Method for preparing antibacterial polyester by use of plant nano-silver

A nano-silver and polyester technology, applied in physical treatment, textile and papermaking, fiber treatment, etc., can solve the problems of not long-lasting antibacterial effect, poor washing resistance, etc., and achieve excellent and durable antibacterial performance, improved dyeing performance, and easy to achieve effects.

Inactive Publication Date: 2014-05-14
SUZHOU UNIV
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The biggest shortcoming of the post-finishing method is that the antibacterial effect of the fabric after finishing is not long enough, and the washability is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing antibacterial polyester by use of plant nano-silver
  • Method for preparing antibacterial polyester by use of plant nano-silver
  • Method for preparing antibacterial polyester by use of plant nano-silver

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Disperse 0.1 g of corn starch in 10 ml of deionized water, stir at 80 ° C until gelatinized to obtain a starch solution, add it to 20 ml of silver ammonia solution with a concentration of 1 wt%, and mix evenly to obtain a starch-silver ammonia composite solution. The solution is placed under the condition of -20°C for freezing treatment, and after it freezes, it is subjected to pulverization treatment to obtain about 30 g of ice powder with a particle size of 1-3 mm.

[0034] The aloe vera leaves are washed and peeled with deionized water to obtain aloe vera inner dan, and then cut into pieces, pulverized, filtered, separated and purified to obtain an aloe vera leaf extract, dispersed in deionized water, and prepared 300 ml of aloe vera with a concentration of 10 wt % Aqueous leaf extract solution, NaOH solution adjusts its pH to 11 to obtain alkaline aloe leaf extract; adding the above ice powder to the alkaline aloe leaf extract, stirring at 40°C for 300min, to obtain ...

Embodiment 2

[0038] Disperse 0.05g of tapioca starch in 5ml of deionized water, stir at 90°C until gelatinized to obtain a starch solution, add it to 20ml of silver ammonia solution with a concentration of 0.5wt%, and mix evenly to obtain a starch-silver ammonia composite solution. The composite solution is frozen at -10°C, and crushed after freezing to obtain about 25g of ice powder with a particle size of 1-3mm.

[0039] Wash and peel the cactus with deionized water to obtain inner denim, then cut into pieces, crush, filter, separate, and purify to obtain cactus extract, disperse in deionized water, and prepare 175ml of cactus leaf extract with a concentration of 40 wt%. aqueous solution, and NaOH solution to adjust its pH to 10.7 to obtain an alkaline cactus leaf extract; add the above-mentioned ice powder to the alkaline cactus leaf extract, and stir at 30°C for 300 minutes to obtain a nanosilver hydrosol with a particle size of 8-30nm ;

[0040] Take 4g of polyester fibers and place ...

Embodiment 3

[0047] Take 10g of polyester fabric and place it in 400ml of scouring solution (recipe: 2g of soda ash, 0.4g of detergent, 0.6g of sodium hydrosulfite), and treat it at 100°C for 30 minutes, take it out and wash it until neutral, and dry it at 80-90°C , and then transferred to 200ml of lye (recipe: NaOH 4g, accelerator 0.3g, dispersant 0.5g), treated at 80°C for 30min, taken out, cleaned, and dried to constant weight.

[0048] Get 0.1g of wheat starch and disperse it in 20ml of deionized water, stir at 90°C until gelatinized to obtain a starch solution; prepare an aloe leaf extract and a cactus extract according to the technical scheme of Examples 1 and 2, and prepare aloe with a concentration of 20 wt % Aqueous solution of leaf extract and 30 wt % aqueous solution of cactus leaf extract were mixed according to the volume ratio of 1:1, then starch solution was added to prepare 500ml composite solution, and the pH of the composite solution was adjusted to 10.2 with NaOH solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing antibacterial polyester by use of plant nano-silver. The method comprises the following steps of: performing surface structure modification pretreatment on the polyester fiber / fabric pretreated by refining liquid by a low-temperature plasma or alkali de-weighting method; and placing the product in plant nano-silver hydrosol for impregnation treatment, or soaking the pretreated polyester fiber / fabric in a silver-ammonia solution, and then transferring to a plant leaf extract liquid-soluble starch composite solution for impregnation treatment to obtain the antibacterial polyester fiber or fabric prepared by use of plant nano-silver. According to the invention, through surface structure modification of polyester, the adsorption capacity of the polyester to nano-silver particles or silver ions is enhanced, the adsorption quantity is obviously increased, and the nano-silver can be attached for a long time without loss; and the obtained polyester fiber / fabric shows excellent and lasting antibacterial performance, and the wet absorption and air permeability, the anti-static ability, the dyeing performance and the like are obviously improved.

Description

technical field [0001] The invention relates to a finishing method of plant nano-silver long-acting antibacterial polyester, which belongs to the technical field of textile finishing. Background technique [0002] With the development of science and technology and the improvement of people's living standards, people have put forward higher hygienic requirements for textiles, and the demand for functional textiles such as antibacterial and deodorant has continued to expand, which has attracted great attention from the textile industry at home and abroad. In comparison, the development of antibacterial functional textiles in China is relatively lagging behind, especially the antibacterial finishing of polyester is still in its infancy. As the largest producer of polyester, strengthening the research and development and promotion of antibacterial polyester fibers and fabrics is important for improving the quality of life and promoting synthetic fibers in my country. The developm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/00D06M15/11D06M11/83D06M10/00D06M11/38D06M101/32
Inventor 陈宇岳林红熊佳庆
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products