Molten iron slag collecting agent and preparation method thereof

A technology of slag collecting agent and molten iron, which is applied in the field of slag collecting agent, can solve the problems of troublesome storage and use, defects of slag inclusion, high cost, and achieve the effects of improving fluidity and dispersibility, bonding residues firmly, and enhancing fluidity.

Active Publication Date: 2014-02-19
WUJIANG HYDRAULIC COMPONENTS FOUNDRY
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the past, the straw ash widely used by foundry manufacturers has the function of heat preservation and avoiding the oxidation of molten iron, and also has a certain effect of collecting slag, but it seriously pollutes the environment, and it is very troublesome to store and use. carbon
With the continuous development of the field of liquid casting hydraulics, the perlite raw ore is directly used as a slag collecting agent after being crushed directly. The slag covering layer, its slag collecting and covering effect is far better than straw ash, but the slag collecting layer is not strong enough, it is easy to break when removing slag, and the adhesion to molten slag is not strong enough, and the perlite raw ore will cause splashing when it bursts on the surface of molten iron , some unexpanded particles are easy to enter the cavity from the gate and cause slag inclusion defects
[0004] In order to improve the slag collection effect, most domestic enterprises import slag collection and covering agent products from abroad, but the price is 5 to 10 times that of domestic products, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molten iron slag collecting agent and preparation method thereof
  • Molten iron slag collecting agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] (1) Preparation of expanded perlite samples: collect and select massive perlite ore with a size of 5-8 cm, crush it into granules by a crusher, sieve and select the crushed particles to 0.9-1.7 mm, and then add auxiliary materials to the sieved particles. Soak in the solvent solution for 10-15 seconds, do pre-expansion treatment, drain the water and put it in a 750°C oven to dry for 2-3 minutes to remove the water adsorbed on the surface of the particles to obtain a perlite sample with a micro-porous structure, and then heat the oven to Preheating at 850-1100 °C makes the pores in the micro-cavities expand, and obtains expanded perlite samples with micro-cavities;

[0029] (2) Preparation of slag collecting agent slurry. Weigh adhesive, heat preservation agent and deoxidizer according to the proportion of covering agent, add them into the stirring tank, add water and stir to obtain a liquid, and use mechanical stirring to mix the liquid with expanded perlite Stir the sa...

Embodiment 1

[0032] The molten iron slagging agent of the present invention was compared with Comparative Example 1 in a tundish with a capacity of 1.5 tons. The chemical components and performance of the slag collecting agent are shown in Table 1.

[0033] Example 1 The preparation process of the slag-collecting agent is as follows: (1) collect and select massive perlite ore with a size of 5-8 cm, and crush it into granules by a crusher, sieve and select the crushed particles to 0.9-1.7 mm, and then pour them into the sieved Add co-solvent solution to the granules and soak for 10-15s, do pre-expansion treatment, drain the water and put it in a 750°C oven to dry for 2-3 minutes to remove the water adsorbed on the surface of the granules to obtain a perlite sample with a micro-porous structure. The oven is then heated to 850°C to preheat to expand the pores in the micro-cavity, and obtain the expanded perlite sample with micro-cavity structure;

[0034] (2) Preparation of slag collecting ag...

Embodiment 2

[0039] In a tundish with a capacity of 1.5 tons, the molten iron slagging agent of the present invention is compared and verified with Comparative Example 2. The chemical components and performance of the slag collecting agent are shown in Table 1, and the difference with Example 1 is only: collecting slag The proportion of each chemical component of the agent is not the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a molten iron slag collecting agent; expanded perlite is used as a substrate, the components and mass percentages (%) of the slag collecting agent are as follows : 69 ~ 76% of SiO2, 0.6 ~ 1.2% of FeO, 1.5 ~ 2.3% of CaO, 0.2 ~ 1.2% of Na2O, 1.0~1.8% of TiO2, 0.8 ~ 1.5% of MgO, 1.0 ~ 1.4% of K2O and 0.1 ~ 0.3% of P, the slag collecting agent also includes by mass percentage (%), 2 ~ 5% of an adhesive , 0.5 ~ 1.2% of a heat insulating agent, 0.3 ~ 2.0% of a deoxidizing agent, and the balance of Al2O3. The invention also provides a preparation method of the slag collecting agent, and the preparation method includes the following steps: (1) preparation of an expanded perlite sample, to be more specific, collecting and selecting blocky perlite ore of 5 to 8cm, crushing into granules by a crusher, screening and picking broken granules to 0.9 ~ 1.7mm, then adding a cosolvent solution to the screened granules for soaking for 10 ~ 15s, performing pre expansion treatment, draining away water, putting into an oven of 750DEG C, drying for 2 ~ 3min to remove the water adsorbed on the surface of granules to obtain a perlite sample with a micro-hole structure, and raising the temperature of the oven to 850 ~ 1100 DEG C for pre heating to expand pores in micro holes to obtain an expanded perlite sample with the micro-hole structure; (2) preparation of slag collecting agent slurry; and (3) preparation of the slag collecting agent. The slag collecting agent of the invention has the characteristics of low cost, low dispersion, good fluidity, and strong slag adhesive capacity.

Description

technical field [0001] The invention relates to a slagging agent used in ladles, tundishes and electric furnaces and a method for preparing the slagging agent. Background technique [0002] Iron and steel is smelted from iron-containing ores. Iron ores are generally not pure, and contain non-metallic impurities such as sulfur and phosphorus. The main components of non-metallic impurities are silicates and oxides. During high-temperature smelting at ℃, non-metallic impurities are also melted. Because of their different properties from iron, a molten state of magma is formed. Because the specific gravity is lighter than that of iron, many small groups of impurities are dispersed and floated on the surface of high-temperature molten iron, and formed after condensation. Residue, if the residue is not removed when the molten iron is poured into the casting, it will be injected together with the molten iron to form lime sand, which will cause casting quality problems. [0003] In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/076
CPCY02P10/20
Inventor 浦巧生
Owner WUJIANG HYDRAULIC COMPONENTS FOUNDRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products