Tin-zinc hot dipping fuel-tank high-strength steel plate with good corrosion resistance and manufacturing method thereof

A technology of high-strength steel plate and manufacturing method, applied in hot-dip galvanizing process, manufacturing tools, heat treatment furnace, etc., can solve the problems of complex shape, zinc clogged fuel filter, poor welding performance, etc., achieve good corrosion resistance, overcome harmful The effect of action

Active Publication Date: 2014-12-31
ANGANG STEEL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

2) Stamping and forming fuel tanks are mostly located under the vehicle body and in the narrow space, and the shape is often very complex, so the motherboard is required to have excellent mechanical properties and surface lubrication properties
Although the cost of hot-dip galvanized steel is low and the corrosion resistance is good, zinc is not a good material for the corrosion resistance of the fuel inside the fuel tank. Zinc will be corroded by water or deteriorated gasoline, which will easily clog the fuel filter. white rust
In addition, the zinc in the zinc coating tends to stain the Cu electrode, so the welding performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tin-zinc hot dipping fuel-tank high-strength steel plate with good corrosion resistance and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The chemical composition of the steel is shown in Table 1. The annealing process is 820°C for 20 seconds, cooled to 320°C at a rate of 50°C per second and held for 60 seconds, then hot-dipped. The temperature of the bath is 300°C, and the zinc content of the bath is 8wt. .%, the balance is tin and unavoidable impurities, air knife purging after leaving the plating solution, air cooling to room temperature, the structure is ferrite + bainite + austenite, and its volume content is 69%-83% %, 15%-23%, 2%-5%.

Embodiment 2

[0033] The chemical composition of the steel is shown in Table 1. The annealing process is 800°C for 40 seconds, cooled to 300°C at a rate of 20°C per second and held for 20 seconds, then hot-dipped. The temperature of the bath is 290°C, and the zinc content of the bath is 10 %wt.%, the balance is tin and unavoidable impurities, air knife purging after leaving the plating solution, air cooling to room temperature, the structure is ferrite + martensite + bainite, the volume content is 56% respectively -68%, 20%-30%, 5%-20%.

Embodiment 3

[0035] The chemical composition of the steel is shown in Table 1. The annealing process is 780°C for 60 seconds, cooled to 280°C at a rate of 70°C per second and held for 50 seconds, then hot-dipped. The temperature of the bath is 270°C, and the zinc content of the bath is 12wt. .%, the balance is tin and unavoidable impurities, air knife purging after leaving the plating solution, air cooling to room temperature, the structure is ferrite + bainite + martensite, and its volume content is 50%-80% %, 15%-25%, 15%-35%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tin-zinc hot dipping fuel-tank high-strength steel plate with good corrosion resistance and a manufacturing method thereof. The steel plate comprises the following elements of: by weight, 0.02-0.10% of C, Si being less than or equal to 0.30%, 0.20-2.50% of Mn, P being less than or equal to 0.10%, S being less than or equal to 0.05%, 0.05-0.50% of Cr, 0.02-1.00% of Ni, 0.02-0.50% of Cu, 0.02-0.50% of Mo, Ti being less than or equal to 0.15%, Nb being less than or equal to 0.15%, and the balance Fe and other unavoidable impurities. The steel plate is prepared by process route of smelting, casting, hot rolling, cold rolling and continuous tin-zinc hot dipping. During the continuous annealing process, a steel band is heated to a two-phase region and is insulated for 10-100s while the temperature is 700-850 DEG C; then, the steel band is rapidly cooled to 300+ / -50 DEG C at the cooling rate of 10-100 DEG C / s, is insulated for 0-150s, undergoes tin-zinc hot dipping at the temperature of 280+ / -30 DEG C, and is finally air-cooled to room temperature after the plating process. The invention has the following advantages and effects: the disadvantage that a traditional lead-containing coated steel plate is harmful to the environment and a IF steel plate has low strength is overcome, and simultaneously the high-strength steel plate provided by the invention has good corrosion resistance and formability.

Description

technical field [0001] The invention belongs to the technical field of hot-dip plating of steel plates, and in particular relates to a high-strength steel plate for hot-dip tin-galvanized fuel tanks with good corrosion resistance and a manufacturing method thereof. Background technique [0002] Steel plates for fuel tanks are a special class of materials, most of which are surface-treated steel plates. The properties required for this type of steel plate are: 1) Corrosion resistance This not only requires resistance to external atmospheric, coastal and other environmental corrosion, but also must be resistant to fuel and moisture corrosion inside the fuel tank. 2) Stamping formability Fuel tanks are mostly located under the car body and in the narrow space, and the shape is often very complex, so the motherboard is required to have excellent mechanical properties and surface lubrication properties. 3) Weldability In the manufacturing process of the fuel tank, seam welding b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/60C22C38/58C22C38/50C22C38/48C22C38/44C21D1/26C21D9/52C23C2/08
Inventor 李锋吕家舜杨洪刚
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap