Well-cementing and self-healing cement slurry for oil-gas field
A self-healing technology for oil and gas fields, applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of seepage reduction and anti-seepage performance, interlayer fluid inter-channeling, failure to function, etc., and achieve settlement stability Good, improved mechanical properties, adjustable thickening time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1:
[0031] A self-healing cement slurry for oil and gas field cementing. Its raw material composition and quality are as follows:
[0032] The quality of G-grade oil well cement is 800g; acrylamide-acrylamide-2-methylpropanesulfonate copolymer 16g; natural oil-containing latex with 10% oil content 80g; OP-40 stabilizer 2g; lignosulfonate 8g; Tributyl phosphate defoamer 4g; Citric acid 0.24g; Water 282g.
[0033] The weighed amount of the slurry water is the total amount of water calculated according to the water-cement ratio, minus the water content in each additive.
[0034] The preparation method of the present invention is as follows: the content of each additive component is uniformly mixed at a low shear rate, then a certain amount of cement is weighed and added to the slurry formulation liquid, and the slurry is mixed according to the API standard to obtain the present invention.
Example Embodiment
[0035] Example 2:
[0036] A self-healing cement slurry for oil and gas field cementing. Its raw material composition and quality are as follows:
[0037] The quality of G-grade oil well cement is 800g, acrylamide-acrylamide-2-methylpropanesulfonate copolymer 16g; OP-40 stabilizer 2g; benzene-butadiene oil latex with 10% oil content 80g; lignin sulfonic acid Salt 8g; Tributyl phosphate defoamer 4g; Citric acid 0.24g; Water 282g.
Example Embodiment
[0038] Example 3:
[0039] A self-healing cement slurry for oil and gas field cementing. Its raw material composition and quality are as follows:
[0040] The quality of G-grade oil well cement is 800g, acrylamide-acrylamide-2-methylpropanesulfonate copolymer 24g; OP-40 stabilizer 2g; natural oil latex with 10% oil content 80g; lignosulfonate 8g; 4g organosilicon defoamer; 2.4g citric acid; 271.5g water.
[0041] The following is a comparative example to verify the use effect of the present invention:
[0042] Grade G oil well cement 800g, acrylamide-acrylamide-2-methylpropanesulfonate copolymer 16g; lignosulfonate 8g; tributyl phosphate 4g; citric acid 0.24g; tap water 324g.
[0043] Table 1 Basic properties of cement slurry
[0044]
[0045]
[0046] Table 2 Self-healing performance of cement slurry
[0047]
[0048] Note: "—" in Table 2 means that self-healing cannot be achieved.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap