A solid-phase microextraction column and capillary technology, which is applied in separation methods, chemical instruments and methods, solid adsorbent liquid separation, etc., can solve the problem of automatic online combination of extraction, analysis and detection, and long extraction time of needle-type SPME fibers , Unable to realize automatic extraction and other problems, achieve the effect of shortening analysis time, improving precision and accuracy, and prolonging service life

Inactive Publication Date: 2015-08-19
DALIAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the solid-phase extraction operation based on graphene-modified silica particles is very complicated, and automatic extraction cannot be realized. The needle-type SPME fiber based on graphene coating has a long extraction time and limited enrichment multiples, and it is difficult to achieve extraction and analysis in the same area. Integrated automatic online connection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Take a quartz capillary with an inner diameter of 0.25mm and a length of 1m, first wash it with 0.1M sodium hydroxide for 0.5 hours, then wash it with 0.1M HCL hydrochloric acid for 0.5 hours, and finally wash it with deionized water until it is neutral, and blow it dry with nitrogen.

[0022] Fill the treated capillary column with 20mM APTES toluene solution, react at room temperature for 12 hours, then take it out and put it in a water bath at 70°C to continue the reaction for 5 hours, then take it out, rinse with toluene, and then rinse with water.

[0023] 0.2 mg / mL graphene oxide aqueous solution was sonicated for a period of time, centrifuged at 3000 rpm for 5 min, 4 mL of supernatant was taken, 10 μL of 10 mM EDC / 5 mM NHS was added, activated for 0.5 hours, and poured into a capillary, React in a water bath at 70°C for 2 hours, blow dry with nitrogen, and obtain an in-tube graphene micro-extraction column.

Embodiment 2

[0025] Take a quartz capillary with an inner diameter of 0.53mm and a length of 1m, wash it with 0.1M sodium hydroxide for 0.5 hours, then wash it with 0.1M HCL hydrochloric acid for 0.5 hours, and finally wash it with deionized water until neutral, and blow it dry with nitrogen.

[0026] Fill the treated capillary column with 20mM APTES toluene solution, react at room temperature for 12 hours, then take it out and put it in a water bath at 70°C to continue the reaction for 5 hours, then take it out, rinse with toluene, and then rinse with water.

[0027] Centrifuge 0.2 mg / mL graphene oxide aqueous solution at 3000 rpm for 5 min after ultrasonication for a period of time, take 4 mL of supernatant, add 10 μL of 10 mM EDC / 5 mM NHS, activate for 0.5 hours, and pour it into the capillary , reacted in a water bath at 70°C for 2 hours, and dried with nitrogen to obtain a graphene micro-extraction column in a tube.

Embodiment 3

[0029] Take a quartz capillary with an inner diameter of 0.25mm and a length of 1m, first wash it with 0.1M sodium hydroxide for 0.5 hours, then wash it with 0.1M HCL hydrochloric acid for 0.5 hours, and finally wash it with deionized water until it is neutral, and blow it dry with nitrogen.

[0030] Fill the treated capillary column with 20mM APTES toluene solution, react at room temperature for 12 hours, then take it out and put it in a water bath at 70°C to continue the reaction for 5 hours, then take it out, rinse with toluene, and then rinse with water.

[0031] Centrifuge 0.2 mg / mL carbon nanotube aqueous solution for a period of time at 3000 rpm for 5 min, take 4 mL of supernatant, add 10 μL of 10 mM EDC / 5 mM NHS, activate for 0.5 hours, pour it into a capillary, React in a water bath at 70° C. for 2 hours, blow dry with nitrogen, and obtain an in-tube carbon nanotube micro-extraction column.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an in-tube solid-phase micro-extraction column and a preparation method thereof, and belongs to the technical field of analytic chemistry sample pretreatment. The in-tube solid-phase micro extraction column is composed of a quartz capillary tube and a graphene oxide coating layer, wherein the graphene oxide coating layer is fixed on the inner wall of the quartz capillary tube through chemical bonding. During preparation, the inner wall of the quartz capillary tube is successively washed with an acid, washed with an alkali and blown to dry by nitrogen, a toluene solution containing 3-aminopropyltriethoxysilane (APTES) is poured into the capillary tube, the capillary tube has both ends sealed and is placed in a water bath for reaction, then a graphene oxide aqueous solution activated by 1-ethyl-3-(3-dimethylaminopropyl)-carbide diimine / N-hydroxy succinimide (EDC / NHS) is poured into the capillary tube, the capillary tube has the both ends sealed and is subjected to a reaction in the water bath, the graphene oxide is allowed to be bonded to the quartz capillary tube wall, and the in-tube solid-phase micro-extraction column is obtained. The in-tube solid-phase micro-extraction column has simple and rapid preparation method, allows the graphene coating layer to have good chemical property, mechanical property and thermal stability, has high extraction capacity and long service life, and has broad application prospects in the analytic chemistry and environmental analysis fields.

Description

technical field [0001] The invention discloses a preparation method of an in-tube solid-phase microextraction column, which is mainly used for the separation and enrichment of target objects in complex aqueous solution samples, and belongs to the technical field of analytical chemical sample pretreatment. Background technique [0002] Pretreatment is an important step in the analysis of complex samples. Through pretreatment, the interfering substances in the sample are removed and the target substance is concentrated to make up for the lack of existing separation technology and instrument detection sensitivity. Environmental sample analysis is roughly divided into four steps: ① sample collection, ② sample pretreatment, ③ analysis and determination, ④ data processing. For the analysis of samples with complex matrices, the time spent on sample pretreatment often accounts for two-thirds or more of the entire analysis process. With the continuous improvement of instrument leve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D15/20
Inventor 谭峰李莲君陈景文全燮
Owner DALIAN UNIV OF TECH