Corrosion and scale inhibitor for treating circulating cooling water
A corrosion and scale inhibitor, circulating cooling water technology, applied in the field of corrosion and scale inhibitors, can solve the problems of high concentration, eutrophication of water body or unsatisfactory treatment effect, high phosphorus content, etc., to improve heat exchange effect, Excellent corrosion and scale inhibition performance, the effect of low phosphorus content
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A corrosion and scale inhibitor for circulating cooling water treatment, its formulation is as follows:
[0023] Table 1: Formula composition of corrosion and scale inhibitors for circulating cooling water treatment
[0024] ingredients Dosage (g) PBTCA (effective content: 50%) 10.0 AA / AMPS (solid content: 30%) 20.0 PASP (solid content: 40%) 15.0 BTA 1.0 HEDP (effective content: 50%) 8.0 water 45.0
[0025] The preparation method of the corrosion and scale inhibitor is as follows: stirring each component evenly.
[0026] The prepared agent was carried out at a concentration of 60 mg / L, and the test of rotary coupon and scale inhibition test was carried out. The test results were: the corrosion rate of 20# steel was 0.065 mm / a, the corrosion rate of copper was 0.0019 mm / a, and the scale inhibition rate was 0.0019 mm / a. The rate is 91%.
Embodiment 2
[0028] A corrosion and scale inhibitor for circulating cooling water treatment, its formulation is as follows:
[0029] Table 2: Formula composition of corrosion and scale inhibitors for circulating cooling water treatment
[0030] ingredients Dosage (g) PBTCA (effective content: 50%) 5.0 AA / AMPS (solid content: 30%) 30.0 PASP (solid content: 40%) 35.0 BTA 2.0 water 28.0
[0031] The preparation method of the corrosion and scale inhibitor is as follows: stirring each component evenly.
[0032] The prepared agent was carried out at a concentration of 60 mg / L for the rotary coupon test and the scale inhibition test. The test results showed that the copper corrosion rate was 0.0009 mm / a, and the scale inhibition rate was 95%.
Embodiment 3
[0034] A corrosion and scale inhibitor for circulating cooling water treatment, its formulation is as follows:
[0035] Table 3: Formula composition of corrosion and scale inhibitors for circulating cooling water treatment
[0036] ingredients Dosage (Kg) PBTCA (effective content: 50%) 10.0 AA / AMPS (solid content: 30%) 60.0 PASP (solid content: 40%) 70.0 BTA 4.0 water 56.0
[0037] The preparation method of the corrosion and scale inhibitor is as follows: stirring each component evenly.
[0038] Apply the medicament prepared in Example 1 to the central air-conditioning circulating cooling water system. The installed capacity of the system is 4 sets of Trane DCWBRC2AAHBX, 2 sets of DCWEBLC2AAHBX, the refrigerant uses R134a, 11 cooling towers, and the temperature difference between the inlet and outlet of cooling water is 5.5- 6.5°C, the temperature difference between the inlet and outlet of chilled water is 4.5-5°C, 6 cooling...
PUM
Property | Measurement | Unit |
---|---|---|
scale inhibition rate | aaaaa | aaaaa |
scale inhibition rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com