Salt spray resistant metal surface silane treatment agent and preparation method thereof

A silane treatment agent and metal surface technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of weak adhesion, uneven density, and voids on metal bodies, and achieve improved film quality, short processing time, and enhanced The effect of stability

Inactive Publication Date: 2013-08-21
MAANSHAN TUORUI METAL SURFACE TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the maturity of the metal surface treatment process, the traditional phosphate conversion and chromate passivation surface treatment technology is gradually replaced by the environmental protection and energy-saving silanization treatment technology due to factors such as environmental pollution and...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A salt spray resistant metal surface silane treatment agent, which is a mixed liquid prepared by the following components, and the weight parts (grams) of each component in each liter of the mixed liquid are:

[0018] Propyl trimethoxysilane 25-30, vinyl trimethoxysilane 15-25, sodium hexametaphosphate 4-5, tetrahydrofuran 1-2, hexamethylphosphoric triamide 5-7, citric acid 3-4, Sorbitol 6-7, film-forming aids 2-4, the rest is water;

[0019] The said film-forming assistant is composed of the following raw materials in parts by weight:

[0020] 1,2-bis(triethoxysilyl)ethane 6, diethylene glycol monobutyl ether 5, acrylic acid 6, sodium metasilicate 2, alum 2, water 20;

[0021] Add the above-mentioned 1,2-bis(triethoxysilyl)ethane to water, stir and heat to 80°C, add acrylic acid and sodium metasilicate, stir and react for 40 minutes, raise the temperature to 100°C, add two Ethylene glycol monobutyl ether and alum were stirred and reacted for 20 minutes, and kept standing for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a salt spray resistant metal surface silane treatment agent, which is a mixed solution prepared from the following components. Per liter of the mixed solution comprises the following components by weight (g): 25-30 of propyltrimethoxy silane, 15-25 of vinyltrimethoxy silane, 4-5 of sodium hexametaphosphate, 1-2 of tetrahydrofuran, 5-7 of hexamethylphosphoric triamide, 3-4 of citric acid, 6-7 of sorbitol, 2-4 of a film-forming agent, and the balance water. The treatment process of the salt spray resistant metal surface silane treatment agent produced in the invention generates no dreg, the treatment time is short, and the control is simple and convenient. Being free of harmful heavy metal ions, the salt spray resistant metal surface silane treatment agent is safe and environment-friendly, and can form a silane coating having excellent corrosion resistance with a metal surface, thus prolonging the service life of metals.

Description

Technical field [0001] The invention mainly relates to a treatment agent, in particular to a metal surface silane treatment agent resistant to salt spray. Background technique [0002] With the maturity of metal surface treatment technology, traditional phosphate conversion and chromate passivation surface treatment technologies have gradually been replaced by environmentally friendly and energy-saving silanization treatment technologies due to environmental pollution and easy harm to the human body. However, the current silane Most chemical treatments rely solely on the film-forming properties of silane, so that the film formed on the surface of the metal workpiece treated with the silane solution has uneven density, voids, cracks, and weak adhesion to the metal body. Summary of the invention [0003] The purpose of the present invention is to make up for the defects of the prior art and provide a salt spray resistant metal surface silane treatment agent and a preparation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/07C09D7/12C09D5/08
Inventor 芮明功
Owner MAANSHAN TUORUI METAL SURFACE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap