Compound microcapsule wall material and application thereof in essence microcapsules for cigarettes

A technology of microcapsule wall material and essence microcapsules, applied in the directions of essential oils/spices, fat generation, etc., can solve the problems of high price, difficult to achieve embedding effect, etc., achieve low moisture content, prolong retention time, high encapsulation Buried rate effect

Inactive Publication Date: 2013-11-20
HUBEI CHINA TOBACCO IND +1
View PDF9 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, almost no wall material can satisfy all the above properties at the same time; using a sin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The composite microcapsule wall material 1 of the present invention is formed by mixing the following components by mass percentage: 45.0% octenyl succinic esterified starch, 20.0% maltodextrin, 15.0% sodium carboxymethyl starch, 12.0% % soybean protein isolate, 2.0% gum arabic, 3.0% sodium caseinate, 2.0% sucrose, 0.2% sodium alginate, 0.3% xanthan gum, 0.5% pullulan.

[0018] Take 60g of composite wall material 1 and dissolve it in 340mL of water to form a wall material solution, stir well and add 12g of California lemon oil. First use a high-speed emulsifying homogenizer to shear at 15,000 rpm for 2 minutes; then use an ultra-high pressure micro-jet homogenizer to process once at a pressure of 35 MPa. The obtained emulsion was subjected to spray drying treatment, the inlet air temperature was 180°C, the outlet air temperature was 80°C, and the feed rate was 5mL / min. Collect California lemon oil microcapsule products and keep them sealed.

[0019] The California lem...

Embodiment 2

[0021] The composite microcapsule wall material 2 of the present invention is formed by mixing the following components by mass percentage: 30.0% octenyl succinic esterified starch, 30.0% maltodextrin, 20.0% sodium carboxymethyl starch, 15.0% % Soy Protein Isolate, 1.0% Gum Arabic, 2.0% Sodium Caseinate, 1.0% Sucrose, 0.4% Sodium Alginate, 0.5% Xanthan Gum, 0.1% Pullulan.

[0022] Take 80g of composite wall material 2 and dissolve it in 320mL of water to form a wall material solution, stir well and add 12g of clove bud oil. First use a high-speed emulsifying homogenizer to shear at 10,000rpm for 3 minutes; then use an ultra-high pressure micro-jet homogenizer to process twice at a pressure of 25MPa. The obtained emulsion was subjected to spray drying treatment, the inlet air temperature was 175°C, the outlet air temperature was 70°C, and the feed rate was 7mL / min. Collect clove bud oil microcapsule products and seal them for preservation.

[0023] The clove flower bud oil mi...

Embodiment 3

[0025] The composite microcapsule wall material 3 of the present invention is formed by mixing the following components by mass percentage: 30.0% octenyl succinic esterified starch, 15.0% maltodextrin, 30.0% sodium carboxymethyl starch, 10.0% % soybean protein isolate, 5.0% gum arabic, 5.0% sodium caseinate, 3.9% sucrose, 0.1% sodium alginate, 0.5% xanthan gum, 0.5% pullulan.

[0026] Take 70g of composite wall material 3 and dissolve it in 230mL of water to form a wall material solution, stir well and add 10g of cumin oil. First use a high-speed emulsifying homogenizer to shear at 12,000 rpm for 2 minutes; then use an ultra-high pressure micro-jet homogenizer to process twice at a pressure of 25 MPa. The obtained emulsion was subjected to spray drying treatment, the inlet air temperature was 165°C, the outlet air temperature was 75°C, and the feed rate was 9mL / min. Collect cumin oil microcapsule products and keep them sealed.

[0027] The fennel oil microcapsule product obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a compound microcapsule wall material and an application thereof in essence microcapsules for cigarettes. The compound microcapsule wall material is mixed by the following components in percentage by weight: 30.0-50.0% of starch octenylsuccinate, 15.0-30.0% of maltodextrin, 10.0-30.0% of sodium carboxymethyl starch, 10.0-30.0% of soy isolate protein, 1.0-5.0% of Arabic gum, 1.0-5.0% of sodium caseinate, 1.0-5.0% of saccharose, 0.1-0.5% of sodium alginate, 0.1-0.5% of xanthan gum and 0.1-0.5% of pullulan. The compound microcapsule wall material provided by the invention is good in solubleness, good in emulsibility, good in film-forming property, low in solution viscosity, and economical and practical benefits. Higher embedding rate can be obtained by using the wall material to prepare the essence microcapsules for cigarettes, and the product is good in sensory performance, smooth and uniform in particle, compact in capsule wall, lower in moisture content, good in dispersibility and stronger in practicality.

Description

technical field [0001] The invention belongs to the technical field of cigarette essence and fragrance, and specifically refers to a composite microcapsule wall material and its application in tobacco essence microcapsules. Background technique [0002] Most tobacco flavors are volatile liquid aromatic substances, and their aroma or flavor can be regarded as the "soul" of Chinese cigarettes. Because most of the ingredients in tobacco flavors are highly volatile, sensitive to light, heat, and oxygen, they are prone to chemical reactions with other components, which can easily lead to flavor distortion or weakening of flavor. These disadvantages limit its application in cigarette formulations, and the life-span of cigarettes will be shortened due to the volatilization and loss of essence during storage. Therefore people urgently hope to find a kind of method that can well protect tobacco essence, improve its stability and processability. [0003] Microcapsule technology is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C11B9/00
Inventor 孙炜炜陈胜熊国玺
Owner HUBEI CHINA TOBACCO IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap