, applied in the field of polyethylene cable materials, can solve the problems of easy fading, difficult coloring of colored cable materials, and low anti-ultraviolet performance, and achieve easy identification, excellent anti-ultraviolet performance, and excellent processing performance Effect

Inactive Publication Date: 2012-10-10
HUANGMEI KEPUDA INDAL
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems in the prior art that the color cable material is difficult to color, the color is unstable and easy to fade, and the anti-ultraviolet performance is not high. A kind of colored anti-ultraviolet polyethylene cable material is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful ultraviolet resistant polyethylene electric cable material
  • Colorful ultraviolet resistant polyethylene electric cable material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1. Preparation of yellow masterbatch: After fully mixing yellow toner with EVA resin, zinc stearate and EBS (ethylene bis stearamide), extrude and granulate at 180°C to make yellow masterbatch; The yellow toner: EVA resin: zinc stearate: the weight ratio of EBS is 45:50:3.5:1.5.

[0028] 2. Preparation of cable material: Take HDPE (HE6062): 70kg, LLDPE (7042) 24.5kg, yellow masterbatch 2.8kg, ultraviolet absorber (UV531) 2.0kg, polyethylene wax 0.4kg, antioxidant AT-10 0.1kg, AT-168 0.2kg, accurately metered and put into the high mixer, run for 2 minutes (note that first run at low speed for 1 minute, then run at high speed for 1 minute), the above-mentioned uniformly mixed raw materials are mixed, extruded, Cooling, dicing, drying and packaging.

Embodiment 2

[0030] 1. Preparation of black masterbatch: After fully mixing black toner with EVA resin, zinc stearate and EBS (ethylene bisstearamide), extrude and granulate at 180°C to make black masterbatch; The black toner: EVA resin: zinc stearate: the weight ratio of EBS is 45:50:3.5:1.5.

[0031] 2. Preparation of cable material: Take HDPE (HE6062): 70.3kg, LLDPE (7042) 25kg, black masterbatch 1.8kg, ultraviolet absorber (UV531) 2.2kg, polyethylene wax 0.4kg, antioxidant AT-10 0.1kg, AT-168 0.2kg, accurately metered and put into the high mixer, run for 2 minutes (note that first run at low speed for 1 minute, then run at high speed for 1 minute), the above-mentioned uniformly mixed raw materials are mixed, extruded, Cooling, dicing, drying and packaging.

Embodiment 3

[0033] 1. Preparation of blue color masterbatch: After fully mixing blue color powder with EVA resin, zinc stearate and EBS (ethylene bisstearyl amide), extrude pellets at 180°C to make blue color masterbatch; The toner: EVA resin: zinc stearate: the weight ratio of EBS is 45:50:3.5:1.5.

[0034] 2. Preparation of cable material: Take HDPE (HE6062): 68.5kg, LLDPE (7042) 26kg, blue masterbatch 2.4kg, ultraviolet absorber (UV531) 2.4kg, polyethylene wax 0.4kg, antioxidant AT-10 0.1kg, AT-168 0.2kg, accurately metered and put into the high mixer, run for 2 minutes (note that first run at low speed for 1 minute, then run at high speed for 1 minute), the above-mentioned uniformly mixed raw materials are mixed, extruded, Cooling, dicing, drying and packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a colorful ultraviolet resistant polyethylene electric cable material, which is prepared from high-density polyethylene HE6062, linear low-density polyethylene 7042, an ultraviolet absorber, a colorful colorant and an antioxidant through steps of mixing, compounding-extruding, cooling, grain-cutting, drying and the like. The colorful colorant provided by the invention is pre-treated by using a special method, so that the material has very good compatibility and dispersing property with a polyethylene base material; and the prepared electric cable material has excellent ultraviolet resistance, anti-aging property and good mechanical property. With the adoption of the colorful ultraviolet resistant polyethylene electric cable material provided by the invention, an electric cable can be kept fadeless for a long period; the aging and chapping of a cable protection layer is slowed to the greatest extent, so that the colorful ultraviolet resistant polyethylene electric cable material is widely applied to photoelectric cable jackets used in an outdoor filed (including a field with non-natural illumination), such as urban and rural communication networks, urban metros, vehicles and ships, and the like, and also can be used for controlling the insulation of the cable. Particularly, the colorful ultraviolet resistant polyethylene electric cable material is suitable for fields that purposes need to be distinguished by colors of the cable in a signal grading transmission and maintenance process or a cable maintaining process.

Description

technical field [0001] The invention relates to a polyethylene cable material, in particular to a colored anti-ultraviolet (UV) polyethylene cable material. Background technique [0002] With the modernization of the optical communication industry and the power transmission industry, the transmission of optical and electrical signals and the transmission of control signals require multiple cables to be laid together. For the convenience of engineering installation and maintenance, the cables need to be distinguished into different colors and can be maintained for a long time. Non-fading, thus giving birth to the market demand for colored anti-ultraviolet (UV) polyethylene cable compound. However, those skilled in the art know that color masterbatches need to be added to colored cable materials, and non-polar polyethylene resins are very difficult to be compatible with polar color toners, and the color dispersibility is poor, and the color of the cable materials made is unsta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08J3/22
Inventor 柯斌游志红沈鹏梅建国
Owner HUANGMEI KEPUDA INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap