Laser welding method for metal sheets applied to ultra low temperature environment

A thin metal plate and laser welding technology, which is applied in laser welding equipment, welding equipment, metal processing equipment, etc., can solve the problems of unfavorable energy security and other issues, and achieve the improvement of ultra-low temperature corrosion resistance and mechanical properties, weld quality and mechanical properties Improve and accelerate the effect of particle diffusion

Active Publication Date: 2014-08-13
ZHANGJIAGANG FURUI HEAVY EQUIP CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these technologies are mainly dependent on imports, which has greatly restricted the development of the LNG industry and is also extremely detrimental to the country's energy security.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Laser welding method for metal sheets applied to ultra low temperature environment
  • Laser welding method for metal sheets applied to ultra low temperature environment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The embodiment of the present invention discloses a laser welding method for thin metal plates applied in an ultra-low temperature environment, including:

[0032] (1) Provide sheet metal I and sheet metal II;

[0033] (2) Clean the parts to be welded of the metal sheet I and the metal sheet II with alcohol or acetone;

[0034] (3) Clamping and fixing the metal sheet I and the metal sheet II, a weld area is formed between the metal sheet I and the metal sheet II;

[0035] (4) placing metal sheet I and metal sheet II integrally in an inert gas environment and heating to the dynamic strain aging temperature of metal sheet I and metal sheet II;

[0036] (5) Fiber laser is used to perform filler wire welding on the weld area;

[0037] (6) Grind, polish and clean the weld area;

[0038] (7) Cover the upper and lower surfaces of the welded metal sheet with aluminum foil as a laser shock energy absorption layer;

[0039] (8) Place the welded metal sheet in a liquid nitroge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a laser welding method for metal sheets applied to an ultra low temperature environment. The method comprises the following steps of: integrally putting a metal sheet I and a metal sheet II in an inert gas environment, heating to the dynamic strain ageing temperatures of the metal sheet I and the metal sheet II, welding a filler wire in a seam zone by adopting fiber laser, putting the welded metal sheets in a liquid nitrogen environment, and emitting high-energy short pulse laser to carry out double-side laser impact on the metal sheets covered with an aluminum foil. The filler wire is welded for the metal sheets through laser at the dynamic strain ageing temperatures, so that the seam quality of a metal welding joint is greatly improved, and the seam zone is combined tightly with the metal sheets; and by laser impact strengthening treatment of the welding joint and the metal sheets in the same working environment at an ultra low temperature, ultra low temperature corrosion resistance and mechanical property of a metal welding member are remarkably improved.

Description

technical field [0001] The invention belongs to the field of laser processing, and in particular relates to a laser welding method for thin metal plates applied in an ultra-low temperature environment. Background technique [0002] Laser welding is a high-energy-density welding method that uses laser as an energy carrier. It focuses the laser into a very thin high-energy-density beam and irradiates it on the workpiece to melt the workpiece by heating and then cool it to obtain a weld. After the laser beam is focused, its power density can reach 106W / cm2, which is dozens or even hundreds of times higher than that of ordinary arc welding. Compared with traditional welding methods, laser welding has the characteristics of large depth-to-width ratio, small heat-affected zone, high weld joint strength, narrow weld seam, small welding deformation, no impact on surrounding tissues, easy automation and no X-ray generation. , These outstanding advantages make laser welding one of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/00B23K26/24B23K26/12B23K26/18B23K26/70B23K26/60
Inventor 殷劲松鲁金忠罗开玉钟金杉罗密陈彦珑
Owner ZHANGJIAGANG FURUI HEAVY EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products