Transparent cold-resistant flame-retardant polypropylene material and preparation method thereof

A technology of flame retardant polypropylene and polypropylene resin, which is applied in the field of preparation of flame retardant polypropylene materials, can solve the problems of life, property damage, easy fire and high heat generation, achieve good transparency and flame retardant effect, and is convenient for large-scale production. The effect of large-scale promotion and use and simple production process

Inactive Publication Date: 2013-05-22
GUANGDONG JUSHI CHEM CO LTD
View PDF7 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Poor low-temperature toughness is a significant shortcoming of polypropylene, especially in some areas with low temperature. Fire, the flame ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The transparent cold-resistant and flame-retardant polypropylene material of this embodiment, wherein the phosphorus-nitrogen-bromine compound flame retardant is a combination of aluminum hypophosphite and piperazine pyrophosphate hydrobromide treated with 1 part by weight of silane Thing, the ratio of aluminum hypophosphite and piperazine hydrobromide pyrophosphate is 4.5:1, and example 1~4 flame retardant is consistent, and raw material composition is as shown in table 1:

[0053] raw material name parts by weight Polypropylene resin 5090T 85 15# white oil 0.1 Toughener POE 8150 10 Linear Low Density Polyethylene 7042 3 Composite phosphorus-nitrogen-bromine flame retardant 3.5 Flame retardant synergist DCP 0.2 Sorbitol nucleating agent M3988 0.1 Antioxidant B215 0.4 Lubricant EBS 0.4

[0054] Table 1

[0055] Its preparation method is:

[0056] (1) Weigh various raw materials according to the weight...

Embodiment 2

[0060] The transparent cold-resistant flame-retardant polypropylene material of this embodiment, raw material composition is as shown in table 2:

[0061] raw material name parts by weight Polypropylene resin 5090T 80 15# white oil 0.1 Toughener POE 8150 10 Linear Low Density Polyethylene 7042 5 Composite phosphorus-nitrogen-bromine flame retardant 3.5 Flame retardant synergist DCP 0.2 Sorbitol nucleating agent M3988 0.2 Antioxidant B215 0.4 Lubricant EBS 0.4

[0062] Table 2

[0063] Its preparation method is identical with embodiment 1.

Embodiment 3

[0065] The transparent cold-resistant flame-retardant polypropylene material of this embodiment, raw material composition is as shown in table 3:

[0066] raw material name parts by weight Polypropylene resin 5090T 75 15# white oil 0.1 Toughener POE 8150 20 Linear Low Density Polyethylene 7042 10 Composite phosphorus-nitrogen-bromine flame retardant 3.5 Flame retardant synergist DCP 0.2 Sorbitol nucleating agent M3988 0.3 Antioxidant B215 0.4 Lubricant EBS 0.4

[0067] table 3

[0068] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a transparent cold-resistant flame-retardant polypropylene material and a preparation method thereof. The material comprises the following components in parts by weight: 65-85 parts of polypropylene resin, 0.1-0.3 part of white oil, 5-20 parts of ethylene-octene copolymer, 3-10 parts of linear low-density polyethylene, 1-5 parts of phosphorus-nitrogen-bromine composite flame retardant, 0.1-0.4 part of flame-retardant synergist, 0.1-0.4 part of nucleating agent, 0.2-0.5 part of antioxidant and 0.2-0.5 part of lubricant. The phosphorus-nitrogen-bromine composite flame retardant comprises the following components in parts by weight: 60-90 parts of organic or inorganic hypophosphite, 10-30 parts of phosphoric-acid-containing piperazidine hydrobromide and 0.5-5 parts of silane coupling agent. The polypropylene material disclosed by the invention has high transparency and high cold resistance as well as flame retardancy. The material has the advantages of favorable compatibility and precipitation resistance, and can be used for preparing plastic products requiring high transparency, high cold resistance and flame retardancy.

Description

technical field [0001] The invention relates to a transparent cold-resistant and flame-retardant polypropylene material with high transparency, low temperature resistance and flame retardancy of the material; the invention also relates to a preparation method of the flame-retardant polypropylene material. Background technique [0002] Polypropylene (PP) is a general-purpose thermoplastic obtained by the polymerization of propylene. Due to its rich source of raw materials and relatively simple synthesis process, PP has the characteristics of low density, low price and good processability compared with other general-purpose thermoplastics. Its yield strength, tensile strength, surface hardness and elastic modulus are all excellent. And it has outstanding environmental stress cracking and wear resistance, and has been widely used in various fields of industrial production. [0003] Due to the relatively slow crystallization speed of polypropylene melt, large spherulites are ea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/00C08L23/08C08K13/06C08K9/06C08K5/5313C08K5/3462C08K3/32C08K5/54C08K5/14B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 龚文幸何燕岭张翼翔程瑞良张秀芹
Owner GUANGDONG JUSHI CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap