Foam heat insulation plate and preparation method thereof

A technology of foam insulation board and expression method, which is applied in the field of building materials, can solve the problems of poor heat insulation and sound insulation, flammability of insulation board, inconvenient construction, etc., and achieve the effect of excellent heat preservation performance, good insulation and convenient construction

Inactive Publication Date: 2013-08-07
苏州市德莱尔建材科技有限公司
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a foam insulation board and its preparation method, which solves the technical problems in the existing insulat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Step 1: Weigh various raw materials according to the ratio of mass and number as described below

[0027] Waste PS foam particles 100;

[0028] 425 # Portland cement 30;

[0029] Early strength superplasticizer 50;

[0030] Expanded Perlite Powder 200;

[0031] Fiberglass 50;

[0032] PU adhesive 50;

[0033] Rosin soap foaming agent 1;

[0034] TCPP2;

[0035] Fly Ash 1.

[0036] The second step: first crush the waste PS foam particles, add 425 # Portland cement, fully mixed for 5-10 minutes;

[0037] Step 3: Add early-strength superplasticizer to the mixed material in the second step, stir it into a slurry, then add the remaining components, heat to 150°C, pressurize 5MPa, stir into a slurry, and then add it to the mold;

[0038] Step 4: Let stand for 1 hour, remove the mold after cooling to 60°C, and keep in water for 7 days.

Embodiment 2

[0040] Step 1: Weigh various raw materials according to the ratio of mass and number as described below

[0041] Waste PS foam particles 100;

[0042] 425 # Portland cement 50;

[0043] Early strength superplasticizer 100;

[0044] Expanded Perlite Powder 300;

[0045] Fiberglass 100;

[0046] PU adhesive 80;

[0047] Rosin soap foaming agent 10;

[0048] TCPP5;

[0049] fly ash 5.

[0050] The second step: first crush the waste PS foam particles, add 425 # Portland cement, fully mixed for 5-10 minutes;

[0051] Step 3: Add early-strength superplasticizer to the mixed material in the second step, stir it into a slurry, then add the remaining components, heat to 150°C, pressurize 5MPa, stir into a slurry, and then add it to the mold;

[0052] Step 4: Let stand for 1 hour, remove the mold after cooling to 60°C, and keep in water for 7 days.

Embodiment 3

[0054] The first step: Weigh various raw materials according to the ratio of mass and number as described below:

[0055] Waste PS foam particles 100;

[0056] 425 # Portland cement 40;

[0057] Early strength superplasticizer 70;

[0058] Expanded Perlite Powder 250;

[0059] Fiberglass 75;

[0060] PU adhesive 60;

[0061] Rosin soap foaming agent 5;

[0062] TCPP 3.5;

[0063] fly ash 2.5.

[0064] The second step: first crush the waste PS foam particles, add 425 # Portland cement, fully mixed for 5-10 minutes;

[0065] Step 3: Add early-strength superplasticizer to the mixed material in the second step, stir it into a slurry, then add the remaining components, heat to 150°C, pressurize 5MPa, stir into a slurry, and then add it to the mold;

[0066] Step 4: Let stand for 1 hour, remove the mold after cooling to 60°C, and keep in water for 7 days.

[0067] All components of the compositions in the above examples and comparative examples can be purchased commercia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a foam heat insulation plate. The foam heat insulation plate comprises the following components in parts by weight: 100 parts of waste PS (polystyrene) foam particles, 30-50 parts of No. 425 Portland cement, 50-100 parts of early strength superplasticizer, 200-300 parts of expanded perlite powder, 50-100 parts of glass fiber, 50-80 parts of PU (polyurethane) adhesive, 1-10 parts of resin soap foaming agent, 2-5 parts of flame retardant and 1-5 parts of fly ash. The product has excellent heat insulation performance, and the heat conductivity can achieve 0.05W/(m.K); the relative density is 0.3, the compression strength is 0.4-0.6MPa, and the bending modulus is 0.25MPa; and the foam heat insulation plate is non-toxic, odorless, less prone to combustion, acid and alkali-resistant, good in insulativity, convenient to construct and long in service life, can be widely used and can continuously replace existing materials.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a foam insulation board and a preparation method thereof. Background technique [0002] With the development of social urbanization, science and technology, and humanization, foamed cement boards have been widely used in large-span industrial plants, warehouses, large locomotive garages, stadiums, exhibition halls, airports, large public facilities, activity rooms and In construction projects in various fields such as residential interlayer and partition wall insulation of residential buildings, it overcomes the thermal insulation difference caused by the foam insulation materials used in the past, the high thermal sensitivity rate, and the characteristics of cracks. [0003] At present, a lot of waste PS plastics are abandoned, causing solid waste pollution. With the popularization of the concept of humanization and the formation of a new harmonious society, it is very necessar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B38/02C04B18/20
CPCY02W30/91
Inventor 计慷
Owner 苏州市德莱尔建材科技有限公司
Who we serve
  • R&D Engineer