A manufacturing method and technology of pottery products, which are applied in the field of manufacturing low-temperature energy-saving one-pass fired laterite painted and glazed pottery products, can solve the problems that the manufacturing method cannot be fired in one pass, and improve the grade and market share, increase the degree of sintering, Effect of reducing firing cost

Active Publication Date: 2015-03-11
福建省春秋陶瓷实业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a low-temperature, energy-saving and one-time-firing laterite painted and glazed pottery manufacturing method to solve the problems that the traditional laterite pottery manufacturing method cannot be fired once.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Manufacture green body: Mix the following raw materials in parts by weight: 65 parts of laterite, 5 parts of feldspar, 5 parts of black limestone, 5 parts of fluorite, 5 parts of kaolin, 5 parts of quartz, and 3 parts of lead-free frit , 2 parts of talc, 20 parts of water, mix well and grind into a soil slurry, inject the soil slurry into the mold for 0.5 hours, demould it, and let it air dry naturally at room temperature, and then dry it naturally after trimming and wiping water to obtain a green body ;

[0021] (2) Color painting: adjust the materials according to the shape and pattern of the pottery, and draw flower and grass patterns on the required parts of the green body in step (1);

[0022] (3) Manufacturing glaze water: Mix the following raw materials in weight fractions: 80 parts of low expansion glaze powder, 3 parts of zinc oxide, 10 parts of coloring agent, 3 parts of quartz powder, 2 parts of calcium carbonate, 2 parts of titanium oxide, 30 parts of wa...

Embodiment 2

[0026] (1) Manufacture green body: Mix the following raw materials in parts by weight: 60 parts of laterite, 6 parts of feldspar, 6 parts of black limestone, 6 parts of fluorite, 6 parts of kaolin, 6 parts of quartz, 4 parts of lead-free frit , 2.5 parts of talc, 25 parts of water, after mixing evenly, grind it into a soil slurry, inject the soil slurry into the mold for 0.75 hours, demould it, air dry it naturally at room temperature, and then dry it naturally after trimming and wiping water to obtain a green body ;

[0027] (2) Color painting: adjust the materials according to the shape and pattern of the pottery, and draw animal patterns on the required parts of the body in step (1);

[0028] (3) Manufacturing glaze water: Mix the following raw materials in weight fractions: 85 parts of low-expansion glaze powder, 4 parts of zinc oxide, 12 parts of coloring agent, 4 parts of quartz powder, 3 parts of calcium carbonate, 3 parts of titanium oxide, and 35 parts of water, Mix ...

Embodiment 3

[0032] (1) Manufacture green body: Mix the following raw materials in parts by weight: 63 parts of laterite, 8 parts of feldspar, 8 parts of black limestone, 8 parts of fluorite, 8 parts of kaolin, 8 parts of quartz, 4 parts of lead-free frit , 3 parts of talc, 30 parts of water, mix well and grind into a soil slurry, pour the soil slurry into the mold for 0.8 hours, demould it, air dry it naturally at room temperature, and then dry it naturally after trimming and wiping water to obtain a green body ;

[0033] (2) Color painting: adjust the coloring materials according to the shape and pattern of the pottery products, and draw natural landscape patterns on the required parts of the green body in step (1);

[0034] (3) Manufacturing glaze water: Mix the following raw materials in weight fractions: 90 parts of low expansion glaze powder, 5 parts of zinc oxide, 15 parts of coloring agent, 5 parts of quartz powder, 5 parts of calcium carbonate, 5 parts of titanium oxide, 40 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-temperature energy-saving manufacture method for once-sintered printed glazed red soil pottery products. The manufacture method comprises the steps of manufacturing green bodies, painting, manufacturing glazing liquid, glazing and sintering and the like. The manufacture method changes the formula of the red soil green bodies, decreases the proportion of red soil in the green bodies, and increases the sintering degree of the green bodies; gas in the green bodies is released timely during sintering. Therefore, the phenomena such as glaze jumping, and foaming and husking are avoided. The pottery products can be formed through once sintering, so that the sintering cost is reduced.

Description

technical field [0001] The invention relates to the technical field of ceramic technology, in particular to a low-temperature, energy-saving, one-pass firing method for producing laterite painted and glazed pottery products. Background technique [0002] Authorized notification number CN101993237B is a method for manufacturing low-temperature laterite painted and glazed ecological pottery products invented by the applicant. This manufacturing method improves the traditional three-firing method for laterite pottery products. The red clay body is sent into the kiln for the first firing, and then painted and glazed after being taken out, and then sent into the kiln for the second firing to obtain the finished product. Compared with the traditional three-firing method, this method reduces the cost to a certain extent, but the energy consumption of the two-firing is still high. [0003] The reason why laterite pottery products are fired twice is because the laterite body of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/00
Inventor 陈永定陈国生
Owner 福建省春秋陶瓷实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap