Fluorite powder finishing process

A fluorite powder and process technology, applied in the direction of calcium/strontium/barium halide, calcium/strontium/barium fluoride, etc., can solve the problems of small profit margin, tail throwing loss, waste of resources, etc., and achieve easy operation and simple equipment. , the effect of small particle size change

Active Publication Date: 2016-06-22
FUXIN JINSHENG ENVIRONMENTAL SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Fluorite powder with a calcium fluoride content of more than 97% is an acidic chemical grade fluorite powder used in the production of hydrofluoric acid. The traditional fluorite powder flotation production process used in patents CN87105202, CN1063058, and CN101712014 uses sodium carbonate and water glass as regulators. Use oxidized paraffin soap or oleic acid as collector, heat to 30~40℃, flotation fluorite fine powder, domestic high-grade fluorite ore is basically mined, now mainly use low-grade fluorite ore to produce fluorite fine powder , but more than 97% of fluorite fine powder is flotation from low-grade fluorite ore, the tailing loss is serious, a large amount of resources are lost, the cost is high, and the profit margin is small. Generally, the fluorite powder content of flotation is about 90% (85 %~95%), containing high silicates and calcium carbonate components, which cannot meet the requirements of acidic chemical grade fluorspar powder. This kind of fluorspar powder is generally used in smelting, manufacturing ceramics, glass manufacturing and other industries. a waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1, put 10Kg of fluorite powder containing 93.58% into the reactor, add 5Kg of 40% hydrofluoric acid aqueous solution, stir for 10 minutes, put it into the sedimentation tank and let it stand for 10 hours, then filter, and recover the filtered liquid Utilize, solid is rinsed with the clear water of 20Kg, and the pH value of the aqueous solution after washing is 6. The solid is transferred to the neutralization tank, and 10Kg of saturated calcium hydroxide solution is added to soak for 10 hours and then filtered. The filtered solid is then rinsed with 6Kg of water until the pH value of the washed aqueous solution is 8. Dry at ℃ for 2 hours to obtain 9.23Kg of fluorite powder. The calcium fluoride content is 99.10% after testing. The particle size of the fluorite powder is different. The specific particle size is shown in Table 1.

[0011] Table I

[0012] sample total +100 mesh 100~150 mesh 150~200 mesh 200~250 mesh 250~300 mesh -300 mesh ...

Embodiment 2

[0014] Take 1Kg of fluorite powder containing 93.58%, put it into the reactor, add 1Kg of 20% hydrofluoric acid aqueous solution, stir for 10 minutes, put it in the sedimentation tank and let it stand for 10 hours, then filter it, recycle the filtered liquid, and use 2Kg of solid Rinse with clear water, the pH value of the washed aqueous solution is 6. The solid is transferred to the neutralization tank, add 1Kg saturated calcium hydroxide solution to soak for 10 hours and then filter, and the filtered solid is then rinsed with 1Kg clear water until the pH of the washed aqueous solution is The value is 8. Put the solid in a drying oven and dry at 110°C for 2 hours to obtain a product of 0.93Kg. After testing, the calcium fluoride content is 97.51%. The particle size of the fluorite powder is different. The specific particle size is shown in Table 2.

[0015] Table II

[0016] sample total +100 mesh 100~150 mesh 150~200 mesh 200~250 mesh 250~300 mesh -300...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the processing technology of chemical products, and particularly relates to a finishing process of fluorite powder. At a normal temperature of 0-40°C, 1000 parts of fluorite powder with a calcium fluoride content of 85-95% are taken by weight, of which The spar content does not exceed 0.6%, put it into the reaction container, add 300~3000 parts of acidic solution containing 10~50% hydrogen fluoride, mix the fluorite powder slurry evenly, and import the discharged material into the standing tank for 1~24 hours, use Filter and recycle the filtered liquid, rinse the filtered solid with 300~3000 parts of water, transfer the washed solid to the neutralization tank, add 300~3000 parts of alkaline solution to make the solution alkaline , the pH value is 10~14, filter again, rinse with 300~3000 parts of water after filtration, the pH value of the washed water is 7~9, and the washed solid is transferred to a drying oven. After testing, the dried The content of calcium fluoride in high-purity fluorite powder is not less than 97%. The process flow of fluorite powder finishing process is simple, easy to operate, the production equipment is simple, and the investment cost is low.

Description

technical field [0001] The invention belongs to the processing technology of chemical products, in particular to a finishing technology of fluorite powder. Background technique [0002] Fluorite powder with a calcium fluoride content of more than 97% is an acidic chemical grade fluorite powder used in the production of hydrofluoric acid. The traditional fluorite powder flotation production process used in patents CN87105202, CN1063058, and CN101712014 uses sodium carbonate and water glass as regulators. Oxidized paraffin soap or oleic acid is used as collector, heated to 30~40°C, flotation fluorite fine powder, the domestic high-grade fluorite ore is basically mined, and now the low-grade fluorite ore is mainly used to produce fluorite fine powder , but more than 97% of fluorite fine powder is flotation from low-grade fluorite ore, the tailing loss is serious, a large amount of resources are lost, the cost is high, and the profit margin is small. Generally, the fluorite powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F11/22
Inventor 王世勋徐国政许国峰
Owner FUXIN JINSHENG ENVIRONMENTAL SCI & TECH