Ultrahigh-strength and high-toughness steel for pumping rod and production process thereof

An ultra-high-strength, production-process technology, applied in the field of alloy structural steel, can solve problems such as strength reduction, broken rod accidents, and excessive performance differences, and achieve the effects of reducing the number of fractures, increasing fatigue life, and improving cleanliness

Active Publication Date: 2013-08-07
JIANGSU LIHUAI IRON AND STEEL CO LTD +1
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the process of processing such steel into sucker rods, the rod head and the rod tail need to be heat-treated, resulti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrahigh-strength and high-toughness steel for pumping rod and production process thereof
  • Ultrahigh-strength and high-toughness steel for pumping rod and production process thereof
  • Ultrahigh-strength and high-toughness steel for pumping rod and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] The comparison of the chemical composition of the ultra-high-strength sucker rod steel 42CrMoA, patented steel (patent publication number CN101962737A) used in China and the present invention is shown in Table 1 below.

[0032] Table 1 Comparison of chemical composition wt%

[0033]

[0034] Prepared using the following production process:

[0035] (1) LD converter smelting: smelting in a top-bottom combined blowing converter of more than 90 tons, using molten iron and scrap steel as raw materials for preliminary smelting to achieve pre-de-P removal, adding special synthetic refining slag, composite deoxidizer and high purity to the steel The alloy is pre-deoxidized and the composition is adjusted initially, and slag retention is used to prevent the return of P when tapping;

[0036] (2) LF refining: deep deoxidation and alloying of molten steel in a LF furnace of more than 90 tons to produce high-basicity slag (R≥3.0) to strengthen the removal of S and inclusions. The refi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses ultrahigh-strength and high-toughness steel for a pumping rod, which comprises the following chemical components in percentage by mass: 0.32-0.38% of C, 0.17-0.37% of Si, 1.60-1.80% of Mn, 1.10-1.30% of Cr, 0.20-0.30% of Mo, 0.20-0.30% of V, 0.015-0.035% of Al, no more than 0.020% of P, no more than 0.010% of S, no more than 0.002% of [O], no more than 0.0002% of [H] and the balance of Fe. The production process comprises the following steps: smelting in a conventional converter, refining in a refining device, performing silicon-calcium-barium end deoxidation in the late stage of the refining process, performing RH degasification and inclusion removal after refining, casting molten steel into a continuous casting blank, and rolling into phi19-25mm round steel. The invention is reasonable in component design and advanced in process; compared with ultrahigh-strength steel for a pumping rod available on the existing market, the steel disclosed by the invention has higher strength and toughness, the tensile strength Rm is no less than 1200 MPa, the extension percentage delta5 is no less than 12%, the percentage reduction in area Z is no less than 48%, accidents of pumping rod breakage in a high-load environment can be effectively decreased, and the economic loss can be obviously reduced.

Description

technical field [0001] The invention relates to alloy structural steel in the iron and steel industry, in particular to super-high-strength, high-toughness steel for sucker rods (35Mn2CrMoV) and a production process thereof. Background technique [0002] At present, the mechanical production wells account for more than 90% of the total number of oil production wells, and the rod pump oil production method accounts for more than 90% of the mechanical production wells. Therefore, the rod pump oil production method has occupied an important position in my country's crude oil production. The sucker rod is an important component of the rod pumping equipment, which transmits the power of the pumping unit to the downhole pump. In the process of oil production, the sucker rod string is subjected to asymmetric cyclic load, and the working medium is well fluid (crude oil and mine water), most of which contain corrosive media, so the main failure modes of the sucker rod are fatigue fra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38E21B17/00
Inventor 王忠英孙大文翟万里陈子坤袁敏
Owner JIANGSU LIHUAI IRON AND STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap