Theaflavin matt glaze and manufacturing method thereof

A manufacturing method and a matte glaze technology, which are applied in the field of ochre matte glaze for antique ceramic wine bottles and the field of manufacture thereof, can solve the problems of inability to achieve the simple effect, poor color saturation, uneven color and the like, and achieve a good antique effect. , Increase the water absorption rate, the effect of uniform color

Active Publication Date: 2013-03-06
江苏省宜兴彩陶工艺厂
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional yellow matt glaze mainly uses titanium yellow powder as the pigment. The yellow glaze made of titanium yellow powder has poor color saturation and slightly low tinting strength. Especially when making antique ceramic products, the color is uneven and cannot achieve the simple and simple effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The tea-yellow matte glaze and its manufacturing method, the steps are as follows, the tea-yellow material for ceramics is first prepared, and the following raw materials are proportioned according to the weight percentage: 83% of titanium dioxide, 8% of antimony oxide, 1.8% of nickel oxide, and 7.2% of potassium dichromate . Weigh the raw materials of the above components, first put titanium dioxide, antimony oxide, and nickel oxide into the stirring mill according to the proportion and stir for 40 minutes, then dissolve the potassium dichromate weighed according to the proportion with hot water and then add the above Stir the pre-stirred ingredients for another 20 minutes, pass through a 60-mesh sieve, and then put them into a sagger for calcination. Mesh sieve to make tea-yellow material.

[0013] Then prepare the ocher yellow glaze, according to the weight percentage ratio of the following raw materials: 18% feldspar, 19.5% quartz, 20.5% Suzhou soil, 5.5% boron fri...

Embodiment 2

[0016] The tea-yellow matte glaze and its manufacturing method, the steps are as follows, the tea-yellow material for ceramics is first prepared, and the following raw materials are proportioned according to the weight percentage: 83.5% of titanium dioxide, 7.5% of antimony oxide, 2.2% of nickel oxide, and 6.8% of potassium dichromate .

[0017] Weigh the raw materials of the above components, first put titanium dioxide, antimony oxide and nickel oxide into the stirring mill according to the proportion and stir for 40 minutes first, dissolve the potassium dichromate weighed according to the proportion with hot water and then add the above Stir the pre-stirred ingredients for another 20 minutes, pass through a 60-mesh sieve, and then put them into a sagger for calcination. Mesh sieve to make tea-yellow material.

[0018] Then prepare the ocher yellow glaze, according to the weight percentage of the following raw materials: 18.5% feldspar, 20% quartz, 21% Suzhou soil, 5.0% boro...

Embodiment 3

[0021] The tea-yellow matte glaze and its manufacturing method, the steps are as follows, the tea-yellow material for ceramics is first prepared, and the following raw materials are proportioned according to the weight percentage: titanium dioxide 84%, antimony oxide 7.4%, nickel oxide 1.6%, potassium dichromate 7.0% .

[0022] Weigh the raw materials of the above components, first put titanium dioxide, antimony oxide and nickel oxide into the stirring mill according to the proportion and stir for 40 minutes first, dissolve the potassium dichromate weighed according to the proportion with hot water and then add the above Stir the pre-stirred ingredients for another 20 minutes, pass through a 60-mesh sieve, and then put them into a sagger for calcination. Mesh sieve, the tea-yellow material made.

[0023] Then prepare the ocher yellow glaze, proportioning by weight percentage of the following raw materials: 19% feldspar, 20.5% quartz, 20% Suzhou soil, 4.5% boron frit, 13.5% do...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to ceramic glaze and a manufacturing method thereof, in particular to theaflavin matt glaze for an antique ceramic bottle and a manufacturing method thereof. The theaflavin matt glaze is characterized in that titanium dioxide, antimony oxide, nickel oxide and potassium dichromate are adopted as raw materials to be blended and calcined into theaflavin coloring materials, and then the theaflavin coloring materials are mixed with feldspar, quartz, Suzhou soil, boron frit, dolomite and calcite to be smashed into theaflavin matt glaze. A ceramic product which is calcined with the theaflavin matt glaze is simple and unsophisticated in glazing color, good in antique effect, uniform in color and applicable to top-grade bottles.

Description

technical field [0001] The invention relates to a ceramic glaze and a manufacturing method thereof, in particular to an ocher matt glaze for antique ceramic wine bottles and a manufacturing method thereof. Background technique [0002] The traditional yellow matt glaze mainly uses titanium yellow powder as the pigment. The yellow glaze made of titanium yellow powder has poor color saturation and slightly low tinting strength. Especially when making antique ceramic products, the color is uneven and cannot achieve the simple and simple effect. . Contents of the invention [0003] In order to solve the above problems, the present invention provides a kind of ocher matt glaze with uniform color and good antique effect and a manufacturing method thereof, the steps comprising: [0004] (1) Making tea-yellow material [0005] Titanium dioxide, antimony oxide, nickel oxide, and potassium dichromate are used as raw materials, and the weight percentages are: titanium dioxide 81-88...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86
Inventor 高永康杨庆华
Owner 江苏省宜兴彩陶工艺厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com