Adhesive composition and surface-protective film

A binder and composition technology, applied in the direction of adhesives, adhesive types, ester copolymer adhesives, etc., can solve problems such as inability to meet performance requirements, and achieve the prevention of adhesive residue and excellent antistatic performance , improve the effect of preventing

Active Publication Date: 2014-01-15
FUJIMORI KOGYO CO LTD
View PDF9 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, even if each performance requirement can be satisfied individually, all the performance requirements required for the adhesive layer as a surface protection film cannot be satisfied.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive composition and surface-protective film
  • Adhesive composition and surface-protective film
  • Adhesive composition and surface-protective film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0111] Nitrogen gas was introduced into a reaction apparatus equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction pipe, thereby replacing the air in the reaction apparatus with nitrogen. Then, added 100 parts by weight of 2-ethylhexyl acrylate, 0.9 parts by weight of 8-hydroxyoctyl acrylate, 0.5 parts by weight of acrylic acid, 3 parts by weight of polyethylene glycol monoacrylate, 5 N-vinylpyrrolidone in parts by weight, and simultaneously add 60 parts by weight of solvent (ethyl acetate). Then, 0.1 parts by weight of azobisisobutyronitrile as a polymerization initiator was dropped over 2 hours, and reacted at 65° C. for 6 hours to obtain acrylic acid used in Example 1 with a weight average molecular weight of 500,000. Copolymer Solution 1. A part of the acrylic copolymer was taken and used as a sample for acid value measurement described later.

Embodiment 2~9 and comparative example 1~4

[0113] Except that the composition of each monomer was adjusted as described in (A) to (E) and (I-2) in Table 1, it was carried out in the same manner as the above-mentioned acrylic copolymer solution 1 used in Example 1, Acrylic copolymer solutions used in Examples 2-9 and Comparative Examples 1-4 were obtained.

[0114] Table 1

[0115]

[0116]

[0117] [Example 1]

[0118] To the acrylic copolymer solution 1 of Example 1 manufactured as described above, 1.5 parts by weight of 1-octylpyridinium hexafluorophosphate, 0.2 parts by weight of KF-351A (polyether-modified siloxane of HLB=12) were added. Compound), 2.5 parts by weight of acetylacetone and stirring, add 1.0 parts by weight of Coronate HX (coronet HX, isocyanurate of hexamethylene diisocyanate compound), 0.2 parts by weight of Coronate L (coronet L, toluene diisocyanate compound and trimethylolpropane), 0.02 parts by weight of dioctyltin dilaurate, and then stirred and mixed to obtain the adhesive composition ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention provides an adhesive composition with excellent anti-static function, durability and machinability, and the balance of bonding force of the composition under low peeling speed and high peeling speed is excellent. The adhesive composition is formed by crylic acid polymer containing co-polymer; the co-polymer crylic acid polymer comprises (A) (methyl) acrylate monomer containing alkyl and having carbon number C4-C10, (B) co-polymer monomer containing hydroxyl, (C) co-polymer monomer containing carboxylic, (D) poly alkylene diol single (methyl) acrylate monomer and (E) vinyl monomer containing nitrogen without hydroxyl or (methyl) crylic acid alkyl ester monomer having alkoxy, (F) isocyanate compound having tri-sense, (G) cross-linking inhibitor, (H) cross-linking catalyst, (I) antistatic agent, and (J) polyether modified siloxane compound; and the acid value of the crylic acid polymer is 0.01-8.0.

Description

technical field [0001] The present invention relates to a surface protection film used in the manufacturing process of a liquid crystal display. More specifically, the present invention relates to an adhesive for a surface protection film for protecting the surface of an optical component such as a polarizing plate or a retardation plate by sticking on the surface of an optical component such as a polarizing plate or a retardation plate constituting a liquid crystal display. An adhesive composition, and a surface protection film using the adhesive composition. Background technique [0002] Conventionally, in the manufacturing process of optical components such as polarizing plates and retardation plates, which are components of liquid crystal displays, a surface protection film is attached to temporarily protect the surface of the optical component. Such a surface protection film is used only in the process of manufacturing an optical component, and when the optical compone...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/08C09J7/02C08F283/06
CPCC09J7/22C09J7/38C09J7/40C09J133/04C09J175/04C09J2203/318C09J2301/302C09J2301/312C09J2301/408
Inventor 长仓毅岛口龙介长谷川良
Owner FUJIMORI KOGYO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products