Modified Rosin Resin

A technology for modifying rosin and resin, applied in the field of rosin resin, can solve problems such as poor fluidity and easy discoloration of road paint, and achieve the effects of reducing carbon emissions, reducing oxidative discoloration, and being beneficial to environmental protection

Inactive Publication Date: 2015-10-28
DRAGON FISH PAINT
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a modified rosin resin, which can solve the problems of easy discoloration and poor fluidity in the actual production and application of road paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1--making 4000 kilograms of modified rosin resins:

[0014] Raw materials used: 2200 kg of primary rosin; 400 kg of fumaric acid; 600 kg of glycerin; 794 kg of low iodine value fatty acid; 0.4 kg of anthraquinone; 2,6-di-tert-butyl-p-cresol 2 kg; 4,4-bis(6-tert-butyl-m-cresyl)thiophenol 1.2 kg; Trinonylphenyl phosphite 0.4 kg.

[0015] The production steps are:

[0016] (1) Put 2,200 kg of first-grade rosin into the melting kettle, pass through carbon dioxide gas protection, heat up to 200°C to melt the rosin, and pump it into the esterification pot after it is completely melted;

[0017] (2) Keep feeding carbon dioxide gas protection, start stirring, put in 400 kg of fumaric acid, raise the temperature to 200°C, and keep it warm for 1 hour;

[0018] (3) Add 0.4 kg of anthraquinone, 2 kg of tris(2,4-di-tert-butylphenyl) phosphite, 0.6 kg of 4,4-bis(6-tert-butyl-m-tolyl)thiophenol, 600 kg of glycerin, 794 kg of low iodine value fatty acids, slowly heated up...

Embodiment 2

[0021] Embodiment 2--making 4000 kilograms of modified rosin resins:

[0022] Raw materials used: 2400 kg of primary rosin; 200 kg of fumaric acid; 992.8 kg of glycerin; 400 kg of low iodine value fatty acid; 2 kg of anthraquinone; ; 0.4 kg of 2,6-di-tert-butyl-p-cresol; 2 kg of 4,4-di(6-tert-butyl-m-cresyl)thiophenol; 2 kg of trinonylphenyl phosphite.

[0023] The production steps are:

[0024] (1) Put 2,400 kg of first-grade rosin into the melting kettle, pass in carbon dioxide gas protection, heat up to 200°C to melt the rosin, and pump it into the esterification pot after it is completely melted;

[0025] (2) Keep feeding carbon dioxide gas protection, start stirring, put in 200 kg of fumaric acid, raise the temperature to 200°C, and keep it warm for 1 hour;

[0026] (3) Add 2 kg of anthraquinone, 0.8 kg of tris(2,4-di-tert-butylphenyl) phosphite, 1 kg of 4,4-bis(6-tert-butyl-m-cresyl)thiophenol, 992.8 kg of glycerin, 400 kg of low iodine value fatty acids, slowly heate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified rosin resin and belongs to the technical field of chemical industry. The modified rosin resin comprises, by weight, 55-60% of first-grade rosin, 5-10% of fumaric acid, 15-24.82% of glycerol, 10-20% of low-iodine-value fatty acid, 0.01-0.05% of anthraquinone, 0.02-0.05% of tri-(2, 4-di-tertiary butyl phenyl) phosphite ester, 0.01-0.05% of 2, 6- di-tertiary butyl p-cresol, 0.03-0.05% of 4, 4-di-(6-tertiary butyl-m-methylphenyl) thiophenol, and 0.01-0.05% of tri-nonyl phenyl phosphite ester. The modified rosin resin can solve the problem that road paint prepared is prone to discolor and poor in liquidity during actual production and application processes.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a rosin resin used for producing road paint. Background technique [0002] Generally, the modified rosin resin used in the production of horse route paint is through the addition reaction of rosin and maleic anhydride or fumaric acid, so that the conjugated double bond disappears, the chemical properties are stable, and the tendency of oxidative discoloration is reduced, and then it is esterified with polyols. Chemical reaction, reduce the acid value of the product, increase the softening point, so as to meet the use requirements. However, due to the easy oxidation of rosin, there are still problems in the actual production and application of road paints such as easy discoloration after paint making and poor fluidity. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a modified rosin resin, which can solve th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D193/04C09D7/12C09F1/04
Inventor 周绍忠李英松韦光南苏丽董春霞陈兆阳黄冕
Owner DRAGON FISH PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap