Production process of Japanese paper adhesive tape base paper

A production process, the technology of paper tape, applied in the field of papermaking, can solve the problems of poor paper softness, low high-temperature anti-aging degree, high production cost, etc., and achieve the effects of cost reduction, good water permeability and improved softness

Inactive Publication Date: 2013-02-13
杭州新兴纸业有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The base paper of washi tape used in China mainly depends on imports, and there are few domestic manufacturers.
At the same time, the current domestic production of washi tape base paper has disadvantages such as poor softness of paper, low high-temperature anti-aging degree, and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] a 100% pure Canadian northern wood pulp is decomposed and beaten to obtain a slurry with a concentration of 3.5% and a degree of percussion of 18oSR;

[0020] b Then the polyester chemical fiber is decomposed by a deflagging machine, and mixed with the slurry obtained in step a to obtain a mixed slurry with a concentration of 2%, and the addition of the polyester chemical fiber is 3% of the total mass of the mixed slurry;

[0021] c. Add 3.0% of the total weight of the mixed slurry into the mixed slurry and mix it evenly with an appropriate amount of polyethylene oxide, and then form it through the inclined wire papermaking network, press for dehydration, and dry in a large cylinder (the surface temperature of the dryer is controlled at 107 ℃ -113°C range), coiling, rewinding and cutting to obtain 28g / ㎡ base paper for papermaking;

[0022] d After the base paper is dipped by the coating machine, it is coated with latex with a glass transition temperature of minus 27°C, ...

Embodiment 2

[0024] a 100% pure Canadian northernwood wood pulp is decomposed and beaten to obtain a slurry with a concentration of 3.7% and a degree of percussion of 20oSR;

[0025] b Then the polyester chemical fiber is decomposed by a deflagging machine, and mixed with the slurry obtained in step a to obtain a mixed slurry with a concentration of 2.5%, and the addition of the polyester chemical fiber is 2.5% of the total mass of the mixed slurry;

[0026] c. Add 3.0% of the total weight of the mixed slurry into the mixed slurry and mix it evenly with an appropriate amount of polyethylene oxide, and then form it through the inclined wire papermaking network, press for dehydration, and dry in a large cylinder (the surface temperature of the dryer is controlled at 107 ℃ -113°C range), coiling, rewinding and cutting to obtain 28g / ㎡ base paper for papermaking;

[0027] d After the base paper is dipped by the coating machine, it is coated with latex with a glass transition temperature of minu...

Embodiment 3

[0029] a 100% pure Canadian northern wood pulp is decomposed and beaten to obtain a slurry with a concentration of 4.0% and a degree of percussion of 19oSR;

[0030] b Then the polyester chemical fiber is decomposed through a deflagging machine, and it is mixed with the slurry obtained in step a to obtain a mixed slurry with a concentration of 2.3%, and the addition of the polyester chemical fiber is 2% of the total mass of the mixed slurry;

[0031] c. Add 3.2% of the total weight of the mixed slurry into the mixed slurry and mix it evenly with an appropriate amount of polyethylene oxide, then form it through the inclined wire papermaking network, press for dehydration, and dry in a large cylinder (the surface temperature of the dryer is controlled at 107°C -113°C range), coiling, rewinding and cutting to obtain 28g / ㎡ base paper for papermaking;

[0032] d After the base paper is dipped by the coating machine, it is coated with latex with a glass transition temperature of min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of Japanese paper adhesive tape base paper. The production process includes steps: a pure wood pulp is subjected to defibering and pulping to obtain size with concentration to be 3.5-4.0% and beating degree to be 18-20 oSR; b polyester chemical fibers are subjected to defibering and mixed with the size obtained from the step a to obtain mixed size with concentration to be 2-2.5%, wherein the filling quantity of polyester chemical fibers is 2-3% of the total mass of the mixed size; c wet strength agents and polyethylene oxide are filled into the mixed size and evenly mixed, then a net portion is formed through inclined wire papermaking, and after squeezing for dehydration, drying in a vat, reeling and rewinding slitting, a piece of papermaking base paper is obtained; and d the base paper is soaked by aid of a coating machine and then is coated with adhesives, the gluing amount is controlled to be in a 10-12g / m<2> range, and after drying, reeling and slitting rewinding, the Japanese paper adhesive tape base paper is obtained. The Japanese paper adhesive tape base paper is soft, high in longitudinal tensile strength and good in water seepage resistance and high temperature ageing resistance.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a production process for washi tape base paper. Background technique [0002] Washi tape base paper is a special paper with high technical content and high added value. Washi tape base paper, weight: 38±3 grams, specification: roll width 950mm. The base paper of washi tape used in China mainly depends on imports, and there are few domestic manufacturers. At the same time, the base paper of washi tape produced in China has disadvantages such as poor softness of paper, low degree of anti-aging at high temperature, and high production cost. Contents of the invention [0003] Due to the defects in the prior art, the present invention provides a production process for washi tape base paper. The washi tape base paper obtained by the process is soft, has a longitudinal tensile strength of not less than 25N / cm, and has good water seepage resistance, High-temperature aging resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21F5/02D21H23/78
Inventor 李建明
Owner 杭州新兴纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More