Water-based heat insulation paint and preparation method thereof

A technology for thermal insulation and coating, applied in the direction of coating, can solve the problems of difficult to achieve emissivity, complex selection and sintering process, etc., and achieve the effect of maintaining the ambient temperature unchanged, alleviating mismatches, and eliminating odors

Inactive Publication Date: 2013-03-13
大连高宝龙科技有限公司
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Radiant heat insulation coatings can radiate absorbed heat out of the room in the form of thermal emission, thereby adjusting the indoor temperature. However, the selection of functional pigments and fillers for preparing radiant heat insulation coatings and the sintering process are complicated, and it is difficult to achieve a stable emissivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050]The content of styrene-acrylic emulsion is 35%, coalescent 2%, antifreeze 2%, thickener 1%, defoamer 0.7%, dispersant 0.5%, 3M hollow glass microspheres 5%, paraffin / modified silicon The mass fraction of algae earth composite phase change material accounts for 15% of the total mass of the coating (the paraffin content in the composite phase change material is 40%), titanium dioxide 16%, and distilled water make up the balance.

[0051] Add the dispersant and antifreeze to distilled water, place it on a low-speed mixer and stir well, add the composite phase change material and titanium dioxide slowly in the order of density first and then increase, and stir at a speed of about 3000 rpm. Foaming agent, then slowly add film-forming aids and 1 / 2 thickener, stir evenly at low speed, then move to high-speed mixer, add the remaining 1 / 2 thickener, stir at 3000 rpm, stir for about 30 Minutes is the pigment paste.

[0052] Slowly add 3M hollow glass microspheres into the color p...

Embodiment 2

[0055] The content of pure acrylic emulsion is 35%, coalescent 2%, antifreeze 2%, thickener 1%, defoamer 0.7%, dispersant 0.5%, 3M hollow glass microspheres 5%, paraffin / modified silicon The mass fraction of algae earth composite phase change material accounts for 15% of the total mass of the coating (the paraffin content in the composite phase change material is 40%), titanium dioxide 16%, and distilled water make up the balance.

[0056] Add the dispersant and antifreeze to distilled water, place it on a low-speed mixer and stir well, add the composite phase change material and titanium dioxide slowly in the order of density first and then increase, and stir at a speed of about 3000 rpm. Foaming agent, then slowly add film-forming aids and 1 / 2 thickener, stir evenly at low speed, then move to high-speed mixer, add the remaining 1 / 2 thickener, stir at 3000 rpm, stir about 60 Minutes is the pigment paste.

[0057] Slowly add 3M hollow glass microspheres into the color paste, ...

Embodiment 3

[0060] The content of vinyl acetate emulsion is 35%, coalescent 2%, antifreeze 2%, thickener 1%, defoamer 0.7%, dispersant 0.5%, 3M hollow glass microspheres 5%, paraffin / modified The mass fraction of diatomite composite phase change material accounts for 15% of the total mass of the paint (the paraffin content in the composite phase change material is 40%), titanium dioxide 16%, and distilled water make up the balance.

[0061] Add the dispersant and antifreeze to distilled water, place it on a low-speed mixer and stir well, add the composite phase change material and titanium dioxide slowly in the order of density first and then increase, and stir at a speed of about 3000 rpm. Foaming agent, then slowly add film-forming aid and 1 / 2 thickener, stir evenly at low speed, then move to high-speed mixer, add the remaining 1 / 2 thickener, stir at 3000 rpm, stir about 45 Minutes is the pigment paste.

[0062] Slowly add 3M hollow glass microspheres into the color paste, and stir at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based heat insulation paint and a preparation method of the paint; the water-based heat insulation paint is prepared by mixing water, film forming matter, a dispersing agent, an anti-freezing agent, a defoaming agent, a film forming auxiliary agent, a thickening agent, functional filler, composite phase change material and titanium dioxide. The water-based heat insulation paint is coated on the surface of a wall body, and has the effects of heat insulation and building indoor temperature regulation after being cured at the room temperature and completely dried.

Description

technical field [0001] The invention relates to a thermal insulation coating used for interior and exterior walls of buildings, in particular to a water-based thermal insulation coating and a preparation method thereof, belonging to the technical field of chemical coatings. Background technique [0002] With the international community's increasing requirements for energy saving and emission reduction, wall insulation has become an important part of building energy conservation. At present, my country's thermal insulation materials are changing from industrial thermal insulation to architectural thermal insulation. Thermal coating is one of the development directions of building thermal insulation materials. Building thermal insulation coatings are often divided into three categories: barrier thermal insulation coatings, reflective thermal insulation coatings and radiation thermal insulation coatings. The barrier heat insulation coating is a silicate composite coating based...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D133/04C09D131/04C09D7/12
Inventor 于锦周雷周静李华宇付新
Owner 大连高宝龙科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com