Composition for solid plasticized high-flame-retardant PVC sheath material and preparation method of composition

A technology of solid plasticizer and composition, which is applied in the field of solid plasticized high flame retardant PVC sheath material composition and its preparation field, can solve the problems of large amount of addition, loss of material mechanical properties, etc., and prevent radiation oxidation And degradation, enhanced mechanical properties, uniform flow effect

Inactive Publication Date: 2013-05-01
JIANGSU BAOYUAN GAOXIN ELECTRIC
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large amount of its addition, the mechanical properties of the material are greatly lost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1: Weigh 8% of sodium antimonide inorganic flame retardant, 7% of solid plasticizer, and 1% of antioxidant in a high-speed mixer according to mass percentage, and mix for no less than 2 minutes; then weigh 50% Polyvinyl chloride resin, 25% flame retardant plasticizer, 5% decabromodiphenylethane flame retardant are poured into a high-speed mixer and mixed for no less than 3 minutes; then add 5% antimony trioxide and 6% in turn The stabilizer, 0.5% modifier and 0.5% release agent are mixed for no less than 3 minutes; the flame retardant plasticizer is tricresyl phosphate, and the solid plasticizer is "Am-168 solid plasticizer". The release agent is calcium stearate. The mixed material is added to a two-stage extruder and melt blended to prepare the composition for the high flame-retardant PVC cable outer sheath material of the present invention.

[0015] The obtained composition is vulcanized into a sheet in a vulcanizer, the vulcanization temperature is 160° C., an...

Embodiment 2

[0016] Example 2: Weigh 8% sodium antimonide inorganic flame retardant, 7% solid plasticizer, and 1% antioxidant in a high-speed mixer and mix for more than 2 minutes according to mass percentage; then weigh 50% polychloride Vinyl resin, 22% flame retardant plasticizer, 5% decabromodiphenyl ethane flame retardant, pour into a high-speed mixer and mix for no less than 3 minutes; then add 5% antimony trioxide, 6% stable Mixing agent, 0.5% modifier, 0.5% mold release agent for no less than 3 minutes; flame retardant plasticizer is tricresyl phosphate, solid plasticizer is "Am-168 solid plasticizer", mold release The agent is calcium stearate. The mixed material is added to a two-stage extruder and melt blended to prepare the composition for the high flame-retardant PVC cable outer sheath material of the present invention.

[0017] The obtained composition is vulcanized into a sheet in a vulcanizer, the vulcanization temperature is 160° C., and the time is 15 minutes, and then the l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composition for a solid plasticized high-flame-retardant PVC (polyvinyl chloride) sheath material and a preparation method of the composition, and belongs to the technical field of cable materials. According to the composition and the preparation method, an Am-168 solid plasticizer and sodium antimonide flame retardant are introduced into the high-flame-retardant PVC cable sheath material; the traditional fire retardant damages other properties of the material while achieving the flame-retardant purpose; however, sodium antimonide does not affect body properties of the material while achieving the flame-retardant modification purpose due to a structure and constituent characteristics of sodium antimonide; the compatibility and adhesive strength with plastic are improved greatly; the dispersity is good; a loading level can be raised; the impregnating property is good; the mixing time is short; uniform flowing is realized in a mold; and forming is good. Mechanical properties of the material are improved, and the composite high-flame-retardant cable sheath material prepared by the composition for the composite high-flame-retardant cable sheath material has good mechanical properties and flame resistance.

Description

Technical field [0001] The invention relates to a composition for a solid plasticized high flame-retardant PVC sheath material and a preparation method thereof, and belongs to the technical field of cable materials. technical background [0002] Flexible PVC plastics for wires and cables have been mass-produced as a large category of PVC soft products. With the rapid development of the wire and cable industry, the varieties and use conditions of cable materials are getting higher and higher, especially for ships, In aviation and other work, the demand for high oxygen index flame-retardant cable materials is increasing. This product has already come out abroad. Some domestic manufacturers and scientific research units are discussing this product. However, due to the aging performance and flame retardant performance And process performance are unstable, especially the appearance of the pay-off line is dull, and there are particles that are difficult to plasticize, resulting in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06H01B3/44H01B7/295C08K13/02C08K5/03C08K3/22C08K3/10C08K5/526C08K5/098B29B9/06B29C47/92B29C48/92
Inventor 周春云解洪俊蔡玉林
Owner JIANGSU BAOYUAN GAOXIN ELECTRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap