Boil-resistant polyester powder coating, and preparation method and application thereof

A technology of polyester powder and water boiling resistance, applied in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as poor water resistance, and achieve the effect of improving water boiling resistance, reducing costs and improving water resistance.

Active Publication Date: 2013-06-12
NINGBO SOUTH SEA CHEM
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved in the present invention is that the water resistance of the HAA curing agent system adopted in the polyester-HAA type polyester powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] The boiling-resistant polyester powder coating described in this embodiment is obtained by dry mixing a high-acid value polyester resin particle system and a low-acid value polyester resin particle system with a ratio of parts by weight of 1:1.

[0060] The high acid value polyester resin particle system consists of the following components by weight:

[0061] High acid value polyester resin ( P2200) and the mixed curing agent system of HAA and isocyanate Degussa VESTAGON B1530 totaled 70 parts; wherein, the ratio of the parts by weight of the high acid value polyester resin to HAA in the high acid value polyester resin particle system was 92:8 , the ratio by weight of the high acid value polyester resin to isocyanate is 10:1;

[0062] Pigment A is titanium dioxide CR826 and iron red mixed in equal proportions 10 parts in total; Filler A is 20 parts of barium sulfate (Hunan Hechuang HC-801) whose surface has been treated with hydrophobicity;

[0063] 3 parts of aux...

Embodiment 2

[0075] The boiling-resistant polyester powder coating described in this embodiment is obtained by dry mixing a high-acid value polyester resin particle system and a low-acid value polyester resin particle system with a ratio of parts by weight of 1:1.

[0076] The high acid value polyester resin particle system consists of the following components by weight:

[0077] High acid value polyester resin (Crylcoat TM E04131) with HAA and biuret polyisocyanate curing agent A total of 80 parts of the mixed curing agent system; wherein, the ratio by weight of the high acid value polyester resin and HAA in the high acid value polyester resin particle system is 92:8, and the high acid value polyester resin The ratio with the weight part of isocyanate is 15:1;

[0078] Filler A is 30 parts of barium sulfate filler (B-301 produced by Shanghai Longman) whose surface has undergone hydrophobic treatment;

[0079] The auxiliary agent A is 5 parts, and the auxiliary agent A includes levelin...

Embodiment 3

[0090] The boiling-resistant polyester powder coating described in this embodiment is obtained by dry mixing a high-acid value polyester resin particle system and a low-acid value polyester resin particle system with a ratio of parts by weight of 1:1.

[0091] The high acid value polyester resin particle system consists of the following components by weight:

[0092] The mixed curing agent system of high acid value polyester resin (Sanxie B-5600) and HAA and isocyanate Degussa VESTAGON B1530 totals 60 parts; wherein, the high acid value polyester resin in the high acid value polyester resin particle system The ratio of parts by weight with HAA is 92:8, and the ratio of parts by weight of the high acid value polyester resin and isocyanate is 20:1;

[0093] Pigment A iron red for 15 copies;

[0094] Filler A is aluminum hydroxide (NABALTEC company's A40) 10 copies.

[0095] The low-acid value polyester resin particle system is made up of the following components by weight:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a boil-resistant polyester powder coating which comprises the following components: a high-acid-value polyester resin particle system containing high-acid-value polyester resin, curing agents A and stuffing A, and a low-acid-value polyester resin particle system containing low-acid-value polyester resin, curing agents B and stuffing B. The curing agents A and the curing agents B are mutually-independent mixed curing agent systems of hydroxyalkyl acidamide (HAA) and isocyanic acid ester. The stuffing A and the stuffing B are mutually-independent aluminum hydroxides or hydrophobic stuffing. According to the boil-resistant polyester powder coating, the hydrophobic stuffing is added into the high-acid-value polyester resin particle system and the low-acid-value polyester resin particle system, so that water permeation is effectively blocked, and therefore the polyester powder coating is protected. The boil-resistant property of the boil-resistant polyester powder coating is even more than that of a polyester powder coating which is curded by means of triglycidyl isocyanurate (TGIC) curing agents.

Description

technical field [0001] The invention belongs to the field of functional powder coatings, in particular to a boiling-resistant polyester powder coating and its preparation method and application. Background technique [0002] With its advantages of economy, environmental protection, high efficiency and excellent performance, powder coatings are gradually replacing organic solvent-based coatings, becoming an important development direction in the coatings industry, and have maintained a relatively fast growth rate. Polyester powder coatings are widely used in the field of outdoor coating of buildings due to their excellent durability, decoration and formability. [0003] Polyester powder coatings can be divided into pure polyester type and mixed type according to different curing agent systems. Among them, polyester-TGIC (polyester triglycidyl isocyanurate) type pure polyester powder coating is the earliest used For powder coatings in the field of weather resistance, the curi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/00C09D175/06C09D5/46C09D7/12
Inventor 张云伟
Owner NINGBO SOUTH SEA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap