Preparation method of microemulsion cutting fluid with good oil extraction performance

A technology of cutting fluid and oil drainage, which is applied in the field of preparation of microemulsion cutting fluid, can solve the problems of reducing the service life of cutting fluid, losing the superiority of microemulsion cutting fluid, poor oil drainage performance of microemulsion cutting fluid, etc., and reaching the service life Excellent comprehensive effect of elongation and cooling, and good environmental protection performance

Inactive Publication Date: 2012-11-07
TIANCHANG RUNDA METAL ANTIRUST AUX
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the microemulsion cutting fluid also has the following disadvantages during use: the oil discharge performance of the microemulsion cutting fluid is poor. It becomes an emulsion, which makes the microemulsion cutting fluid lose its superiority and greatly reduces the service life of the cutting fluid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A preparation method of a microemulsion cutting fluid with good oil drainage. The cutting fluid is composed of the following components by weight percentage: diethanolamine 5%, triethanolamine 6%, boric acid 7%, 60% petroleum sodium sulfonate 7%, Fatty alcohol polyoxyethylene ether 6%, the lipophilic-hydrophilic balance value of the fatty alcohol polyoxyethylene ether is 2-4, sulfonated castor oil soap 7%, polyol oleate 8%, sulfurized fatty acid ester 5 %, 40℃ kinematic viscosity is 10-32mm 2 / s naphthenic oil 10%, benzotriazole 0.5%, emulsified silicone oil 0.2%, water balance, the preparation method includes the following steps:

[0018] 1) Add boric acid, diethanolamine, triethanolamine, and water into the reaction tank in proportions, and stir for 30 minutes at 40°C;

[0019] 2) Add 60% sodium petroleum sulfonate, fatty alcohol polyoxyethylene ether, sulfonated castor oil soap, polyol oleate, sulfurized fatty acid ester, benzotriazole and emulsified silicone oil to the n...

Embodiment 2

[0022] A preparation method of a microemulsion cutting fluid with good oil drainage, the cutting fluid is composed of the following components by weight percentage: diethanolamine 7%, triethanolamine 4%, boric acid 9%, 60% petroleum sodium sulfonate 5%, Fatty alcohol polyoxyethylene ether 8%, the lipophilic-hydrophilic balance of the fatty alcohol polyoxyethylene ether is 2-4, sulfonated castor oil soap 5%, polyol oleate 10%, sulfurized fatty acid ester 3 %, 40℃ kinematic viscosity is 10-32mm 2 / s naphthenic oil 12%, benzotriazole 0.3%, emulsified silicone oil 0.4%, water balance, the preparation method includes the following steps:

[0023] 1) Add boric acid, diethanolamine, triethanolamine, and water into the reaction tank in proportion, and stir at 50°C for 20 minutes;

[0024] 2) Add 60% sodium petroleum sulfonate, fatty alcohol polyoxyethylene ether, sulfonated castor oil soap, polyol oleate, sulfurized fatty acid ester, benzotriazole and emulsified silicone oil to the naphthe...

Embodiment 3

[0027] A preparation method of microemulsion cutting fluid with good oil drainage, the cutting fluid is composed of the following components by weight percentage: diethanolamine 6%, triethanolamine 5%, boric acid 8%, 60% petroleum sodium sulfonate 6%, Fatty alcohol polyoxyethylene ether 7%, the lipophilic-hydrophilic balance value of the fatty alcohol polyoxyethylene ether is 2-4, sulfonated castor oil soap 6%, polyol oleate 9%, sulfurized fatty acid ester 4 %, 40℃ kinematic viscosity is 10-32mm 2 / s naphthenic oil 11%, benzotriazole 0.4%, emulsified silicone oil 0.3%, water balance, the preparation method includes the following steps:

[0028] 1) Add boric acid, diethanolamine, triethanolamine, and water into the reaction tank in proportion, and stir at 45°C for 25 minutes;

[0029] 2) Add 60% sodium petroleum sulfonate, fatty alcohol polyoxyethylene ether, sulfonated castor oil soap, polyol oleate, sulfurized fatty acid ester, benzotriazole and emulsified silicone oil to the naph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Kinematic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a microemulsion cutting fluid with good oil extraction performance. The method comprises steps of: 1) adding 7-9% of boric acid, 5-7% of diethanol amine, 4-6% of triethanolamine and water in a certain proportion into a reaction tank, and stirring at 40-50 DEG C for 20-30 min; 2) successively adding 5-7% of petroleum sodium sulfonate with concentration of 60%, 6-8% of fatty alcohol-polyoxyethylene ether, 5-7% of sulfonated castor oil soap, 8-10% of polyol oleate, 3-5% of sulfurized aliphatic ester, 0.3-0.5% of benzotriazole and 0.2-0.4% of emulsified silicone oil into 10-12% of naphthenic oil at 40-50 DEG C, and stirring for 30-40 min; and 3) cooling the mixture obtained in the step 2 ) to 30-35 DEG C, then adding the mixture from the step 1), and stirring for 60-90 min.

Description

Technical field [0001] The invention relates to the technical field of metal cutting processing, in particular to a preparation method of a microemulsion cutting fluid with good oil drainage. Background technique [0002] Cutting fluids are divided into two categories: non-water-soluble (oil-based) fluids and water-soluble (water-based) fluids according to the chemical composition of the oil. The oil-based cutting fluid has better lubrication performance and poor cooling effect. Compared with oil-based cutting fluid, water-based cutting fluid has relatively poor lubrication performance and better cooling effect. [0003] Emulsion combines the lubricity and anti-rust properties of oil with the excellent cooling properties of water, and at the same time has good lubrication and cooling properties, so it is very effective for high-speed and low-pressure metal cutting with a large amount of heat. Compared with oil-based cutting fluids, the advantages of emulsions are greater heat dis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M173/00C10N40/22C10N30/12C10N30/04C10N30/06
Inventor 林伟江海涛江海波江浩
Owner TIANCHANG RUNDA METAL ANTIRUST AUX
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products