A homogenizer with pre-annealing function

A glue homogenizer and pre-annealing technology, which is applied in the field of glue homogenizers, can solve the problems of low film-making efficiency, achieve the effects of improving glue dispensing efficiency, streamlining the preparation process, and improving film-making efficiency

Active Publication Date: 2016-01-13
SHANGHAI INST OF TECHNICAL PHYSICS - CHINESE ACAD OF SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The invention provides a glue leveler capable of multiple times of film-baking and pre-annealing function, which overcomes the experience of manual glue dropping operation and solves the problem of low efficiency of film making by sol-gel method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A homogenizer with pre-annealing function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Implementation example

[0023] 1. Prepare the precursor solution. Mn for the target component 1.56 co 0.96 Ni 0.48 o 4 Manganese oxide, respectively weigh 91.76g of manganese acetate tetrahydrate, 57.39g of cobalt acetate tetrahydrate, 28.66g of nickel acetate tetrahydrate, dissolve the powder according to the ratio of 400ml of acetic acid and 100ml of water for every 100g of acetate, pour into In the solution holding dish of the negative pressure suction filter, select a filter membrane with a pore size of 0.45 μm to carry out negative pressure suction filtration, filter out the impurity precipitate in the solution, and obtain Mn 1.56 co 0.96 Ni 0.48 o 4 Precursor solution, and put the solution into a storage bottle for later use.

[0024] 2. Preparation of manganese-cobalt-nickel-oxygen film. Using the homogenizer device in alumina (Al 2 o 3 ) prepared Mn on the substrate 1.56 co 0.96 Ni 0.48 o 4 After each spin-coating of the film, use its self-heatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glue mixing machine with a pre-annealing function. The glue mixing machine comprises a glue filling device, a heating device, a heat abstractor and a glue mixer, wherein the glue filling device is used for simplifying a manual glue dropping process into a control process of simple switch motion of a normal close type water valve, so that the glue dropping efficiency is improved, and the problem caused by experience-based glue dropping is avoided; the heating device is used for heating a sample and achieving a low-temperature pre-annealing function of a film; the heat abstractor is used for cooling an inner container of the glue mixer, promoting the exchange of heat and gas inside and outside the heating device, and discharging escaping organic substances after heating; the glue mixer is used for realizing glue throwing operation when the film is prepared. The glue mixing machine provided by the invention has the advantages that a film preparing experiment process of glue dropping, glue throwing and low-temperature pre-annealing in a sol-gel method is simplified into a film preparing experiment process of repeating glue dropping, glue throwing, low-temperature pre-annealing and then concentrated high-heat treatment with a rapid annealing furnace, so that the film preparing time is shortened, and the film preparing efficiency is greatly improved.

Description

technical field [0001] The invention relates to a glue homogenizer, in particular to a glue homogenizer with pre-annealing function. Background technique [0002] The sol-gel method is an important preparation method of thin film materials, which has the advantages of low synthesis temperature, convenient doping, flexible and controllable experimental conditions, and low cost [see Reference 1]. This method generally requires the use of a homogenizer (for spin-coating the precursor solution onto the substrate) and a rapid annealing furnace (for heat treatment of the sample), which requires manual dispensing, spinning, low-temperature thermal annealing, high-temperature Annealing and other experimental processes [see reference 2]. In its traditional application, the law has the following room for improvement. [0003] The first thing that needs to be improved is the manual dispensing and spin-coating process. Before each heat treatment process, it is necessary to use a glue...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05C9/14B05C5/02B05C11/00B05C11/08B05C11/10
Inventor 黄志明欧阳程周炜吴敬高艳卿龙芳褚君浩
Owner SHANGHAI INST OF TECHNICAL PHYSICS - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap