Flyash tamping plug and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technology of fly ash, which are applied in blasting, ceramic material production, etc., can solve the problems of reducing the utilization rate of blastholes, leakage of explosive capacity, and low compactness, so as to improve the utilization rate of blastholes, good economic benefits, and manufacture The effect of simple method
Active Publication Date: 2015-01-21
中铁十局集团第二工程有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the plasticity of loess blasthole clay is poor, and it is not easy to fill the hole when sealing the hole, and the compactness is not high, which will easily lead to the leakage of explosive power and reduce the utilization rate of the blasthole.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] A kind of fly ash gun mud, made of the following raw materials by weight: 90 parts of low liquid limit clay, coarse sand (M X =3.1-3.7) 5 parts, fly ash (loss on ignition ≤ 8%, fineness ≤ 25%, water demand ratio ≤ 105%) 6 parts, water 14 parts.
[0014] The preparation method comprises the following steps: taking low-liquid-limit clay, coarse sand, fly ash and water according to the amount and mixing them evenly to form a primary material; processing the primary material into a clay roll after hardening for 1 hour; Wrap the roll in plastic wrap.
Embodiment 2
[0016] A kind of fly ash gun mud, made of the following raw materials by weight: 100 parts of low liquid limit clay, coarse sand (M X =3.1-3.7) 6 parts, fly ash (loss on ignition ≤ 8%, fineness ≤ 25%, water demand ratio ≤ 105%) 7 parts, water 15 parts.
[0017] The preparation method comprises the following steps: taking low-liquid-limit clay, coarse sand, fly ash and water according to the amount and mixing them evenly to form a primary material; processing the primary material into clay rolls after hardening for 1.5 hours; Wrap the roll in plastic wrap.
Embodiment 3
[0019] A kind of fly ash gun mud, made of the following raw materials by weight: 110 parts of low liquid limit clay, coarse sand (M X =3.1-3.7) 7 parts, fly ash (loss on ignition ≤ 8%, fineness ≤ 25%, water demand ratio ≤ 105%) 8 parts, water 17 parts.
[0020] The preparation method comprises the following steps: taking low-liquid-limit clay, coarse sand, fly ash and water according to the amount and mixing them evenly to form a primary material; processing the primary material into clay rolls after hardening for 2 hours; Wrap the roll in plastic wrap.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a flyash tamping plug and a preparation method thereof and belongs to the field of water pressure blasting technology. The flyash tamping plug is prepared from the following raw materials in parts by weight: 90-110 parts of low liquid limit clay (liquid limit (50%)), 5-7 parts of coarse sand, 6-8 parts of flyash and 14-17 parts of water. The preparation method comprises the following steps of: weighing the low liquid limit clay, the coarse sand, the flyash and the water as required and uniformly mixing to form primary material; hardening the primary material for 1-2h and fianlly processing the hardened into a tamping plug rolls. According to the novel tamping plug, flyash and clay powder are used as core materials, local materials are used, and the cost is saved. The corresponding preparation method is simple, the water-retaining property of the obtained product is good, the flyash tamping plug can be stored for 12 hours after being processed into the tamping plug rolls; if coated with a plastic film, the storage time can be further prolonged, and the existing common loess tamping plug only can be stored for 5 hours under no protection.
Description
technical field [0001] The invention belongs to the technical field of hydraulic blasting, and in particular relates to a blasting clay for hydraulic blasting, and also relates to a preparation method of the blasting clay. Background technique [0002] In recent years, with the development of railway engineering, hydraulic blasting technology has become increasingly mature. This technology takes advantage of the incompressible nature of water, and the explosion energy is transmitted to the surrounding rock of the blasthole through water with almost no loss, which is very beneficial to rock breaking. Under the expansion of the explosive gas, the water will produce a "water wedge" effect, which is beneficial to the further breaking of the rock. At the same time, the water in the blast hole can also play the role of atomization and dust reduction, which can greatly reduce dust pollution. [0003] At present, the clay used in practical engineering is mainly loess clay. Howeve...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more