Pinkish red UV ink-jet ink for high-speed ink-jet printing and preparation method thereof

An inkjet ink and inkjet printing technology, which is applied in the field of magenta ultraviolet (UV) inkjet ink and its preparation, can solve the problems of ink limitation, can not meet the requirements of high-speed inkjet printing, etc., and achieve the effect of simple process

Inactive Publication Date: 2015-07-15
BEIJING INSTITUTE OF GRAPHIC COMMUNICATION
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, a variety of radiation-curable inkjet inks have been proposed in patents, but the application of these inks is limited to inkjet printing, printing and dyeing, and is far from meeting the requirements of high-speed inkjet printing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pinkish red UV ink-jet ink for high-speed ink-jet printing and preparation method thereof
  • Pinkish red UV ink-jet ink for high-speed ink-jet printing and preparation method thereof
  • Pinkish red UV ink-jet ink for high-speed ink-jet printing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Mix 30 parts of prepolymer, 42 parts of monomer, and 8 parts of dispersant, place on a constant temperature magnetic stirrer and stir for 30 minutes to mix evenly; add 20 parts of azo red, and use a stirrer to stir the mixture for 30 minutes for pre-dispersion , using a high-speed grinder to grind for 90 minutes to obtain a magenta ink paste. Wherein the azo red is selected from the RT-355-D of Ciba Company, and the prepolymer is hyperbranched polyester acrylic resin selected from the EB150 series of Cytec Company, and the monomer is commercially available acrylic acid 2-ethoxyethoxy Mixture of ethyl ester, hexanediol diacrylate and trimethylolpropane triacrylate in the ratio of 2-ethoxyethoxyethyl acrylate, hexanediol diacrylate and trimethylolpropane triacrylate= 5:3:2 (weight ratio), the dispersant is a dispersant containing organically modified polysiloxane selected from the dispersers series of TEGO Company.

[0032]Mix 20 parts of monomer, 50 parts of film-formin...

Embodiment 2

[0034] Mix 30 parts of prepolymer, 51 parts of monomer, and 4 parts of dispersant, place on a constant temperature magnetic stirrer and stir for 30 minutes to mix evenly; add 15 parts of quinacridone red, and use a stirrer to stir the mixture for 30 minutes for pre-treatment. After dispersion, use a high-speed grinder to grind for 90 minutes to obtain a magenta ink paste. Wherein the quinacridone red is selected from Ciba Company's Micro Korea 5B-K, the prepolymer is a commercially available polyester acrylate, and the monomer is a commercially available 2-phenoxyethyl acrylate, phthalic acid A mixture of diethanol diacrylate and ethoxylated trimethylolpropane triacrylate in a ratio of 2-phenoxyethyl acrylate: phthalate diethanol diacrylate: ethoxylated Trimethylolpropane triacrylate=9:6:1 (weight ratio), and the dispersant is EFKA series selected from BASF Company.

[0035] Mix 30 parts of monomer, 46 parts of film-forming resin, 1 part of photoinitiator (including hydrogen ...

Embodiment 3

[0037] Mix 30 parts of prepolymer, 48 parts of monomer, and 12 parts of dispersant, and stir for 30 minutes to mix evenly; add 10 parts of azo red, use a stirrer to stir the mixture for 30 minutes for pre-dispersion, and use a high-speed grinder to grind for 60 Minutes to get magenta ink paste. Wherein the azo red is selected from the RT-355-D of Ciba Company, the prepolymer is commercially available polyester acrylate, and the monomer is commercially available isobornyl acrylate, triethylene glycol dimethacrylate and trimethylolpropane trimethacrylate, the ratio is isobornyl acrylate: triethylene glycol dimethacrylate: trimethylolpropane trimethacrylate = 7:9:4 ( weight ratio), the dispersant is byk-168 selected from BYK company.

[0038] Mix 20 parts of monomer, 42 parts of film-forming resin, 6 parts of photoinitiator, and 2 parts of leveling agent, add 30 parts of color paste, and stir for 60 minutes with a stirrer to obtain magenta UV inkjet ink. The monomer is a mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
surface tensionaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a pinkish red UV ink-jet ink for high-speed ink-jet printing and a preparation method thereof. The pinkish red UV ink-jet ink is used for printing of paper materials and belongs to the technical field of digital printing. The pinkish red UV ink-jet ink comprises, by weight, 15 to 30 parts of color paste, 20 to 35 parts of a monomer, 40 to 50 parts of a film forming resin, and 1 to 10 parts of a photoinitiator. The color paste comprises, by weight, 10 to 25 parts of a pinkish red pigment, 15 to 30 parts of a prepolymer, 40 to 60 parts of a monomer and 4 to 10 parts of a dispersant. The pinkish red UV ink-jet ink is prepared by stirring and high-speed grinding. The pinkish red UV ink-jet ink satisfies ink-jet printing requirements, has particle size less than 0.5 microns, viscosity of 20 to 30cP (at 25 DEG C), surface tension of 20 to 35mN / m (at 25 DEG C), a curing rate of 30 to 50m / min (based on light source linear power of 200W / cm), and conductivity less than 18 microseconds per centimeter.

Description

technical field [0001] The invention relates to a magenta ultraviolet (UV) inkjet ink for high-speed inkjet printing and a preparation method thereof. The printing material is mainly paper, and belongs to the technical field of digital printing. Background technique [0002] The key advantage of UV curing technology is that it does not contain solvents, has no VOC emissions, and avoids the impact of traditional solvent-based inks on the environment. It is considered a "green technology" and can achieve instant curing. The drying speed of the ink is higher than that of Water-based or solvent-based inks, but UV inks are mainly used in traditional printing methods, such as offset printing, silk screen printing, etc. As a kind of digital printing technology, inkjet printing has the advantages of non-impact transfer printing, simple operation, and low requirements for printing materials. Printing equipment that combines UV curing technology with inkjet printing has been released....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/101C09D11/322
Inventor 张婉黄蓓青魏先福顾灵雅刘江浩杨晓
Owner BEIJING INSTITUTE OF GRAPHIC COMMUNICATION