High-viscosity poly alpha-olefin synthetic oil (PAO) and preparation method thereof

A technology for olefin synthesis oil and olefin, which is applied in the production of liquid hydrocarbon mixture, petroleum industry, etc., can solve the problems of expensive catalyst, inability to separate catalyst and product, and high product cost, achieve low molecular weight distribution, reduce production cost, The effect of reducing pollution

Active Publication Date: 2015-02-25
CHINA PETROLEUM & CHEM CORP +1
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the reaction, the catalyst and the product still cannot be separated, and the catalyst is expensive, so the cost of obtaining the product is very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-viscosity poly alpha-olefin synthetic oil (PAO) and preparation method thereof
  • High-viscosity poly alpha-olefin synthetic oil (PAO) and preparation method thereof
  • High-viscosity poly alpha-olefin synthetic oil (PAO) and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Preparation of triethylamine acidic ionic liquid of chloroaluminate hydrochloride:

[0044] Add 40.4g of dry triethylamine hydrochloride into a 500ml round-bottomed flask, keep the temperature not higher than 80°C under a nitrogen atmosphere, add 97.8g of aluminum trichloride to the round-bottomed flask in batches, the anion-cation molar ratio is 2.5: 1. Keep magnetic stirring for 12 hours, and store under dry conditions for later use. The molecular structure of the ionic liquid is shown in formula (4), and it is called triethylamine chloroaluminate hydrochloride ionic liquid.

[0045] Formula (4)

Embodiment 2

[0047] Preparation of Triethylbenzylammonium Chloroaluminate Acidic Ionic Liquid:

[0048] Add 36.9g of dry triethylbenzyl ammonium chloride into a 500ml round bottom flask, keep the temperature not higher than 80°C under nitrogen atmosphere, add 26.0g of aluminum trichloride into the round bottom flask in batches, anion and cation The molar ratio was 1.2:1, kept under magnetic stirring for 12 hours, and stored under dry conditions for future use. The molecular structure of the ionic liquid is shown in formula (5), and it is called triethylbenzyl ammonium chloroaluminate ionic liquid.

[0049]

Embodiment 3

[0052] Weigh 0.2 g of the ionic liquid in Example 1 and add it to a 250 ml three-necked round-bottomed flask, put the round-bottomed flask into a low-temperature reaction bath, keep the temperature at 0° C., pass nitrogen gas to maintain an inert atmosphere, and stir mechanically. Weigh 40g of 1-decene and add it into the feeding tube so that the weight ratio of α-olefin to ionic liquid is 200:1, and keep a constant dropping rate into the flask. After reacting for 180min, the three-neck flask is allowed to stand for stratification and separated. Take out the upper layer polymer, add 1% NaOH aqueous solution to inactivate the ionic liquid remaining in the polymer, wash the polymer product with water, analyze its composition with GPC after drying, and then remove the unreacted monomer and dimer by distillation under reduced pressure , and then hydrogenated to obtain a colorless and transparent poly-alpha-olefin synthetic oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pour pointaaaaaaaaaa
pour pointaaaaaaaaaa
viscosity indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a poly alpha-olefin synthetic oil (PAO) and a preparation method thereof. The preparation method comprises the following steps of contacting alpha-olefins with an ionic liquid at a temperature of -10-100 DEG C to form a polymerization reactant; separating the polymerization reactant from the ionic liquid; and distilling the polymerization reactant and hydrorefining, thus obtaining the poly alpha-olefin synthetic oil. The ionic liquid is composed of anionic components and cationic components, wherein the anionic components are one or more selected from aluminum trichloride, alkyl aluminium, halogenated alkyl aluminium and aluminium bromide; the cationic components are one or more selected from alkylammonium salts; the molar ratio of the anionic components and cationic components is 1-3 : 1; the mass ratio of poly alpha-olefin and the ionic liquid is 1-200 : 1; and reaction time is 15-360 min. Kinematic viscosity at 100 DEG C (K.V[100 DEG C]) of the obtained PAO is larger than 50 mm<2> / s. The high-viscosity PAO product is provided.

Description

technical field [0001] The present invention relates to synthetic oils, in particular to a 6 ~C 16 Poly-alpha-olefin synthetic oil produced from olefin as raw material and its preparation method. Background technique [0002] Poly-α-olefin synthetic oil (PAO for short) is a kind of synthetic hydrocarbon lubricating oil, mainly composed of C 6 ~C 16 The α-olefins are polymerized under the action of a catalyst, and then hydrogenated to obtain regular long-chain alkanes. Known for their molecular stability, PAOs are superior to mineral base oils in lubricant applications. The lower molecular weight distribution makes it have lower volatility, and it will not cause oil loss due to evaporation under high temperature conditions, resulting in thickening of lubricating oil and increased fuel consumption; the multi-branched isoparaffin structure endows it with excellent Low-temperature viscosity and very low pour point, thereby reducing the impact on engine parts and batteries s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10G50/02
Inventor 张耀段庆华刘依农李玲
Owner CHINA PETROLEUM & CHEM CORP