Continuous long fiber reinforced PPS composite material and preparation method thereof

A composite material and long fiber technology, which is applied in the field of continuous long fiber reinforced PPS composite material and its preparation, can solve the problems of impeller rigidity to be improved, unsatisfactory toughening effect of PPS material, etc., and achieves light weight, high dimensional stability, Practical effect

Active Publication Date: 2013-12-25
HEFEI GENIUS NEW MATERIALS
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this invention is that the 30-50% glass fiber reinforced PPS used is melted and mixed in a twin-screw extruder. Due to the shearing effect of the twin-screw, the length of the glass fiber is relatively short, only 0.3-0.5mm, which is not suitable for PPS materials. The toughening effect of the impeller is not ideal, resulting in the rigidity of the impeller to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous long fiber reinforced PPS composite material and preparation method thereof
  • Continuous long fiber reinforced PPS composite material and preparation method thereof
  • Continuous long fiber reinforced PPS composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043](1) Weigh the raw materials of each component (in parts by weight) according to the following ratio, and dry the PPS: drying temperature: 120°C; drying time: 6h;

[0044] PPS 457 copies,

[0045] Continuous long fiber reinforcement 500 parts,

[0046] 8 parts of coupling agent,

[0047] 20 parts lubricant,

[0048] Antioxidant 15 parts,

[0049] The melting point of PPS resin is 280°C, the melt flow rate MFR (2.095mm, 315°C, 5.0Kg) is 240g / 10min; the continuous long fiber reinforcement is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 2400g / Km; The coupling agent is silane coupling agent KH550; the lubricant is silicone powder GM-100; the antioxidant is antioxidant 1098 (3,5-di-tert-butyl-4-hydroxyphenylpropionyl-hexanediamine) and antioxidant The compound system of agent PEPQ (tetra(2,4-di-tert-butylphenol)-4,4'-biphenyl diphosphite), the weight ratio of the two is 1:2;

[0050] (2) Mixing preparation:

[0051] Add the ab...

Embodiment 2

[0060] (1) Weigh the raw materials of each component (in parts by weight) according to the following ratio, and dry the PPS: drying temperature: 120°C; drying time: 6h;

[0061] PPS 557 copies,

[0062] Continuous long fiber reinforcement 400 parts,

[0063] 8 parts of coupling agent,

[0064] 20 parts lubricant,

[0065] Antioxidant 15 parts,

[0066] The melting point of PPS resin is 280°C, the melt flow rate MFR (2.095mm, 315°C, 5.0Kg) is 240g / 10min; the continuous long fiber reinforcement is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 2400g / km; The coupling agent is silane coupling agent KH550; the lubricant is silicone powder GM-100; the antioxidant is antioxidant 1098 (3,5-di-tert-butyl-4-hydroxyphenylpropionyl-hexanediamine) and antioxidant The compound system of agent PEPQ (tetra(2,4-di-tert-butylphenol)-4,4'-biphenyl diphosphite), the weight ratio of the two is 1:2;

[0067] (2) Mixing preparation:

[0068] Add the a...

Embodiment 3

[0077] (1) Weigh the raw materials of each component (in parts by weight) according to the following ratio, and dry the PPS: drying temperature: 120°C; drying time: 6h;

[0078] PPS 650 copies,

[0079] Continuous long fiber reinforcement 300 parts,

[0080] 8 parts of coupling agent,

[0081] 20 parts lubricant,

[0082] Antioxidant 15 parts,

[0083] The melting point of PPS resin is 280°C, the melt flow rate MFR (2.095mm, 315°C, 5.0Kg) is 240g / 10min; the continuous long fiber reinforcement is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 2400g / km; The coupling agent is silane coupling agent KH550; the lubricant is silicone powder GM-100; the antioxidant is antioxidant 1098 (3,5-di-tert-butyl-4-hydroxyphenylpropionyl-hexanediamine) and antioxidant The compound system of agent PEPQ (tetra(2,4-di-tert-butylphenol)-4,4'-biphenyl diphosphite), the weight ratio of the two is 1:2;

[0084] (2) Mixing preparation:

[0085] Add the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of polymer materials, and relates to a continuous long fiber reinforced PPS composite material and a preparation method thereof. The composite material comprises the following components by weight: 450-650 parts of polyphenylene sulfide, 300-500 parts of a continuous fiber reinforced agent, 5-10 parts of a coupling agent, 10-30 parts of an antioxidant and 10-20 parts of a lubricant. Compared with the prior art, an engine cooling water pump impeller made from the material through injection moulding has characteristics of light weight, good dimensional stability, stable working dynamic balancing performance, strong resistance to chemical corrosion and high strength; an automobile water pump using the continuous long fiber reinforce PPS impeller has smooth working performance, high efficiency and long service life, and can work normally at the temperature of -40 DEG C to -140 DEG C.

Description

technical field [0001] The invention relates to the field of polymer materials, and relates to a continuous long fiber reinforced PPS composite material and a preparation method thereof. Background technique [0002] The automobile water pump is an important part of the engine cooling system. Its function is to pump the coolant, so that the coolant flows quickly in the cooling water channel of the engine, so as to take away the heat generated when the engine is working, and maintain the normal operating temperature of the engine. The water pump used in the automobile engine is a centrifugal water pump, which is composed of a casing, an impeller, a bearing, a pump shaft, a water seal, and a transmission pulley. The impeller is an important part of the water pump. At present, the materials used for the impeller of the automobile engine cooling water pump are mainly cast iron, steel plate or aluminum alloy, each with its own characteristics and shortcomings. Cast iron impeller...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08L83/04C08K13/04C08K7/14C08K5/09C08K5/098B29C47/92B29B7/00B29C48/40B29C48/92
CPCB29B9/14B29B7/46B29B7/72B29B7/7461B29B7/90B29B9/06B29B9/12B29C48/875B29C48/05B29C48/04B29C48/40
Inventor 杨桂生蒋超杰符茂华孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka