A kind of manufacturing method of carbon fiber composite cable wire

Abstract

The invention relates to a manufacturing method of a carbon fiber composite material cable wire. The carbon fiber composite material cable wire comprises a load bearing core (12) and a protection layer (13), wherein the protection layer (13) is covered outside the load bearing core (12) through a winding process, the load bearing core (12) is a high-temperature-resistance mechanical property epoxy resin and carbon fiber compound, and the protection layer (13) is a compound of high-temperature-resistance and weather-resistance epoxy resin compositions and glass fibers. The carbon fiber composite material cable wire adopts the blending epoxy resin of the hydantoin epoxy resin and low-viscosity epoxy resin as resin substrates, the requirement of glass fiber on the low viscosity of the resin can be met, and the cable core can also have excellent high-temperature-resistance performance.

Description

technical field [0001] The invention relates to a cable core, in particular to a method for manufacturing a carbon fiber composite material cable. Background technique [0002] As a substitute for traditional steel cores, carbon fiber composite cables are required to have excellent mechanical properties as well as high temperature resistance, UV resistance and Aging, etc., have high requirements on the comprehensive performance of the cable core. [0003] The structure of the traditional carbon fiber composite cable production method is a load-bearing core made of carbon fiber and epoxy resin composite material inside, and a protective layer made of glass fiber and epoxy resin composite outside, both of which share the same resin system. Under the same resin system, properties such as high temperature resistance, tensile strength, flexural strength, modulus, compressive strength, UV resistance, and aging resistance affect each other. Increasing a certain aspect of performan...

AI Technical Summary

Problems solved by technology

[0004] Because the resin curing system at room temperature (18-25°C) often reacts too slowly, the efficiency is not high, and the reaction is not complete, so the room temperature curing epoxy system has many disadvantages, such as epoxy resin is mostly brittle after curing, and there is insufficient toughness The disadvantages are that the performance of the reinforced fiber cannot be effectively exerted, and the composite material is often destroyed due to the premature failure of the epoxy resin when bearing the load.

[0005] In addition, the room temperature curing system is mostly cured at room temperature, and the high temperature resistance of the cured product is poor, so it cannot be applied to medium and high temperature environments or occasions with high temperature requirements