Halogen-free flame-retardant elastomer composition

An elastomer and composition technology, applied in the direction of organic insulators, etc., can solve problems such as affecting product quality, unable to stabilize production or processing, and reducing production efficiency.

Active Publication Date: 2012-11-28
KINGFA SCI & TECH CO LTD +2
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compositions using powdered phosphorus- or nitrogen-containing flame retardants such as melamine cyanurate, melamine phosphate, ammonium polyphosphate, phosphinate, or diphosphinate can produce " Coke" precipitates, which will reduce production efficiency and affect product quality
Chinese patent CN101827885A discloses a flame retardant composition, with piperazine and melamine (poly/pyro) phosphate compound, silicone oil, and monoamide compound of higher aliphatic monocarboxylic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame-retardant elastomer composition
  • Halogen-free flame-retardant elastomer composition
  • Halogen-free flame-retardant elastomer composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0068] The present invention will be further described below through specific embodiments. The following examples are preferred implementation forms of the present invention, but the implementation manners of the present invention are not limited by the following examples.

[0069] The raw materials used in the examples and comparative examples are now described as follows, but not limited to these materials:

[0070] Grade Introduction SKYPEL G155D Thermoplastic polyester elastomer, Shore D hardness is 55D, obtains commercially from SK company SKYPEL G130D Thermoplastic polyester elastomer, ShoreD hardness is 30D, obtains commercially from SK company Kraton A1536HS Styrene-ethylene / butylene-styrene block copolymer, commercially available from Kraton Corporation SEBS 6150 Styrene-ethylene / butylene-styrene block copolymer, commercially available from Taiwan Image INFUSE 9817 Polyolefin elastomer, commercially available from DOW Corpor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a halogen-free flame-retardant elastomer composition. The halogen-free flame-retardant elastomer composition comprises the following components in percentage by weight: 15-70% of thermoplastic polyester elastomer, 0-50% of styrene type elastomer and/or polyolefin type elastomer, 25-40% of flame retardant and 2-5% of processing aids, wherein the flame retardant is of a mixture containing piperazine phosphate, melamine phosphate and ammonium polyphosphate. The halogen-free flame-retardant elastomer composition disclosed by the invention can effectively inhibit the precipitation of coke charge during the processing process and improve the processing performances of the composition, has the characteristics of high halogen-free flame-retardant grade, good mechanical properties, good anti-aging performance and easiness in extrusion molding and processing, and is very suitable for power cords, data transmission lines and the like of high-end consumptive electronic and electrical appliances.

Description

technical field [0001] The invention relates to an elastomer composition, in particular to a halogen-free flame-retardant elastomer composition and its application. Background technique [0002] Halogenated compounds such as polyvinyl chloride (PVC) and neoprene have excellent flame retardant properties and are widely used in the wire industry, but they will produce a large amount of toxic gases during fire or incineration, which will cause great damage to the human body and the environment. Hazard, recently, the demand for halogen-free flame-retardant elastomers used to replace PVC wire and cable materials has exploded. [0003] At present, there are many composite materials specially developed for halogen-free flame-retardant wires, such as polyolefin / inorganic flame retardant (due to the need to add a large amount of flame retardant, which affects the mechanical properties of the composite, such as insufficient flexibility and elasticity), poly Olefin or elastomer / intume...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/00C08L51/00C08L23/16C08L23/12C08L23/00C08L23/08C08L23/20C08L83/04C08K13/02C08K5/521C08K5/3492C08K3/32C08K5/20C08K5/101C08K5/103H01B3/18
Inventor 黄恒梅王林李玉虎郭少华胡志华付锦锋蔡彤旻叶南飚
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products