Preparation method of inn/gan/glass structure

A glass and glass substrate technology, applied in the field of deposition and preparation of new optoelectronic materials, can solve the problems of difficulty in reducing device cost, hindering the development of InN material devices, and high price of sapphire substrates, achieve good electrical performance and stability, and solve the problem of lattice Mismatched, low-cost effects

Active Publication Date: 2016-04-20
辽宁太阳能研究应用有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As we all know, the price of sapphire substrate is relatively high. Using it as the substrate of InN material makes it difficult to reduce the cost of InN material-based devices, which seriously hinders the development of InN material devices.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of inn/gan/glass structure
  • Preparation method of inn/gan/glass structure
  • Preparation method of inn/gan/glass structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The Corning glass substrate was ultrasonically cleaned with acetone, ethanol and deionized water for 5 minutes, then dried with nitrogen and sent to the reaction chamber; the reaction chamber was evacuated to 9.0×10 -4 Pa, the substrate is heated to 485°C, trimethylgallium and nitrogen carried by hydrogen are introduced into the reaction chamber, and the flow rates of the two are 0.5sccm and 80sccm, controlled by a mass flow meter; the total pressure of the control gas is 1.2Pa; The electron cyclotron resonance power is 650W, and the reaction is 30min, and the GaN buffer layer thin film on the Corning glass substrate is obtained. Then continue to use the ECR-PEMOCVD system to evacuate the reaction chamber to 8.0×10 -4 Pa, the substrate is heated to 300°C, trimethylindium and nitrogen carried by hydrogen are introduced into the reaction chamber, the flow ratio of the two is 4:150, and the flow is 4sccm and 150sccm, controlled by a mass flow meter; control gas ...

Embodiment 2

[0054] The Corning glass substrate was ultrasonically cleaned with acetone, ethanol and deionized water for 5 minutes, then dried with nitrogen and sent to the reaction chamber; the reaction chamber was evacuated to 9.0×10 -4 Pa, the substrate is heated to 485°C, trimethylgallium and nitrogen carried by hydrogen are introduced into the reaction chamber, and the flow rates of the two are 0.6sccm and 90sccm, controlled by a mass flow meter; the total pressure of the control gas is 1.2Pa; The electron cyclotron resonance power is 650W, and the reaction is 30min, and the GaN buffer layer thin film on the Corning glass substrate is obtained. Then continue to use the ECR-PEMOCVD system to evacuate the reaction chamber to 8.0×10 -4 Pa, the substrate is heated to 200°C, trimethylindium and nitrogen carried by hydrogen are introduced into the reaction chamber, the flow ratio of the two is 4:120, and the flow rate is 4sccm and 120sccm, controlled by a mass flow meter; control ...

Embodiment 3

[0056] The Corning glass substrate was ultrasonically cleaned with acetone, ethanol and deionized water for 5 minutes, then dried with nitrogen and sent to the reaction chamber; the reaction chamber was evacuated to 9.0×10 -4 Pa, the substrate is heated to 485°C, trimethylgallium and nitrogen carried by hydrogen are introduced into the reaction chamber, and the flow rates of the two are 0.5sccm and 120sccm, controlled by a mass flow meter; the total pressure of the control gas is 1.2Pa; The electron cyclotron resonance power is 650W, and the reaction is 30min, and the GaN buffer layer thin film on the Corning glass substrate is obtained. Then continue to use the ECR-PEMOCVD system to evacuate the reaction chamber to 8.0×10 -4 Pa, the substrate is heated to 100°C, trimethylindium and nitrogen carried by hydrogen are introduced into the reaction chamber, the flow ratio of the two is 5:120, and the flow is 5 sccm and 120 sccm, controlled by a mass flow meter; control ga...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of deposition and preparation of new photoelectric materials, and provides a method for preparing an InN / GaN / glass structure with good electrical performance and good stability. The invention comprises the following steps: 1) After the glass substrate is ultrasonically cleaned with acetone, ethanol, and deionized water in sequence, it is blown dry with nitrogen and sent into the reaction chamber; 2) ECR-PEMOCVD system is used to vacuumize the reaction chamber and heat The glass substrate is fed into the reaction chamber with trimethylgallium and nitrogen carried by hydrogen. The flow rates of trimethylgallium and nitrogen are 0.5sccm-0.8sccm and 80sccm-120sccm respectively; the total pressure of the gas is controlled, and the electron cyclotron resonance reaction is obtained at GaN buffer film on glass substrate. 3) Continue to use the ECR-PEMOCVD system to evacuate the reaction chamber, heat the glass substrate to 200°C to 400°C, and pass trimethylindium and nitrogen carried by hydrogen into the reaction chamber.

Description

technical field [0001] The invention belongs to the technical field of deposition and preparation of novel photoelectric materials, and in particular relates to a method for preparing an InN / GaN / glass structure. Background technique [0002] Indium nitride (InN) is an important member of group III nitrides. Compared with GaN and ALN, InN has the highest mobility and peak rate, and has unique advantages in the application of high-speed high-frequency transistors and other electronic devices. ; Its room temperature band gap is located in the near-infrared region, and it is also suitable for preparing optoelectronic devices such as high-efficiency solar cells, semiconductor light-emitting diodes, and optical communication devices. However, due to the low decomposition temperature of InN, a low growth temperature is required, and NH as a N source 3 The decomposition temperature is high, so generally InN films are grown on some substrates such as sapphire. As we all know, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C16/511C23C16/34B32B9/04B32B17/06
Inventor 鞠振河郑洪张东
Owner 辽宁太阳能研究应用有限公司