A seawater and paint-resistant technology, applied in the field of paint, can solve problems such as cracks and metal fractures, and achieve the effects of reducing permeability, reducing transmittance, and excellent seawater corrosion resistance

Inactive Publication Date: 2013-01-16
WUJIANG HUACHENG COMPOSITE MATERIAL SCI & TECH
View PDF3 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under the action of tensile stress on the metal, cracks will appear in the area where the passivation film is destroyed, which will become the anode area of ​​the corrosion battery. Continuous electrochemical corrosion may eventually lead to the fracture of the metal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seawater corrosion-resistant paint
  • Seawater corrosion-resistant paint
  • Seawater corrosion-resistant paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Prepare the components according to the weight ratio shown in Table 1.

[0024] Table 1 The weight ratio of Example 1 to Example 3

[0025]

[0026] The molecular weight of the above-mentioned polyvinyl acetate is 200,000 to 300,000.

[0027] The above-mentioned defoaming agent is tributyl phosphate.

[0028] The aforementioned coupling agent is silane coupling agent TM-30.

[0029] The epoxy resin is epoxy resin E-42.

[0030] The curing agent adopts phenolic hexamethylene diamine.

[0031] The solvent is ethyl acetate.

[0032] The preparation method is:

[0033] S1: Take chloroprene rubber, polytetrafluoroethylene, polyvinyl acetate, add half the weight of the solvent, and stir evenly;

[0034] S2: Add epoxy resin, petroleum resin, coupling agent, defoamer, and silica sol to the mixture obtained in S1, and stir it evenly at a speed of 600-1000 rpm;

[0035] S3: Add cerium nitrate, montmorillonite, red iron oxide, zinc phosphate, barium sulfate, aluminum tripolyphosphate, titanium ox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides seawater corrosion-resistant paint which comprises component A and component B. The component A comprises the following materials by weight: 20-30 parts of epoxy resin, 10-20 parts of petroleum resin, 5-10 parts of chloroprene rubber, 3-6 parts of polytetrafluoroethylene, 2-8 parts of polyvinyl acetate, 2-4 parts of a coupling agent, 1-2 parts of a defoaming agent, 5-8 parts of silica sol, 1-2 parts of cerium nitrate, 1-2 parts of montmorillonite, 1-2 parts of iron red, 4-6 parts of zinc phosphate, 2-3 parts of barium sulfate, 3-4 parts of aluminum tripolyphosphate, 1-2 parts of titanium oxide, 4-7 parts of zinc oxide, 25-35 parts of and solvent. The component B comprises the following materials by weight: 20-35 parts of a curing agent, and 15-20 parts of butanol. The inventive paint has excellent seawater corrosion resistance, salt fog resistance above 2,000 hr, 10% NaOH solution resistance above 30 days, and artificial seawater resistance above 4,200 hr.

Description

Technical field [0001] The invention provides a seawater corrosion-resistant paint, which belongs to the technical field of paint. Background technique [0002] The ocean can provide mankind with material resources, space resources and energy for survival and development. my country is a large maritime country with a coastline of more than 18,000 kilometers, more than 6,500 coastal islands, and a maritime area under its jurisdiction of more than 3 million square kilometers. my country has abundant marine resources and a thriving marine industry, but the marine environment is very harsh and highly corrosive. Therefore, marine corrosion and protection are issues that urgently need to be resolved in my country’s economic development. [0003] Most ships use metal shells. In the marine environment, metal is affected by seawater temperature, seawater content, ocean atmospheric temperature, and ocean atmospheric humidity. The degree of corrosion is very serious. Corrosion not only reduc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D157/02C09D111/00C09D127/18C09D131/04C09D7/12C09D5/08
Inventor 肖伟荣
Owner WUJIANG HUACHENG COMPOSITE MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap