Cloud wire coating and preparation method thereof

A technology of cloud silk and formula, applied in the direction of coating, etc., can solve the problems of peeling of paint film, broken silk, insufficient acid and alkali resistance and scrub resistance.

Inactive Publication Date: 2013-01-16
WUHU SHUANGBAO BUILDING MATERIAL
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many impurities and particles in the existing cloud silk paint, the paint quality is not delicate, broken wires and tears are common during wire drawing, and peeling and cracking of the paint film also occur from time to time. Scrub resistance often cannot meet the requirements of actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] A kind of cloud silk paint, which is prepared by proportioning the following raw material components in parts by weight: hydroxyethyl cellulose (Shandong Yutian Chemical Co., Ltd.) 5.5, AMP-95 (Nanjing Gutian Chemical Co., Ltd.) 2.5, PE100 wetting agent (Guangzhou Hengyu Chemical Co., Ltd.) 2.5, film-forming aid alcohol ester 12 (Guangzhou Xuanning Chemical Technology Co., Ltd.) 20, Kasong preservative KF-88 (Guangzhou Yuedi Chemical Co., Ltd.) 2, ethylene glycol (Jinanhui World Chemical Co., Ltd.) 14. NXZ type defoamer (Taiwan Zhongya Chemical Co., Ltd.) 2.5, pearl powder (Merck, Germany) 200, S-40 polystyrene emulsion (Xinhui Chemical Factory, Xinhui District, Jiangmen City Co., Ltd.) 425, ASE-60 thickener (Rohm and Haas) 4, sodium salt dispersant KMW-B1 (Guangzhou Shote Chemical Co., Ltd.) 6, deionized water 300.

[0080] Above-mentioned cloud silk paint is prepared according to the following method:

[0081] (1) Weigh the amount of deionized water into the reaction...

Embodiment 2

[0088] A kind of cloud silk paint, characterized in that it is composed of raw material components including the following parts by weight: cellulose acetate butyrate (Tianjin Xiens Biochemical Technology Co., Ltd.) 7, AMP-95 (Nanjing Gutian Chemical Co., Ltd. ) 1. Span-80 (Dow Chemical) 4. Coalescent propylene glycol methyl ether (Yangzhou Eurasia Chemical Industry Co., Ltd.) 15. Preservative MIT (Guangzhou Chunmei Chemical Co., Ltd.) 3. Ethylene glycol (Jinan Huishi Chemical Co., Ltd. Company) 8. SRE CN silicone defoamer (Wacker Chemicals) 4. Pearlescent powder (Merck, Germany) 150, acrylic emulsion (Shandong Future Chemical Technology Co., Ltd.) 500, DR-72 thickener (Rohm Haas) 2. Sodium salt dispersant SN-5040 (Taiwan Zhongya Chemicals Co., Ltd.) 9. Deionized water 200.

[0089] Above-mentioned cloud silk paint is prepared according to the following method:

[0090] (1) Weigh the amount of deionized water into the reaction kettle, start the high-speed disperser, and contr...

Embodiment 3

[0097] A cloud silk paint, which is characterized in that it is composed of the following raw material components in proportion by weight: carboxymethyl cellulose (Zibo Hailan Chemical Co., Ltd.) 4, AMP-95 (Nanjing Gutian Chemical Co., Ltd.) 4 , AES (Guangzhou Gongxin Chemical Co., Ltd.) 1. Coalescent propylene glycol butyl ether (Jinan Yuxing Fine Chemical Co., Ltd.) 25. Preservative benzoic acid (Guangzhou Sibo Chemical Co., Ltd.) 1. Ethylene glycol (Jinanhui World Chemical Co., Ltd.) 20, BASF LF43 defoamer (BASF Co., Ltd., Germany) 1, pearl powder (Merck, Germany) 240, silicone acrylic resin (Wujiang Heli Resin Co., Ltd.) 350, polyurethane thickener 621N (Shanghai Jiyi Chemical Co., Ltd.) 6. Sodium hexametaphosphate dispersant (Shandong Weifang Xinfa Chemical Co., Ltd.) 3. Deionized water 400.

[0098] Above-mentioned cloud silk paint is prepared according to the following method:

[0099] (1) Weigh the amount of deionized water into the reaction kettle, start the high-spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cloud wire coating and a preparation method of the cloud wire coating. The cloud wire coating comprises the following raw constituents by weight: 4-7 parts of cellulose, 1-4 parts of AMP-95, 1-4 parts of wetting agent, 15-25 parts of coalescing agent, 1-3 parts of preservatives, 8-20 parts of ethylene glycol, 1-4 parts of defoamer, 150-240 parts of pearl powder, 350-500 parts of emulsion, 2-6 parts of thickeners, 3-9 parts of dispersing agent and 200-40 parts of deionized water. The cloud wire coating disclosed by the invention is fine and smooth in quality, and prevents the phenomena of wire fracture and tearing during wire drawing; with the coating, a film can be well adhered, and the seaming, the peeling and the cracking are prevented; and particularly, the coating has strong scrub resistance, water resistance and alkali resistance.

Description

technical field [0001] The invention belongs to the coating class in the chemical category, relates to the field of water-based art coatings, in particular to a cloud silk paint and a preparation method thereof. Background technique [0002] Cloud paint is a water-based art paint that is applied to the wall by using special tools such as spray guns and airbrushes and special techniques. The lacquer is non-toxic and tasteless, and the coating film has the advantages of strong adhesion, scrub resistance, and no fading. However, there are many impurities and particles in the existing cloud silk paint, the paint quality is not delicate, broken wires and tears are common during wire drawing, and peeling and cracking of the paint film also occur from time to time. Scrub resistance often cannot meet the requirements of actual use. Contents of the invention [0003] One of the objectives of the present invention is to address the deficiencies of the prior art, to provide a fine ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/06C09D133/00C09D133/04C09D7/12C09D5/28
Inventor 胡昌悌
Owner WUHU SHUANGBAO BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products