Polyvinyl chloride synthetic leather for sports shoes and manufacturing method of polyvinyl chloride synthetic leather

A polyvinyl chloride and synthetic leather technology, applied in chemical instruments and methods, synthetic resin layered products, applications, etc., can solve problems such as hydrolysis resistance, insufficient weather resistance, product quality problems, residues, etc., and achieve good vapor permeability Effect of moisture absorption conductivity, increased flexibility, and high adhesive fastness

Inactive Publication Date: 2013-03-27
HEFEI ANSHAN COATING FABRICS
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other issues limit its further wide application
Polyvinyl chloride synthetic leather for sports shoes has the advantages of excellent hydrolysis resistance, abrasion resistance, scratch resistance, flame retardancy, etc., but there are problems in product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A polyvinyl chloride synthetic leather for sports shoes, comprising a surface layer, a foam layer, an adhesive layer, and raised cloth,

[0027] The surface layer is prepared from the following raw materials in parts by weight (kg):

[0028] SG-1 type PVC resin 40, SG-6 type PVC resin 80, propylene glycol adipate polyester 35, n-butyl methacrylate 25, propylene glycol sebacate polyester 15, PVC color paste 5, isooctyl dimercaptoacetate Di-n-octyl tin ester 1, calcium stearate 2, isooctyl tin dimethyl dimercaptoacetate 2, modified attapulgite 5, carbon black N220 40, precipitated silica 35, antioxidant 1010 1, 3 - Aminopropyltrimethoxysilane 2, crosslinker TAC 1;

[0029] The foam layer is made of the following raw materials in parts by weight (kg):

[0030] SG-1 type PVC resin 40, SG-5 type PVC resin 80, acetyl triethyl citrate 35, dibutyl maleate 15, n-butyl methacrylate 35, azodicarbonamide 2, 4 ,4'-Oxobisbenzenesulfonyl hydrazide 2, expandable microsphere foaming ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyvinyl chloride (PVC) synthetic leather for sports shoes. The polyvinyl chloride synthetic leather comprises a surface layer, a foaming layer, an adhering layer, and a brushing fabric, and is characterized in that the surface layer is prepared from the following raw materials in parts by weight: 40-50 parts of SG-1 type PVC resin, 70-80 parts of SG-6 type PVC resin, 30-35 parts of hexanedioic acid propylene glycol polyester, 25-30 parts of n-butyl methacrylate, 15-20 parts of sebacic acid propylene glycol polyester, 5-6 parts of PVC color paste, 1-2 parts of bis(isooctyl thioglycolate) dioctyldllauryltin, 1-2 parts of calcium stearate, 1-2 parts of dimethyl bis(isooctyl thioglycolate) and 5-10 parts of modified attapulgite. The PVC synthetic leather is increased in flexibility through the improvement of a formula and a process, has a natural comfortable hand feel similar to a natural leather, is not easily broken or torn and damaged after 3-5 years, and is suitable for being used as a fabric of the sports shoes.

Description

technical field [0001] The invention belongs to the technical field of chemical synthetic leather fabric processing, in particular to polyvinyl chloride synthetic leather for sports shoes and a manufacturing method thereof. Background technique [0002] At present, polyurethane and PVC synthetic leather for sports shoes are widely used in commercial furniture and household furniture. Polyurethane synthetic leather has the advantages of high imitation and good hand feeling, and has been widely favored by the market. However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other problems limit its further wide application. Polyvinyl chloride synthetic leather for spo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/06B32B27/08B32B13/12B32B27/30B32B27/40A43B1/00
Inventor 藏德虎
Owner HEFEI ANSHAN COATING FABRICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap