Preparation method of metalized film of induction cooker capacitor

A metallized film and capacitor technology, applied in metal material coating process, ion implantation plating, coating, etc., can solve the problems of film rupture, film-foil gap, cost waste, etc., and achieve a small probability of film rupture and improve The effect of compressive strength and service life improvement

Active Publication Date: 2013-05-22
NINGBO GREAT SOUTHEAST WAN XIANG SCI & TECH
View PDF5 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the whole machine in the market is oriented towards ultra-thin and micro-miniature development, although the foil film composite material has a strong current-carrying and electric resistance capability, its disadvantage is that it is large in size and is not conducive to the use of the whole machine. Another disadvantage is that polypropylene film and aluminum foil Composite rolling and other processes are difficult to control, especially in the process of winding the core, due to the difference in hardness and toughness of the two materials, there will be gaps between the film and foil, so that the heat shrinkage of the material is not sufficient when setting the shape, resulting in a gap between the film and foil. It is easy to be broken down by electricity, and the scrap rate is high, resulting in waste of cost
And because the raw material impurity that selects when the prior art prepares capacitor metallization film is more, so can cause the performance of the capacitor metallization film that produces is relatively poor, and because prior art prepares capacitor metallization film when longitudinal and transverse stretching process The setting of various parameters is not good, so it is likely to cause the film to break, and the film rupture will affect the normal production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The following specific embodiments further describe the present invention, but the present invention is not limited to the following specific embodiments.

[0018] A preparation method of a metallized film of an induction cooker capacitor, which comprises the following steps:

[0019] (1) Selection and preparation of raw materials: polypropylene raw materials with isotacticity ≥ 97% and ash content ≤ 16 ppm are required; the polypropylene raw materials are produced by BOREALLS POLYMERS Company in Belgium;

[0020] (2), extruder extruding melt: the polypropylene raw material processed in step (1) is filtered through a high-density filter, and then the melt is extruded through an extruder. It is more than 1200 mesh, and the temperature of the extruder is 220 ~ 260 ° C;

[0021] (3) Cooling by chill roll and air shower: the melt produced in step (2) is cooled and shaped by chill roll and air shower to obtain a cast sheet, and the temperature of the chill roll is 85-95 ℃,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Ash contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of preparation of a capacitor, and in particular relates to a preparation method of a metalized film of an induction cooker capacitor. The preparation method comprises the following steps of: selection and preparation of raw materials, extruding a melt through an extruder, cooling the melt through a chilling roller and an air shower, drawing the melt in a vertical direction, drawing the melt in a transverse direction, testing the thickness of the drawn melt, performing procedures of trimming and corona treatment, rolling, time sequence treatment, slicing, and vacuum-evaporating the metalized film. Through the steps, the prepared metalized film is comparatively high in performance, comparatively low in rejection rate, low in cost and high in current carrying capability.

Description

technical field [0001] The invention relates to the field of capacitor preparation, in particular to a preparation method of a metallized film of an induction cooker capacitor. Background technique [0002] Electric appliances are very important in people's daily life. With the continuous improvement of people's living standards, induction cooker, as a household appliance, is easy to use and has a variety of kitchen functions, so it is welcomed by many families, and the market prospect is more and more broad. . The capacitor plays a very important role in the working of the induction cooker, so the capacitor is one of the key components of the induction cooker. interference effect. The capacitor core is the heart of the capacitor, so the material of the capacitor manufacturing core must have a high-frequency, high-temperature, high-current shock-resistant high-molecular polypropylene film as the medium, so as to ensure the long-term stable operation of the whole machine. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C69/00B29B13/10B29C47/88B29C55/12B29C59/10B29C71/00C23C14/20C23C14/24B29C48/08B29C48/91
CPCB29C48/08B29C48/91B29C48/914
Inventor 黄剑鹏
Owner NINGBO GREAT SOUTHEAST WAN XIANG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products