Polyacrylate emulsion and preparation method thereof

A technology of polyacrylate emulsion and n-butyl acrylate, applied in the field of polyacrylate emulsion and preparation, can solve the problems of precipitation, high temperature stickiness, alcohol intolerance, etc. Effect

Active Publication Date: 2014-02-26
HANGZHOU HIWETECH CHEM TECH CO LTD
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The object of the present invention is to provide a kind of polyacrylate emulsion and synthetic method, this polyacrylate emulsion does not use organic solvent, non-toxic environmental protection, and preparation method can overcome the ubiquitous "heat" in polyacrylate emulsion synthesized by traditional emulsion polymerization method. Sticky, cold and brittle", not resistant to organic solvents and other defects, applied in PVC wallpaper printing ink, can solve the problems of high temperature stickiness, precipitation of plasticizers and resistance to organic solvents such as alcohol to wipe, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] (1) Dissolve 0.05 parts by weight of sodium lauryl sulfate and 0.2 parts by weight of nonylphenol polyoxyethylene ether in 5 parts by weight of deionized water to form an aqueous phase, and then add 25 parts by weight of methyl methacrylate and 1 weight part of n-butyl acrylate were added into the water phase, and stirred at 30° C. and 400 rpm for 30 minutes for pre-emulsification to form a core layer pre-emulsion.

[0049] (2) 0.15 parts by weight of sodium lauryl sulfate and 0.6 parts by weight of nonylphenol polyoxyethylene ether were dissolved in 5 parts by weight of deionized water to form an aqueous phase, and then 10 parts by weight of methyl methacrylate , 8 parts by weight of n-butyl acrylate and 0.15 parts by weight of N-(isobutoxy) methacrylamide were added to the water phase, and stirred at 30°C and 400rpm for 20 minutes for pre-emulsification to form a cross-linked layer pre-emulsification liquid.

[0050] (3) 0.05 parts by weight of sodium lauryl sulfate ...

Embodiment 2

[0054] (1) Dissolve 0.05 parts by weight of sodium lauryl sulfate and 0.2 parts by weight of nonylphenol polyoxyethylene ether in 5 parts by weight of deionized water to form an aqueous phase, and then add 20 parts by weight of methyl methacrylate and 1 weight part of n-butyl acrylate were added into the water phase, stirred at 40° C. and 600 rpm for 60 min to form a core layer pre-emulsion.

[0055] (2) 0.3 parts by weight of sodium lauryl sulfate and 1.2 parts by weight of nonylphenol polyoxyethylene ether were dissolved in 5 parts by weight of deionized water to form an aqueous phase, and then 15 parts by weight of methyl methacrylate , 8 parts by weight of n-butyl acrylate and 0.2 parts by weight of N-(isobutoxy)methacrylamide were added to the water phase, and stirred at 50° C. and 800 rpm for 20 minutes to form a cross-linked layer pre-emulsion.

[0056] (3) 0.1 parts by weight of sodium lauryl sulfate and 0.4 parts by weight of nonylphenol polyoxyethylene ether were dis...

Embodiment 3

[0060] (1) Dissolve 0.2 parts by weight of sodium lauryl sulfate and 0.8 parts by weight of nonylphenol polyoxyethylene ether in 5 parts by weight of deionized water to form an aqueous phase, and then add 25 parts by weight of methyl methacrylate and 1 weight part of n-butyl acrylate were added into the water phase, stirred at 30° C. and 800 rpm for 50 min to form a core layer pre-emulsion.

[0061] (2) 0.12 parts by weight of sodium lauryl sulfate and 0.48 parts by weight of nonylphenol polyoxyethylene ether were dissolved in 5 parts by weight of deionized water to form an aqueous phase, and then 10 parts by weight of methyl methacrylate , 9 parts by weight of n-butyl acrylate and 0.1 parts by weight of N-(isobutoxy) methacrylamide were added to the water phase, and stirred at 30° C. and 400 rpm for 30 minutes to form a cross-linked layer pre-emulsion.

[0062] (3) 0.06 parts by weight of sodium lauryl sulfate and 0.24 parts by weight of nonylphenol polyoxyethylene ether were...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyacrylate emulsion and a preparation method thereof. The polyacrylate emulsion is prepared from the following raw materials in parts by weight: 21.1-35.3 parts of a pre-emulsion in a nuclear layer, 21.3-34.1 parts of a pre-emulsion in a crosslinking layer, 8.05-12.2 parts of a pre-emulsion in a shell, 22.21-34.43 parts of initiator aqueous liquor, 0.01-0.08 part of an anionic emulsifier d, 0.04-0.32 part of a non-ionic emulsifier d and 20 parts of deionized water d. The solid content of the target emulsion product disclosed by the invention is over 45%, the storage stability of the emulsion through freeze-thaw stability test is longer than 6 months, and the coating is good in temperature resistance. The emulsion is non-sticky at 200 DEG C, and the adhesive force of the coating to a PVC (polyvinyl chloride) substrate reaches level 1, so that the problems that PVC wallpaper is sticky at high temperature, easy in separation of a plasticizer and intolerant to wiping by organic solvents such as alcohol and the like can be effectively solved.

Description

(1) Technical field [0001] The invention relates to a polyacrylate emulsion, in particular to a polyacrylate emulsion used for PVC wallpaper printing ink and a preparation method thereof. (2) Background technology [0002] As an interior decoration material, wallpaper has developed rapidly in my country in recent years. Among them, PVC (polyvinyl chloride) wallpaper is widely used because of its good flame retardancy. PVC wallpaper is a composite material with paper as the base material, PVC plastic coating as the surface layer, and printing ink on it to obtain various exquisite patterns. PVC wallpaper has the advantages of beautiful, durable, high strength, anti-pull, and easy to paste. However, it has the disadvantages of being sticky at high temperature, releasing hydrogen chloride gas which is harmful to human health, migration and exudation of plasticizers used in large quantities, resulting in easy dust absorption on the surface, and decreased wear resistance. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/14C08F220/18C08F220/58C08F220/06C08F2/26C08F2/30C09D11/107
Inventor 许华君许少宏
Owner HANGZHOU HIWETECH CHEM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap