A bridging agent and ink technology, applied in the field of ink printing, can solve the problems of excessive heavy metals in furniture and easy falling off of UV ink patterns, and achieve the effects of good adhesion, avoiding excessive heavy metals and enhancing adhesion.

Inactive Publication Date: 2013-02-20
广州酷漫居动漫科技有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a UV ink bridging agent, the use of the bridging agent can make the pattern printed on the board have good adhesion and color expression, and solve the problem of UV ink patt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV (ultraviolet) ink bridging agent and application thereof
  • UV (ultraviolet) ink bridging agent and application thereof
  • UV (ultraviolet) ink bridging agent and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Follow the steps below to print UV ink on the melamine board:

[0038] (1) Mix resin, curing agent and solvent according to the weight ratio of 1:0.5:0.8 to obtain bridging agent;

[0039] (2) Put the bridging agent into the spraying equipment for spraying, so that the bridging agent is sprayed onto the clean and dried melamine board;

[0040] (3) Dry the melamine board sprayed with bridging agent at room temperature for 60 minutes;

[0041] (4) Place the dried melamine board in a UV inkjet printer for ink spraying to obtain a sample board.

[0042] Wherein the resin comprises the following components by weight percentage: 45% cottonseed oil modified alkyd resin, 20% nitrocellulose, 28% ethyl acetate, 0.5% tetrafluoroethylene gas phase wax, 6.5% ethylene glycol ethyl ether monobutyl ester ; Curing agent contains 50% low free TDI curing agent raw material, 50% ethyl acetate; butyl ester.

[0043] 2. Formaldehyde content test

[0044] According to GB / T18584-2004, ...

Embodiment 2

[0056] 1. Follow the steps below to print UV ink on the melamine board:

[0057] (1) Mix the resin, curing agent and solvent according to the weight ratio of 1.5:0.25:0.5 to obtain the bridging agent;

[0058] (2) Put the bridging agent into the spraying equipment for spraying, so that the bridging agent is sprayed onto the clean and dried melamine board;

[0059] (3) Dry the melamine board sprayed with bridging agent at room temperature for 60 minutes;

[0060] (4) Place the dried melamine board in a UV inkjet printer for ink spraying to obtain samples.

[0061]Wherein the resin comprises the following components by weight percentage: 40% soybean oil modified alkyd resin, 29.4% nitrocellulose, 25% ethyl acetate, 1% paraldehyde, 0.6% tetrafluoroethylene gas phase wax, 4% Ethylene glycol ethyl ether monobutyl ester; curing agent contains 70% low free TDI curing agent raw material, 30% ethyl acetate; solvent includes the following components in weight percentage: 85% ethyl ace...

Embodiment 3

[0075] 1. Follow the steps below to print UV ink on the melamine board:

[0076] (1) Mix the resin, curing agent and solvent in a weight ratio of 1.5:0.75:0.5 to obtain a bridging agent;

[0077] (2) Put the bridging agent into the spraying equipment for spraying, so that the bridging agent is sprayed onto the clean and dried melamine board;

[0078] (3) Dry the melamine board sprayed with bridging agent at room temperature for 60 minutes;

[0079] (4) Place the dried melamine board in a UV inkjet printer for ink spraying to obtain samples.

[0080] Wherein the resin comprises the following components by weight percentage: 30% soybean oil modified alkyd resin, 30% nitrocellulose, 30% ethyl acetate, 1% tetrafluoroethylene gas phase wax, 8% ethylene glycol ethyl ether monobutyl ester and 1% polyether modified polydimethylsiloxane; the curing agent contains 60% low free TDI curing agent raw material, 40% ethyl acetate; the solvent includes the following components in weight per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a UV (ultraviolet) ink bridging agent and application thereof. The bridging agent comprises resin, a curing agent and a solvent, wherein the resin comprises the following components in percentage by weight: 30-50% of alkyd resin, 10-30% of cellulose nitrate, 20-30% of ester solvent, 0-1.5% of antioxidant, 0-0.8% of tetrafluoroethylene gas-phase wax, 3-8% of diethylene glycol monobutyl ether and 0-1% of leveling agent; the curing agent comprises the following components in percentage by weight: 20-80% of low free TDI (toluene diisocyanate) curing agent raw material and 20-80% of ethyl acetate; and the solvent comprises the following components in percentage by weight: 70-90% of ethyl acetate, 8-20% of ethylene glycol monoethyl ether acetate and 1-10% of diethylene glycol monobutyl ether. The bridging agent provided by the invention is used for the UV ink printing of plates and can effectively enhance the adhesive force of ink on the plates.

Description

technical field [0001] The invention relates to the field of ink printing, in particular to a UV ink bridging agent and its application. Background technique [0002] Most of the current furniture panels use paint for color matching or drawing. However, heavy metals are often contained in paints, such as chrome yellow, dark chrome yellow, cadmium red, molybdenum chrome red and other pigments in colored paints, and driers such as lead epoxy acid and lead isooctanoate are mixed in the preparation process. Therefore, these furniture containing heavy metal paints have the risk of excessive heavy metals. [0003] UV ink is an environmentally friendly ink that does not use solvents, has fast drying speed, good gloss, bright colors, water resistance, solvent resistance and abrasion resistance. Its application scope involves many industries such as furniture. In order to solve the problem of excessive heavy metals in furniture with excessive paint, at present, some researchers use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/08C09D101/18C09D11/02C09D11/30
Inventor 杨涛
Owner 广州酷漫居动漫科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap