Moisture barrier material of asphalt

A technology of asphalt and petroleum asphalt, which is applied in the field of asphalt moisture-proof materials, can solve the problems of non-moisture-proof strength and poor stability of asphalt moisture-proof materials, and achieve the effect of good bonding strength, good stability and good water resistance

Inactive Publication Date: 2014-05-07
NANTONG SOUTHEAST HIGHWAY ENG
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] This application aims at the technical problems of existing asphalt moisture-proof materials such as non-moisture-proof and poor strength and stability, and provides a kind of asphalt moisture-proof material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An asphalt moisture-proof material, its composition expressed in parts by mass: 100 parts of petroleum asphalt; 30 parts of zinc yellow; 10 parts of heavy diesel oil; 5 parts of xylene; 10 parts of asbestos wool; 6 parts of mica iron oxide; 10 parts of tung oil 30 parts of vinyl acetate; 5 parts of aluminum stearate; 10 parts of butyl acrylate; 2 parts of butanol; 4 parts of methyl methacrylate; 2 parts of ethylenediamine. Add the above components into the reaction kettle, raise the temperature to 140°C, stir evenly, and then keep the temperature at 70°C for 4 hours.

[0014] The surface of the product is dry for 3 hours, and it is dry for 10 hours; the tensile strength is 200MPa, the water impermeability is 0.3MPa, and there is no leakage in 1 hour; the elongation at break is 500%, and there is no crack at -30°C.

Embodiment 2

[0016] An asphalt moisture-proof material, its composition expressed in parts by mass is: 100 parts of petroleum asphalt; 45 parts of zinc yellow; 15 parts of heavy diesel oil; 8 parts of xylene; 14 parts of asbestos wool; 8 parts of mica iron oxide; 20 parts of tung oil 35 parts of vinyl acetate; 8 parts of aluminum stearate; 15 parts of butyl acrylate; 5 parts of butanol; 10 parts of methyl methacrylate; 3 parts of ethylenediamine. Add the above components into the reaction kettle, raise the temperature to 140°C, stir evenly, and then keep the temperature at 70°C for 4 hours.

[0017] The surface of the product is dry for 2.5 hours, and it is dry for 9 hours; the tensile strength is 250MPa, the water impermeability is 0.3MPa, and there is no leakage in 1 hour; the elongation at break is 500%, and there is no crack at -30°C.

Embodiment 3

[0019] An asphalt moisture-proof material, its composition expressed in parts by mass is: 100 parts of petroleum asphalt; 35 parts of zinc yellow; 12.5 parts of heavy diesel oil; 6.5 parts of xylene; 12 parts of asbestos wool; 7 parts of mica iron oxide; 32.5 parts of vinyl acetate; 6.5 parts of aluminum stearate; 12.5 parts of butyl acrylate; 3.5 parts of butanol; 7 parts of methyl methacrylate; 2.5 parts of ethylenediamine. Add the above components into the reaction kettle, raise the temperature to 140°C, stir evenly, and then keep the temperature at 70°C for 4 hours.

[0020] The product is surface dry for 2 hours and solid for 8 hours; the tensile strength is 300MPa, the water impermeability is 0.3MPa, and there is no leakage in 1 hour; the elongation at break is 500%, and there is no crack at -30°C.

[0021] All components in the above examples are commercially available.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a moisture barrier material of asphalt. The moisture barrier material of asphalt is prepared from the following components in parts by weight: 100 parts of petroleum asphalt, 30-45 parts of zinc yellow, 10-15 parts of heavy diesel fuel, 5-8 parts of xylene, 10-14 parts of asbestos wools, 6-8 parts of mica iron oxide, 10-20 parts of tung oil, 30-35 parts of vinyl acetate, 5-8 parts of aluminum stearate, 10-15 parts of butyl acrylate, 2-5 parts of butanol, 4-10 parts of methyl methacrylate and 2-3 parts of a curing agent. The material is good in bonding strength and free from toxicity, and the time for surface dry is 2-3 hours and the time for hard dry is 8-10 hours. The tensile strength of the product is 200-300MPa, and the product is good in water resistance and stability, waterproof and moistureproof. The material is impermeable at 0.3MPa and no leakage is available within 1 hour. The elongation at break of the product is 500%, and the material is flawless at -30 DEG C and can be widely produced and continuously replace existing materials.

Description

technical field [0001] The application belongs to the field of asphalt materials, in particular to an asphalt moisture-proof material. Background technique [0002] Asphalt is a dark brown complex mixture composed of different molecular weight hydrocarbons and their non-metallic derivatives. It is in liquid state and is a waterproof, moisture-proof and anti-corrosion organic gelling material. It is used in paint, plastic, rubber and other industries as well as road paving. In civil engineering, asphalt is a widely used waterproof material and anti-corrosion material. It is mainly used in the waterproofing of roofs, grounds, and underground structures, and the anti-corrosion of wood and steel. Asphalt is also a widely used pavement structure cementing material in road engineering. It can be used to build asphalt pavement with different structures after it is matched with different mineral materials in proportion. [0003] The domestic heavy-traffic asphalt market is mostly o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L33/08C08K13/02C08K3/22C08K5/098C08K5/17
Inventor 陈磊磊吴志仁马群锋赵张飞何平
Owner NANTONG SOUTHEAST HIGHWAY ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com