3003 reflective foil aluminum alloy

A processing technology and aluminum alloy technology, which is applied in the field of 3003 reflective foil aluminum alloy and its processing technology, can solve the problems of complex smelting casting and rolling technology and high production cost, and achieve the advantages of popularization and application, reduction of production cost and good energy saving effect. Effect

Active Publication Date: 2013-02-06
新疆天展新材料科技有限公司
View PDF10 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the above disclosed invention patent, in its technical solution, 1070A alloy is selected as the material for producing solar aluminum foil. The production cost of this material is relatively high, and the melting and casting technology is relatively complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 3003 reflective foil aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0037] A 3003 reflective foil aluminum alloy, the aluminum alloy contains the following chemical components:

[0038]

[0039] A kind of processing technology of 3003 reflective foil aluminum alloy, its technology comprises following processing steps:

[0040] The first step: ingredients, the raw materials are prepared according to the above chemical composition and ratio;

[0041]The second step: smelting, adding the qualified aluminum ingots and scraps into the flame reverberatory furnace, stirring fully after heating and melting, and analyzing the components when the temperature reaches 735°C, adding Fe, Si, Cu, Mn, The components of Zn, Ti and Mg are adjusted; the temperature is adjusted after the components are qualified, and the temperature of the molten aluminum alloy is 755°C.

[0042] The third step: Refining in a static furnace, transfer the aluminum alloy melt to the static furnace for 10 minutes and then carry out a nitrogen powder spraying refining, the refini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a 3003 reflective foil aluminum alloy. The aluminum alloy comprises silicon, iron, copper, manganese, zinc, magnesium, titanium, and inevitable impurities, and the balance being aluminum. A processing technology includes preparing raw materials, smelting, smelting in a holding furnace, grain refinement, online degassing and deslagging, filteration deslagging, continuous casting and rolling, cold rolling, finish rolling, cutting and packing. Though configuration of the above-mentioned material composition and the processing technology arrangement, the processed aluminum foil is enabled to obtain a large amount of small, uniform, and dispersed two-phase compounds and worked structures with uniform deformation; by using the potential difference between the two-phase compounds and an Al matrix electrode, an appearance of uniform and intensive corrosion pits is achieved for increasing the specific surface area of the aluminum alloy foil through a chemical corrosion treatment; and by using worked structures with uniform deformation, that the surface of the aluminum alloy foil has a high surface quality with uniform color after the corrosion treatment is guaranteed.

Description

technical field [0001] The invention relates to a processing technology of an aluminum alloy material and an aluminum alloy plate, in particular to a 3003 reflective foil aluminum alloy and a processing technology thereof. Background technique [0002] Increasing the specific surface area of ​​aluminum alloy foil is the key technology to increase the heat absorption area of ​​the core material of solar flat collectors. Its main purpose is to form dense porous W, Mo / Al on the surface of aluminum foil. 2 o 3 Coating, so that the size of the discontinuous void on the surface is equivalent to the peak of the visible spectrum (the energy of solar radiation is mainly distributed in the spectral region with a wavelength λ of 0.25 to 3 μm), thereby trapping visible light and improving the absorption of solar energy Rate. [0003] In the prior art, there are two manufacturing methods for increasing the specific surface area of ​​aluminum alloy foil, physical method and chemical met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/02C22F1/04
Inventor 吴丹彭映平黄元春王民生黄善球
Owner 新疆天展新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com