Mixed pulp compound papermaking pulp substrate as well as preparation method and application thereof

A substrate and pulp mixing technology, which is applied in the direction of pulp beating method, pulp beating/refining method, botanical equipment and method, etc., can solve the problems of waste water discharge, product properties, texture, use difference, etc., and achieve good finish, The effect of enhancing uniformity

Active Publication Date: 2014-06-18
苏州吉臣日用品有限公司
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] (2) The papermaking and compounding of various pulps is mostly limited to the field of papermaking technology
[0006] (3) Multi-layer laminated net making is mostly limited to the field of papermaking technology
[0008] (4) The production of viscose pulp needs to be cooked and accompanied by a large amount of wastewater discharge
Moreover, pulp is only an intermediate product of the papermaking process, and there are great differences in product properties, textures, uses, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixed pulp compound papermaking pulp substrate as well as preparation method and application thereof
  • Mixed pulp compound papermaking pulp substrate as well as preparation method and application thereof
  • Mixed pulp compound papermaking pulp substrate as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0085] Weighing: 75 kg of bamboo pulp, 10 kg of reed pulp, 10 kg of sugarcane pulp, and 5 kg of fluff pulp.

[0086] The substrate is a layer in which:

[0087] The average fiber length of bamboo pulp is 0.5mm, and the length ratio of the longest fiber to the shortest fiber is <18;

[0088] The average fiber length of reed pulp is 0.46mm, and the length ratio of the longest fiber to the shortest fiber is <10.2;

[0089] The average fiber length of sugarcane pulp is 0.65mm, and the length ratio of the longest fiber to the shortest fiber is <4.6;

[0090] The average fiber length of fluff pulp is 12 mm, and the length ratio of the longest fiber to the shortest fiber is <5.7;

[0091] The density of fly ash is 1.9g / cm 3 , bulk density 0.531g / cm 3 ; The specific surface area is 800g / cm2 by nitrogen adsorption method 3 , the standard consistency of raw ash is 27.3%; the water demand is 89%; the 28d compressive strength ratio is 37%.

[0092] Preparation method: After mixing a...

Embodiment 2

[0103] Weighing: 75 kg of bamboo pulp, 10 kg of reed pulp, 9.7 kg of sugarcane pulp, 5 kg of fluff pulp, and 0.3 kg of fly ash.

[0104] The substrate is a layer in which:

[0105] The average fiber length of bamboo pulp is 7mm, and the length ratio of the longest fiber to the shortest fiber is <18;

[0106] The average fiber length of reed pulp is 3.68mm, and the length ratio of the longest fiber to the shortest fiber is <10.2;

[0107] The average fiber length of sugarcane pulp is 2.17mm, and the length ratio of the longest fiber to the shortest fiber is <4.6;

[0108] The average fiber length of fluff pulp is 36mm, and the length ratio of the longest fiber to the shortest fiber is <5.7;

[0109] The density of fly ash is 2.9g / cm3 , bulk density 1.261g / cm 3 ; The specific surface area is 19500g / cm2 by nitrogen adsorption method 3 , the standard consistency of raw ash is 27.3-66.7%; the water demand is 130%; the 28d compressive strength ratio is 85%.

[0110] Preparation...

Embodiment 3

[0120] Weighing: 75 kg of bamboo pulp, 10 kg of reed pulp, 8.3 kg of sugarcane pulp, 5 kg of fluff pulp, and 1.7 kg of fly ash.

[0121] The substrate is a layer in which:

[0122] Among them: the average fiber length of bamboo pulp is 3.3mm, and the length ratio of the longest fiber to the shortest fiber is <18;

[0123] The average fiber length of reed pulp is 2.62mm, and the length ratio of the longest fiber to the shortest fiber is <10.2;

[0124] The average fiber length of sugarcane pulp is 1.85mm, and the length ratio of the longest fiber to the shortest fiber is <4.6;

[0125] The average fiber length of fluff pulp is 22mm, and the length ratio of the longest fiber to the shortest fiber is <5.7;

[0126] The density of fly ash is 2.2g / cm 3 , bulk density 0.836g / cm 3 ; The specific surface area is 12023g / cm2 by nitrogen adsorption method 3 , the standard consistency of raw ash is 27.3-66.7%; the water demand is 112%; the 28d compressive strength ratio is 66%.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a mixed pulp compound papermaking pulp substrate as well as a preparation method and an application thereof. The mixed pulp compound papermaking pulp substrate is prepared from following raw materials in parts by weight: 70-80 parts of bamboo pulp, 5-15 parts of reed pulp, 5-15 pats of cane syrup, 2-8 parts of fluff pulp and 0-2 parts of fly ash. The preparation method comprises the following steps: pulping, preparing the pulp, carrying out high-concentration degritting, grinding the pulp, carrying out low-concentration degritting, carrying out pressure screening, slushing, compounding and making paper with the pulp, drying and the like. The raw materials of the mixed pulp compound papermaking pulp substrate are selected from perennial wild herbaceous plants, processing industrial wastes, and fire coal wastes of power planes and industrial boilers; a product is uniform in texture and smooth in surface; no pollutants are discharged in a preparation process; water for diluting, agitating and conveying can be cyclically utilized; the mixed pulp compound papermaking pulp substrate provided by the invention can be used for producing electric mats and cockroach killing pieces or can be used as an industrial filtering material.

Description

technical field [0001] The invention relates to a pulp substrate, a preparation method and its application, in particular to a mixed pulp composite papermaking pulp substrate, a preparation method and its application. Background technique [0002] (1) The use of plant stem and leaf mixed pulp is mostly limited to the field of papermaking technology [0003] CN1173094C discloses a "refined high-white color printing newsprint and its manufacturing method" (application number 02114232.7), which is characterized in that: pulp weight ratio, bleached kraft softwood pulp (BKP); Italian poplar alkaline hydrogen peroxide thermal grinding Mechanical pulp (APMP); bleached mechanical groundwood pulp (GP) 24~30:30~45:30~45, the refined high white color printing newsprint. [0004] (2) The papermaking and compounding of various pulps is mostly limited to the field of papermaking technology [0005] CN101225627B discloses a "method for preparing gas-phase antirust paper from industrial s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H13/36D21D1/02D21D1/20B01D39/14A01N25/18A01N25/20
Inventor 郑明伟张晖王伟君王翠
Owner 苏州吉臣日用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap