Compound type photocatalyst air purification waterborne interior wall coating and preparation method thereof

An air purification and interior wall coating technology, applied in antifouling/underwater coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of photocatalyst failure, slow degradation rate of photocatalyst, poor anti-aging performance, etc. To achieve the effect of improving air purification ability, enhancing photocatalytic ability and improving photocatalytic efficiency

Active Publication Date: 2013-06-05
CHINA STATE CONSTRUCTION ENGINEERING CORPORATION +1
View PDF5 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a composite photocatalyst air-purifying water-based interior wall paint and a preparation method thereof, which solve the technical problems of low photocatalytic activity, poor adhesion and poor anti-aging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound type photocatalyst air purification waterborne interior wall coating and preparation method thereof
  • Compound type photocatalyst air purification waterborne interior wall coating and preparation method thereof
  • Compound type photocatalyst air purification waterborne interior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment one, this composite photocatalyst air purification water-based interior wall paint, its raw material composition is as follows by weight percentage proportioning:

[0047] Photocatalytic filler 10.5%;

[0048] Polyurethane emulsion 48%;

[0049] Propylene glycol phenyl ether 6%;

[0050] Dispersant 6%;

[0051] Stabilizer 4%;

[0052] Wetting agent 2%;

[0053] water 20%;

[0054] Antifungal agent 1.5%;

[0055] Defoamer 1%;

[0056] Leveling agent 0.5%;

[0057] Thickener 0.5%;

[0058] The photocatalytic filler is composed of nano anatase titanium dioxide and nano zinc oxide in a weight ratio of 9:1.

[0059]

Embodiment 2

[0060] Embodiment two, this composite photocatalyst air purification water-based interior wall paint, its raw material composition is as follows by weight percentage proportioning:

[0061] Photocatalytic filler 15%;

[0062] Polyurethane emulsion 25%;

[0063] Propylene glycol phenyl ether 1%;

[0064] Dispersant 2%;

[0065] Stabilizer 2%;

[0066] Wetting agent 1%;

[0067] Water 45%;

[0068] Antifungal agent 4%;

[0069] Defoamer 2%;

[0070] Leveling agent 2%;

[0071] Thickener 1%;

[0072] The photocatalytic filler is composed of nano anatase titanium dioxide and nano tin dioxide in a weight ratio of 5:1.

[0073]

Embodiment 3

[0074] Embodiment three, this composite photocatalyst air purification water-based interior wall paint, its raw material composition is as follows by weight percentage proportioning:

[0075] Photocatalytic filler 13.6%;

[0076] Polyurethane emulsion 41%;

[0077] Propylene glycol phenyl ether 3%;

[0078] Dispersant 4%;

[0079] Stabilizer 3%;

[0080] Wetting agent 1%;

[0081] Water 28%;

[0082] Antifungal agent 2.7%;

[0083] Defoamer 1.5%;

[0084] Leveling agent 1.4%;

[0085] Thickener 0.8%;

[0086] The photocatalytic filler is composed of nano-anatase titanium dioxide and nano-zinc oxide in a weight ratio of 1:1.

[0087]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

Provided are a compound type photocatalyst air purification waterborne interior wall coating and a preparation method thereof. The compound type photocatalyst air purification waterborne interior wall coating comprises, by weight, the following materials of 5.5-22.3% of photocatalysis packing, 25-65% of polyurethane emulsion, 1-6% of propylene glycol phenylate, 2-6% of dispersing agents, 2-4% of stabilizing agents, 1-2% of wetting agents, 20-60% of water, 1.5-4% of mildewproof agents, 1-2% of antifoaming agents, 0.5-2% of flatting agents, and 0.5-1% of thickening agents. The photocatalysis packing is formed by complexation of nanoanatase type titanium dioxide and nano-zinc oxide or nano stannic oxide according to a weight ratio of 5-9:1-5. The coating has good air purifying capacity, and can effectively degrade harmful gases in the air and kill bacterial viruses under excitation of ultraviolet light. As an interior decorative material, the coating has good covering power and adhesive power and excellent stability. The coating and the production method are simple in production process, suitable for various coating methods, and easy to popularize and apply.

Description

technical field [0001] The invention relates to a photocatalyst coating and a preparation method of the coating. Background technique [0002] With the development of social economy and the improvement of living standards, people put forward higher requirements for working and living conditions. The use of a large number of new building materials and decorative materials has created a stylish, beautiful, convenient and comfortable living space for modern people. In the past two decades, due to changes in life and work patterns, modern people spend more and more time indoors. Many people spend almost 90% of their time indoors. As a result, a large number of "sick buildings" are caused by a variety of harmful chemical components contained in new materials, and the number of people suffering from "building disease syndrome", "building complications" and "multiple chemical allergies" continues to increase. People have found that due to the widespread use of new building mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D7/12C09D5/14
Inventor 宋中南石云兴张卫东宋建荣李艳稳屈建秦杰
Owner CHINA STATE CONSTRUCTION ENGINEERING CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap