Formula and production process of co-polypropylene foamed plastic

A technology of copolymerized polypropylene and foam plastics, which is applied in the field of formula and production technology using polypropylene as raw material, can solve the problems of high cost, difficult to degrade and recycle, complex process, etc., and achieve low cost, good shape recovery stability, The effect of simple processing technology

Inactive Publication Date: 2013-09-11
厦门雄亚塑胶科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of the prior art that the products are not easy to degrade and recycle, the cost is high, and the process is complex, etc., the present invention adopts the following technical solutions:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A formulation of copolymerized polypropylene foam, comprising

[0031] Polypropylene resin F5006: 100 parts

[0032] Talc powder reinforcing filler: 10-80 parts

[0033] Active zinc oxide ZNO: 1.0-3.0 parts

[0034] Stearic acid ST: 0.5-1.0 parts

[0035] Zinc stearate ZNST: 1.0-1.5 parts

[0036] Organic peroxide initiator DCP: 0.01-0.05 parts

[0037] Cross-linking aid TMPTMA: 1.0-3.0 parts

[0038] Coupling agent 172: 0.2-0.5 parts

[0039] Peroxide crosslinking agent DCP: 0.5-0.8 parts

[0040] Azo blowing agent AC165: 1.0-5.0 parts.

[0041] The product performance test of the foamed plastic obtained by using the above formula is as follows, linear ratio: 1.7; volume expansion ratio: 4.913; hardness: 75C; specific gravity: 0.16g / cm^3.

[0042] Above-mentioned formula is just a larger range value of each component in the formula, not concrete, is a preferred version of formula of the present invention as embodiment 2, and the formula of embodiment 2 comprise...

Embodiment 2

[0053] Example 2 gives the specific number of parts of each component of the formula, which is a more preferred solution. For the product obtained in Example 2, the performance test results of the product are as follows, linear magnification: 2.0; volume expansion magnification: 8.0; Hardness: 60C; specific gravity 0.09 g / cm^3.

[0054] A production process for producing copolymerized polypropylene foam using the above formula, the steps include: 1. Weigh the required raw materials according to the proportion of the above formula, and mix the main base material (polypropylene resin), processing aids, and initiators evenly and put them into 2. Mix through the internal mixer in step 1, and set the internal mixing temperature to 125°C. When the temperature reaches the set value, put the crosslinking agent and foaming agent into the internal mixer, and blank The temperature is set to 135°C, and the blanking time is set to 15 minutes; 3. Transfer the mixture in step 2 to the open m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a formula and a production process of a co-polypropylene foamed plastic. By using co-polypropylene as a raw material, the obtained foam product has the advantages of light mass, high strength, low cost, good heat resistance, degradability and easy recovery, etc., and has no influence on the environment. Meanwhile, resources are saved, the processing process is simple, and the processing equipment involves traditional machines, so that there is no additional increase of equipment investment, and the cost can be reduced to the utmost. With excellent heat insulation, sound absorption and noise reduction properties, the co-polypropylene foamed plastic is very suitable for home decoration.

Description

technical field [0001] The invention relates to a formula and process of foamed plastics, in particular to a formula and production process using copolymerized polypropylene as a raw material. Background technique [0002] Because of its light weight, good heat insulation effect, good cushioning effect, good insulation, stable anti-corrosion performance, and low price, foam plastics can not only beautify product packaging, but also provide cushioning protection for products, and are widely used in daily necessities In the fields of packaging, industry, agriculture, transportation, military, aerospace and other fields, basically all products in the market need to use foamed plastics. Traditional foamed plastics are made of EVA, PE, PS and other materials. , but traditional materials such as EVA, PE, PS, etc. have very large defects, high cost, cumbersome processing technology, cannot be degraded and recycled after use, cause great environmental pollution, and cause a great wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08K13/02C08K3/34C08K3/22C08K5/09C08K5/098C08K5/14C08J9/10B29B7/28B29B7/72B29C44/02
Inventor 许超群
Owner 厦门雄亚塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com