Nanometer stone material and production method thereof

A nano-material and stone technology, applied in the field of construction and decoration materials, can solve the problems of non-pollution resistance, easy damage, poor heat resistance of artificial stone, etc., and achieve the effect of low cost, simple operation and excellent stain resistance

Inactive Publication Date: 2013-04-17
李建平
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Protective coating materials cannot fundamentally solve the problems of artificial stone such as poor heat resistance, non-pollution resistance, and easy damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A nano-stone material, comprising a main material, a cementing agent and a nano-material, the weight percentage of each component is: 1-20% of the nano-material, 65-90% of the main material, and 3-15% of the cementing agent; the main material is natural For stone and (or) industrial waste, the binder is a mixture of curing agent, color paste, etc. and polymer or inorganic adhesive, and the nanomaterial is metal or metal oxide nano powder, or nano metal oxide solution.

[0032] Above-mentioned natural stone material can be used common stone powder, pebble, or river sand, and industrial waste residue can be used discarded glass lens, slag etc.

[0033] The composition and weight percentage of the cement are: 23% of colored viscous liquid, 12% of resin, 15.5% of curing agent, 39% of color paste, 1-3% of fly ash 4%, release wax 2.5%, silica gel 4%.

[0034] The metal or metal oxide nano-powder is nano-powder of fumed nano-silica, silicon oxide, titanium oxide, zinc oxide, ...

Embodiment 2

[0044] A nanometer stone material, the weight percentage of each component is: 5% of silicon oxide nanometer powder, 85% of the mixture of river sand and blast furnace waste residue, and 10% of cementing agent. The composition of the cement is the same as the cement in Example 1.

Embodiment 3

[0046] A nano-stone material, the weight percent of each component is: 15% mixed solution of 30% nano-silicon oxide solution and 10% nano-titanium oxide solution, 78% of natural stone, and 7% of cementing agent. The composition of the cement is the same as the cement in Example 1.

[0047] The nano-stone material provided by the present invention is a mineral-filled polymer composite material (referred to as solid surface material or solid plate material) that is made of nano-materials plus discarded glass lenses, slag, river sand, natural stone powder, and cement, and is vacuum-cast or molded. ), is a non-radioactive element, environmentally friendly, reusable green new building decoration material. Has the following characteristics:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nanometer stone material and a production method thereof. The nanometer stone material comprises a main material and cementing agent, wherein the main material is a natural stone material and (or) industrial waste slag; and the cementing agent is a mixture of curing agent and color paste matched with polymers or inorganic cementing agent; the nanometer stone material further comprises a nanometer material; and the contents of the components of the nanometer stone material are as follows in percentage by weight: 1-20 percent of nanometer material, 65-90 percent of main material and 3-15 percent of cementing agent. The nanometer stone material is a mineral filling type polymer based composite produced by the steps of high-pressure vacuum shaping, drying, polishing and the like, and has the characteristics of difficulty in abrasion, good heat resistance, dirt resistance and the like; and the production method has simple operation and low cost, and can be widely applied in the industries of public building and interior decoration.

Description

technical field [0001] The invention relates to a nano-stone and a production method thereof, belonging to the field of construction and decoration materials. Background technique [0002] Artificial stone is a panel material widely used in construction and home decoration in the market. Compared with other materials, artificial stone has the characteristics of rich patterns and colors, integral molding, seamless bonding at any length, and no trace at the seams. and hard plastics, etc. [0003] Artificial stone is mainly composed of cement and main materials. The binder can be polymer (such as unsaturated polyester resin, epoxy compound), or inorganic adhesive (such as cement, lime and other silicates), the main material is developed from marble, calcite, quartz sand to the use of industrial waste slag (such as blast furnace Waste slag, copper slag, nickel slag, waste glass, etc.). According to the raw materials used in the production of artificial stone, it can be divid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00