Attapulgite-modified polyvinyl chloride synthetic leather and manufacturing method thereof

A technology of polyvinyl chloride and attapulgite, which is applied in chemical instruments and methods, synthetic resin layered products, textiles and papermaking, etc., can solve the problems of product quality, hydrolysis resistance, insufficient weather resistance, residue and other problems, and achieve high Adhesive fastness, good vapor permeability and moisture absorption conductivity, and the effect of increasing flexibility

Inactive Publication Date: 2013-03-27
HEFEI ANSHAN COATING FABRICS
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] An attapulgite modified polyvinyl chloride synthetic leather, comprising a surface layer, a foaming layer, an adhesive layer, and a raised cloth,

[0027] The surface layer is made of the following parts by weight (kg) of raw materials into a slurry:

[0028] SG-2 PVC resin 70, SG-5 PVC resin 30, triethyl citrate 15, epoxy butyl oleate 30, n-butyl methacrylate 25, PVC color paste 6, dibasic lead phosphite 2. Tribasic lead sulfate 1, modified diatomaceous earth 5, alumina 35, nano calcium carbonate 45, fast pressing carbon black N660 25, titanate coupling agent TMC-TTS 1, antioxidant 168 1, N-2-(aminoethyl)-3-aminopropyltrimethoxysilane 1, silane coupling agent KH550 2, protein powder 3;

[0029] The foamed layer is made by mixing the following parts by weight (kg) of raw materials into a slurry:

[0030] SG-4 PVC resin 40, SG-6 PVC resin 80, propylene glycol adipic acid polyester 35, n-butyl methacrylate 25, propylene glycol sebacate polyester 20, n-butyl methacrylate 25, p-to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses attapulgite-modified polyvinyl chloride (PVC) synthetic leather. The attapulgite-modified PVC synthetic leather comprises a surface layer, a foamed layer, a bonding layer and a brushing fabric, and is characterized in that the surface layer is prepared by mixing the following raw materials in parts by weight to form slurry: 70 to 80 parts of SG-2 type PVC resin, 30 to 40 parts of SG-5 type PVC resin, 10 to 15 parts of triethyl citrate, 30 to 35 parts of epoxy butyl oleate, 20 to 25 parts of n-butyl methacrylate, 5 to 6 parts of PVC color paste, 1 to 2 parts of dibasic lead phosphate, 1 to 2 parts of tribasic lead sulfate and 5 to 10 parts of modified diatomite. Through the improvements of the formula and the process, the flexibility of the synthetic leather is improved, and the synthetic leather has a natural comfortable hand feeling similar to that of natural leather and is difficult to damage or tear after being used for 3 to 5 years.

Description

Technical field [0001] The invention belongs to the technical field of chemical synthetic leather fabric processing, in particular to an attapulgite modified polyvinyl chloride synthetic leather and a manufacturing method thereof. Background technique [0002] At present, polyvinyl chloride synthetic leather modified by polyurethane and attapulgite is widely used in the furniture fields such as commercial furniture and household furniture. Polyurethane synthetic leather has the advantages of high simulation and good hand feeling, and has been widely favored by the market. However, a large number of DMF solvents with certain toxicity and volatility are used in the manufacturing process. Even after sufficient drying, DMF will have a large amount of residues, which becomes a source of excessive indoor air VOC pollution. At the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other issues limit its further widespread applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/06B32B27/08B32B19/02B32B37/02B32B37/12C08L27/06C08K13/06C08K9/04C08K9/02C08K5/11C08K5/1515C08K3/34C08K3/22C08K3/26C08K3/04C08K3/36C09C1/42C09C3/08C09C3/06
Inventor 藏德虎
Owner HEFEI ANSHAN COATING FABRICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap