Preparation method of p-aramid fiber-mica paper

A technology of para-aramid fiber and para-aramid fiber, which is applied in the directions of synthetic cellulose/non-cellulose material pulp/paper, fiber raw material processing, inorganic fiber/sheet, etc., can solve the heat resistance of meta-aramid fiber Limited, it is difficult to meet the requirements of high-end fields, and it is difficult to meet the requirements of C-class insulation grade and above materials to achieve major market prospects and practical significance, excellent liquid phase dispersion performance and composite enhancement effect, and excellent mechanical strength.

Active Publication Date: 2016-05-04
YANTAI METASTAR SPECIAL PAPER
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned patents all introduce the method of using meta-aramid fiber to reinforce mica paper, which improves the mechanical properties or dielectric strength of mica paper to a certain extent. However, due to the limited heat resistance of the meta-aramid fiber body, Its long-term use temperature is 200°C, and it is difficult to meet the requirements of C-class insulation grade and above materials, and it is difficult to meet the use in high-end fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of p-aramid fiber-mica paper
  • Preparation method of p-aramid fiber-mica paper
  • Preparation method of p-aramid fiber-mica paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1 adopts the inventive method to prepare para-aramid fiber mica paper

[0034]Ultrasonic treatment is used to peel the muscovite flakes into mica flakes, the power is 800W, and the time is 10h. The particle size of the mica flakes is classified by a sieve, according to the particle size ratio of ≦20 mesh: 20-40 mesh: ≧40 mesh = Combine at a ratio of 1:6:3, then modify with cationic starch, the mass concentration of cationic starch is 0.01%, the modification time is 60min, the concentration of modified mica slurry is 10%, and the modified mica sheet is obtained after washing. ; Use silane coupling agent to modify the para-aramid chopped fiber with a length of 12mm and a fineness of 1.5D, the mass concentration of the coupling agent is 3%, and the consumption is 0.1% of the dry mass of the relative para-aramid chopped fiber, The modification time was 10 hours, fully decomposed and dispersed, and a slurry A with a mass concentration of 0.01% was prepared; the pa...

Embodiment 2

[0035] Embodiment 2 adopts the method of the present invention to prepare para-aramid fiber mica paper

[0036] Ultrasonic treatment is used to peel mica flakes into mica flakes. The power is 1500W, and the time is 5h. The particle size classification of mica flakes is carried out by a sieving instrument. Combine at a ratio of 2:5:3, and then modify with cationic starch, the mass concentration of cationic starch is 0.05%, the modification time is 30min, the concentration of modified mica slurry is 16%, and the modified mica sheet is obtained by washing after modification; Use a silane coupling agent to modify para-aramid chopped fibers with a length of 12mm and a fineness of 1.5D. The mass concentration of the coupling agent is 5%, the modification time is 5h, and the dosage is 0.5% of the absolute dry mass of the chopped fibers. Fully deconcentrate and disperse to obtain a slurry A with a mass concentration of 0.02%; pass the aramid precipitated fiber with a beating degree of...

Embodiment 3

[0037] Embodiment 3 adopts the method of the present invention to prepare para-aramid fiber mica paper

[0038] Ultrasonic treatment is used to peel off mica flakes into mica flakes. The power is 3000W and the time is 1h. The particle size classification of mica flakes is carried out by a sieving instrument. Combine at a ratio of 3:4:3, and then modify with cationic starch, the mass concentration of cationic starch is 0.1%, the modification time is 10 minutes, the concentration of modified mica slurry is 20%, and the modified mica sheet is obtained by washing after modification; Use a silane coupling agent to modify para-aramid chopped fibers with a length of 12mm and a fineness of 1.5D. The mass concentration of the coupling agent is 10%, the modification time is 1h, and the dosage is 1% of the absolute dry mass of the chopped fibers. Fully deconcentrate and disperse to obtain a slurry A with a mass concentration of 0.05%; pass the aramid precipitated fiber with a beating deg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
dielectric strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a p-aramid fiber-mica paper. The preparation method comprises defibering and dispersing silane coupling agent-modified p-aramid chopped fibers to obtain slurry A, carrying out screening on the p-aramid fibrids with a beating degree of 40-65 degrees SR to obtain slurry B, modifying mica plates through an ionic starch solution to obtain modified mica plates, mixing the slurry A, the slurry B and the modified mica plates to obtain uniform mixed slurry, wherein the uniform mixed slurry comprises, by mass, 10-20% of p-aramid chopped fibers, 20-40% of the p-aramid fibrids and 40-70% of the mica plates, carrying out sizing, dehydration and formation on the mixed slurry, carrying out squeezing and drying and carrying out hot press molding to obtain the p-aramid fiber-mica paper. The p-aramid fiber-mica paper obtained through fiber screening and modification, wet method paper making and hot pressing molding has good evenness, excellent mechanical strength, excellent dielectric breakdown strength and high temperature resistance stability.

Description

【Technical field】 [0001] The invention belongs to the intersection field of papermaking industry and insulation industry, and in particular relates to a preparation method of para-aramid fiber mica paper. 【Background technique】 [0002] With the gradual depletion of high-quality mica resources, mica paper prepared from mica fragments has the characteristics of non-toxic, odorless, corrosion-resistant, aging-resistant, small fluctuations in dielectric strength, high and stable corona inception voltage, and is the most advanced in the world. Ideal high temperature resistant insulating material. Mica paper is a paper-based insulating material prepared by modern paper-making wet papermaking with fine mica sheets as the main raw material. Its forming mainly depends on the van der Waals force and electrostatic force between the mica sheets, resulting in a small mechanical strength of the paper. It is difficult to meet the requirements of use and the production efficiency is low. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H15/12D21H13/26D21H13/38D21F11/00D21H25/04
CPCD21F11/00D21H13/26D21H13/38D21H15/12D21H25/04
Inventor 王典新江明孙岩磊张峻华王川光李宏
Owner YANTAI METASTAR SPECIAL PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap